Version Summary Created by Modification Content Size Created at Operation
1 -- 3686 2023-12-20 09:42:00 |
2 Reference format revised. Meta information modification 3686 2023-12-22 02:35:08 |

Video Upload Options

Do you have a full video?

Confirm

Are you sure to Delete?
Cite
If you have any further questions, please contact Encyclopedia Editorial Office.
Rodriguez-Otero, A.; Vargas, V.; Galarneau, A.; Castillo, J.; Christensen, J.H.; Bouyssiere, B. Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks. Encyclopedia. Available online: https://encyclopedia.pub/entry/52962 (accessed on 22 June 2024).
Rodriguez-Otero A, Vargas V, Galarneau A, Castillo J, Christensen JH, Bouyssiere B. Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks. Encyclopedia. Available at: https://encyclopedia.pub/entry/52962. Accessed June 22, 2024.
Rodriguez-Otero, Alba, Vicmary Vargas, Anne Galarneau, Jimmy Castillo, Jan H. Christensen, Brice Bouyssiere. "Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks" Encyclopedia, https://encyclopedia.pub/entry/52962 (accessed June 22, 2024).
Rodriguez-Otero, A., Vargas, V., Galarneau, A., Castillo, J., Christensen, J.H., & Bouyssiere, B. (2023, December 20). Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks. In Encyclopedia. https://encyclopedia.pub/entry/52962
Rodriguez-Otero, Alba, et al. "Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks." Encyclopedia. Web. 20 December, 2023.
Sustainable Harnessing of SiO2 Nanoparticles from Rice Husks
Edit

Rice husks, as a residue from agriculture, had been largely used as a source of power through direct incineration in major rice-producing countries. However, rice husks present an intriguing opportunity as a renewable source of SiO2, offering a low-cost adsorbent with a high surface area and ease of functionalization that can be transformed into diverse mesoporous silica structures or composites, enabling applications in catalysis, drug delivery, water treatment, etc. This dual potential of rice husks can be harnessed by combining bio-oil and syngas production through pyrolysis with the efficient extraction of SiO2, ensuring the comprehensive utilization of the biomass. 

SiO2 nanoparticles rice husk bio-oil circular economy biomass pyrolysis

1. Introduction

Accessibility to sustainable, low-carbon bio-feedstock is one of the key drivers to achieve a European Union (EU) low-carbon economy by 2050. In this context, the development of biomass conversion technologies is being promoted [1].
Agricultural waste is in the spotlight of sustainable biomass production since an important amount of waste is produced yearly and is usually not fully harnessed. The source of this biomass includes primary agricultural resources produced directly on the field after crop harvesting and secondary plant resources obtained during industrial processing of agricultural crops. The potential estimated for the latter in 2030 in the EU report ranges from 56 to 81 million tons, with France, Austria, Germany and Spain being the countries with the largest contributions [1].
Among secondary plant resources, several residues are included, such as olive pits, fruit pulp, husks, shells, etc. Among the largest residues generated in agriculture are those coming from rice plants (Oryza sativa), especially their husks. Rice husk (RH) is the major by-product in the rice milling industry, which is estimated to be 1.2 billion tons annually worldwide [2][3][4].

Rice Husk as a Source of Bio-Energy and SiO2

Dried RHs contain about 15–28 wt% silica, depending on the origin and type, and 72–85 wt% lignocellulose (15–22 wt% lignin, 12–29 wt% hemicellulose, 29–36 wt% cellulose and 3–13 wt% traces of metals). As it does not have sufficient protein content (~4 wt% proteins, oils) for agricultural uses, most RHs are either burned or buried in landfills [5]. RH is the biomass waste containing the largest amount of silica (~210 g/kg of husk) [6]. Even when compared to other husks, such as wheat husk, or other parts of the rice plant, such as the straw, its silica content is the highest.
Therefore, as RHs are not easily decomposed by bacteria due to their highly inorganic content, their accumulation in landfills is not a sustainable option. For this reason, RH incineration has been the most common technique for removal since the heating value is around 15 MJ/kg, and so this energy can be harnessed [7]. Nevertheless, this method produces a high amount of rice husk ash (RHA) that needs to be disposed of as well, with its most common use currently being as a filler, additive, etc., in the building and construction industry. If RH is not properly pretreated before the incineration, the composition of the ashes results in a low-purity silica composite due to the metal and carbon content present in the husk. Rice plants collect silica from the soil, which is stored as silicic acid inside the cellulose micro-compartments of the plant. The metal content varies according to the soil and manures used, but traces of potassium, calcium, magnesium, iron, sodium, manganese, aluminum, phosphorous and sulfur are found [8]. K is the main metal of RH (~2.7 mg/g), followed by Ca (~1.5 mg/g) and Mg and Mn (0.36 mg/g). The presence of K promotes the crystallization of silica into tridymite and cristobalite, a carcinogenic compound featuring a very low surface area (10 m2/g), and leads to the formation of unburnt carbon residues. Then, the silica powder is not white, and the specific surface area is low: from 145 m2/g for calcination at 600 °C to less than 20 m2/g for higher temperatures due to silica crystallization [9].
The low economic efficiency of incineration of RH has led to a search for alternative methods to harness this agricultural waste. For instance, pyrolysis of biomass is a hot topic currently since it leads to the production of pyrolysis gas and bio-oil from the decomposition of the lignocellulosic materials, and in the specific case of rice husk, char rich in silica is obtained as a third by-product. So, for these aforementioned reasons, it is considered to be a more efficient way to thermally degrade organic matter [10][11]. However, it has to be considered that pyrolysis bio-oil has a heating value of around 13–25 MJ/kg, lower than diesel and gasoline [7].
Silicon is the second most abundant element in the Earth’s crust after oxygen, which is brought to the soil by chemical and biological processes. Plants are highly involved in such processes as they transform the silicon present in water into water-soluble silicic acid [H4SiO4, or Si(OH)4], which is accumulated in the form of phytoliths, amorphous hydrated silica (SiO2 with 5–10% H2O). In rice plants, these phytoliths accumulate primarily in the husk. The deposition of silicon in this form offers the plant resistance against pathogens, stresses and pests, enhancing growth and development, thus Si availability in the soil where the rice grows is highly important [12].
Silica is one of the most important inorganic materials in the industry since it has a wide variety of applications, such as in catalyst production, catalyst supports, drug carriers, construction, glass and ceramics and water filtration, among others. Specifically, nanosized silica is of great interest due to its large surface area, thermal conductivity (insulation), good dispersion performance, ease of functionalization, chemical stability and biocompatibility [13]. These properties show an interesting prospect in the development of techniques to harness silica from agricultural waste.
To synthesize highly dispersed mesoporous SiO2 NPs, Stöber synthesis is modified by adding surfactants (such as cetyltrimethylammonium bromide or chloride (CTAB or CTAC)) to direct the mesopores formation by micelle-templating. The water content is also increased. For example, one of the best homogeneous, highly dispersed mesoporous SiO2 NPs was achieved by Möller et al. [14] by replacing NH4OH with triethanolamine (TEA) in mixtures with a molar composition of 1 TEOS: 0.27 CTAC: 1–4 TEA: 137 H2O: 6.2 EtOH. Mesoporous SiO2 NPs of 50 and 100 nm were obtained at 60 °C for TEA/TEOS = 1 and 4, respectively. Surfactant removal was achieved by a twofold extraction in acidified EtOH or by adding NH4NO3 at 60 °C for 2 h. The most convenient method was acidified EtOH at 25 °C with 30 min ultrasounds. The mesoporous SiO2 NPs feature ordered cylindrical homogenous mesopore of 3.5 nm diameter, specific surface areas of 1000 m2/g and mesopore volume of 0.77 mL/g as MCM-41 materials. Another interesting modification of the Stöber synthesis using CTAB is realized by replacing alcohols with aldehydes [15][16]. Mixtures with a molar ratio of 1 TEOS: 0.14 CTAB: 1.6–3.4 NH4OH: 100 H2O: 11–22 acetaldehyde at 27 °C give rise to MCM-41-like mesoporous NPs with particle sizes ranging from 40 to 850 nm. The particle size decreases by increasing the pH (adding more NH4OH) or by decreasing the amount of acetaldehyde. 
Although great results have been achieved in producing porous silica NPs, the mentioned chemical methods imply the use of hazardous chemicals harmful to the environment, such as CTAB, or costly techniques (by the use of TEOS, specifically). For this reason, the interest in developing green processes for producing silica NPs from biomass and agricultural waste is becoming of great interest [17], as evidenced by the publication of more than 400 research articles on the topic since 2019 (Figure 1).
Figure 1. Documents published on silica nanoparticles from rice husk from 1990 to 2023 (Scopus, April 2023).

2. Sustainable Harnessing of SiO2 from Rice Husks

2.1. Traditional Thermochemical Methods: Calcination

In the 1990s, direct combustion of rice husk without any chemical pretreatment was the most common method [18][19]. The first controlled combustion of RH, where amorphous silica powder was synthesized, was reported by Kapur in 1984. Combustion of rice husk led to a 20 wt% of ashes composed mainly of silica. As no purification pretreatment was applied, no pure silica was obtained [19]. Some acid leaching occurred on the rice husk ash after calcination [20]. However, the specific surface area of the resulting nanoparticles was not reported since the main objective was to determine the diameter of the nanoparticles and the effects of changing the ball milling parameters [20].
The type of rice affects the produced nanoparticles; silica nanoparticles synthesized from brown rice husk had the smallest diameter (10 nm) in comparison with sticky (50 nm) or red (20 nm) rice [21]; thus, the origin of the RH also determines its final structure. The soil quality also affects the elemental composition of the RH. Benassi L. et al. (2015) [22] found a difference in the metal composition of Italian and Indian rice husks, which affected the availability of amorphous silica at the same calcination temperatures. Indian RH from different regions was found to have different metallic content, which also affected the formation of amorphous silica and its purity, pointing out the relevance of K2O content in this matter [23].

2.2. Pyrolysis of Rice Husk for Obtaining Bio-Oil and Bio-Silica in the Literature

2.2.1. Bio-Silica Production

Pyrolysis of acid-leached rice husk in an N2 atmosphere was described by Liou et al. (2004) [24], obtaining carbon/silica powders with a surface area of 261 m2/g at 900 °C. No bio-oil is recovered from this process. In the same study, the acid-leached rice husks were calcined with air, and the surface area obtained was 235 m2/g.
To our knowledge, the first pyrolysis performed, with the aim of obtaining pure silica nanoparticles, was reported in 2011 by Wang et al. [25]. However, although it is referred to as pyrolysis, it seems more like combustion since heating in the absence of oxygen does not achieve the obtention of pure silica but a composite of carbon and silica [25].
Liou et al. (2011) performed pyrolysis on acid-leached (hot HCl) RH at 700 °C for 1 h and extracted SiO2 by NaOH 1.5 M at 100 °C for 1 h to produce sodium silicate [26]. The addition of 1 M HCl to this sodium silicate solution to reach pH 7 at 50 °C allowed for the precipitation of SiO2 NPs of 6–8 nm diameter (350 m2/g, mesopore diameter 10.4 nm, V = 0.79 mL/g). These NPs are non-porous and agglomerated, and Na content (1.31 mg/g) is superior to the parent RH.

2.2.2. Combined Bio-Silica and Bio-Oil Production

Research has been made on the production of bio-oil from pyrolyzed rice husks, studying its composition and its feasibility as a biofuel.
Lu Q et al. (2008) [10] analyzed the properties of bio-oil extracted from rice husk, which were similar to other bio-oils in terms of chemical composition. Acids, alcohols, ketones, sugars, etc., were compounds found in rice husk bio-oil similarly as for other bio-oils from different biomasses. However, they found high concentrations of nitrogen, inorganic elements and many low-boiling compounds, but significantly less heavy components, as well as high contents of water, solids and ash, and the presence of alkali metals, which is undesirable as well. The rice husks were not previously leached with acid, which explains the presence of these metals. Their main conclusion was that there is a need to upgrade the bio-oil produced from rice husk before it can be used as biofuel. In this case, the rice husk was not previously treated, and the bio-oil yield was 50 wt%.
Hsu et al. (2015) [27] studied the pyrolysis of RH in a fluidized bed pyrolizer with the aim of producing syngas and bio-oil, but it does not focus on the production of biochar or silica. The yields obtained with a N2 gas flow of 40 L/min and feeding rate of 10 g/min were the following: syngas: 38.52%; bio-oil: 29.44%; and char: 32.04%. The composition of the bio-oil was analyzed, which showed that it was mainly composed of aromatic compounds.

3. Tailoring of SiO2 from Rice Husk to Enhance Porosity

3.1. Mesoporous RH-SiO2 Nanoparticles

One of the main goals of the optimization of the extraction process of silica from rice husk is achieving a large surface area since the surface area is linked to the value of the produced material. Efforts to adapt acid-leaching, grinding and calcination parameters to enhance the porosity of silica from rice husk have been reported.
The effect of calcination temperature was studied by Manasa et al. (2021). Five silica materials were synthesized, with different calcination conditions in the oven after acid leaching. Temperatures of 550, 600 and 650 °C for 3 h combined with air or N2 flow were studied as parameters for the extraction of SiO2. The highest BET surface area (SA) (376 m2/g) was achieved with RH-SIO2-600A calcined at 600 °C. RH-SiO2-600A had a pore size of 4.5 nm and a pore volume of 0.38 mL/g. The same RH subjected to pyrolysis with only N2 at 600 °C was a composite C/SiO2, named RH-SiO2-600N, which presented a lower SA of 267 m2/g, a smaller pore diameter (2.7 nm) and a smaller pore volume (0.17 mL/g) [28]. With higher temperatures than 600 °C, the SA decreases, and the pore size increases, possibly due to nanoparticles sintering.

3.2. Ordered Mesoporous RH-SiO2 Nanoparticles

Ordered structures of silica, known as the MCM (Mobil Composition of Matter) family, have the potential for a wide range of processes. These materials combine amorphous characteristics with the ordered structure of homogeneous mesopores with adjustable diameters from 2 to 10 nm, developing a specific surface area as high as 1000 m2/g due to very thin walls (1 nm) in between the pores. Rice husk has been explored as a raw material to produce biogenic MCM-41 by hydrothermal methods.
Most studies use similar methodologies for the production of biogenic MCM. Rice husk is pretreated with acid and then calcinated, then the silica in RHA is extracted by an alkali solution to form a sodium silicate solution. This solution is mixed with a surfactant solution such as CTAB, the pH is increased, and the solution is aged [29][30][31][32]. The solid obtained needs to be treated, usually by calcination, in order to remove the surfactant.

3.3. Shaping RH-SiO2 NPs into Macroporous Structures

The assembly of mesoporous silica into macroporous structures such as monoliths presents great advantages for industrial applications, such as flow processes.
The use of rice husk as a silica precursor for this material has been explored by Bahrami et al. (2017) [33] by freeze-casting a water-based bio-silica solution.
Both amorphous (ARHA) and crystalline (CRHA) (80/20 cristobalite/tridymite) rice husk ash were synthesized with acid-leaching pretreatment only for ARHA and calcination at 600 and 900 °C, respectively. Obtained ARHA had a specific surface area of 151 m2/g and pore volume of 0.23 mL/g, while CRHA particles form agglomerates with a specific surface area of 1.5 m2/g. Before freeze-casting, both RHA were ground with a high-energy planetary ball mill to produce a fine powder (d < 10 μm).
Freeze-cast monoliths with lamellar and cellular pore structures (macropores in the range of 10–50 μm) were obtained from ARHA and CRHA. It was found that the crystallinity of the starting material does not have a significant impact on the macropores’ structure compared to other parameters of the synthesis (freezing rate and solid content).

4. RH-SiO2 Applications

4.1. RH-SiO2 for Biomedical Applications

The main goals for biomedical applications such as drug delivery are to reduce side effects and treatment costs. The use of biogenic nanomaterials produced from waste resources accomplishes these objectives.
Biogenic silica nanoparticles (NPs) synthesized by acid leaching at 120 °C and calcination at temperatures of 500–700 °C were tested for cell viability for human stem cells revealing high biocompatibility [34]. In the same way, SiO2 NPs were produced and then milled after calcination to an average diameter of <150 nm in order to be used as a carrier of Penicillin-G. Once the drug was added to the silica, in vitro release was studied in simulated body fluid (SBF), concluding that the silica NPs can act as a carrier that delays the release of the drug in the body [20].

4.2. RH-SiO2 for Energy Storage

Nanosized SiO2 can also be used for photovoltaic and energy storage applications. SiO2 NPs properties, such as high surface area and hydrophilic surface, enhance electrochemically active centers, which favors electrolyte transport through the material, which can be applied in the development of supercapacitors [35]. SiO2/C composites obtained by direct pyrolysis of rice husk were used for Li-ion sulfur batteries, showing high capacities as electrode material [36]. Other researchers doped the silica with tin oxide in order to gain reactivity through the sol-gel method. These showed good performance as electrodes for making electrochemical supercapacitors [37].

4.3. RH-SiO2 as Catalyst Support

Silica nanoparticles have been used as catalyst supports, taking advantage of their large surface area. Silica prepared through microwave-assisted acid leaching and posterior calcination was used as an iron-oxide-containing nanocatalyst for toluene alkylation and oxidation of benzyl alcohol [38].
A SiO2/C-nickel-based catalyst was obtained through rice husk pyrolysis for the selective hydrogenation of furfural derived from biomass [39]. A similar nickel-based catalyst supported on RH silica showed high performance in yielding H2 production during non-oxidative methane cracking [28]. As can be seen, silica’s thermal stability is really attractive for use in catalytic reactions. Also, various studies have proved SiO2 to be a better support for Ni than other traditional materials [40].

4.4. RH-SiO2 as Adsorbent for Water Cleaning

4.4.1. Adsorption of Chemicals of Emerging Concern and Other Micropollutants

The current trends explored by researchers in adsorption are the utilization of agri-waste-based biomass due to its low cost, simple design and the added value of being a method of waste valorization [41].
Activated carbon has been the most traditionally used adsorbent, and it has been demonstrated to be efficient with hydrophobic compounds but highly inefficient with hydrophilic and electrically charged molecules. Moreover, the efficiency of activated carbon is reduced in the presence of organic matter, and the regeneration of adsorbents is questionable [42].
However, the ease of obtention of activated carbon from lignocellulosic residues via pyrolysis at 500–600 °C and posterior activation at 700 °C has always made this material extremely attractive. Moreover, it can be easily functionalized.
Therefore, the most recent advances that are being made in adsorption correspond to the need to develop efficient, reusable and cheaper adsorbents than activated carbon, as well as materials that can retain PMOCs (persistent mobile organic compounds) or PMTs (persistent mobile and toxic). The recent introduction of nanotechnology into wastewater treatment has shown to be a feasible solution to the issue of CECs [41][43].

4.4.2. Adsorption of Metals in Water

The adsorptive capacities of silica nanoparticles can be exploited for water cleaning by the recovery of toxic metals present in wastewater. As mentioned before, for micropollutants, currently, there is a great interest in developing cost-effective, simple and environmentally friendly techniques to deal with this issue. SiO2 has been applied to heavy metal removal from water [44][45][46][47][48].
Silica derived from rice husk has been less studied as an adsorbent of metals. Silica NPs extracted from RHA via the sol-gel method with a particle size of around 50 nm and a surface area of 70 m2/g were studied for the removal of Fe2+ ions in water. Iron adsorption capacity was found to be 9 mg/g at its maximum at pHs higher than 5 in 20 min [49].
SiO2 NPs were produced from rice husk by incubation in fungal biomass for its biotransformation. These NPs were tested for their adsorption of Pb in water spiked with 88 ppb, the same concentration measured in samples from fish farms, showing maximum adsorption after 120 h of contact time. Then, the goal of this study was to test the adsorption ability of SiO2 NPs in vivo in fishes supplemented with Pb and silica NPs, which showed effective adsorption of Pb at 1 ppm in the fish O. niloticus, hence reducing its mortality rates [50].
The removal of Cr3+ and Cu2+ by milled rice husk was tested. In this case, no extraction of SiO2 was performed, and the husk was used directly in a batch test with 100 ppm of each metal. As previously seen in other studies, the highest adsorption capacity (22.5 mg Cr3+/g and 30 mg Cu2+/g) reaches its peak at pH > 5 [51]. The use of rice husk ash directly as an adsorbent has also been studied in the literature; however, rice husk ash has smaller surface areas compared with amorphous SiO2 NPs [52]. These adsorption abilities can be implemented for the treatment of real wastewater, such as tannery wastewater, which is rich in Cr3+. Silica NPs were obtained from calcinated and leached rice husks using the sol-gel method. At pH 6, the highest adsorption capacity was determined to be 385 mg Cr3+/g, and the chromium complexes were better adsorbed when the size of the pores was increased since their diffusion into the particles seems to be the limiting factor [53].
To summarize, among the different procedures outlined previously, the following references focus on optimal techniques for generating high-surface silica nanoparticles from rice husk, cost-effective methods for shaping silica nanoparticles into monoliths suitable for flow applications, utilizing silica nanoparticles from rice husk for value-added materials like MCM-41, and the economical application of silica materials derived from rice husk for removing pollutants.

5. Conclusions

Silica nanoparticles have great, well-known properties such as a tunable specific surface area and particle shape and diameter. They can be obtained (i) directly after acid-leaching of rice husk and controlled pyrolysis and/or calcination, (ii) by rice husk calcination (leading to classical rice husk ash from industry) followed by silica dissolution by NaOH (or Na2CO3) and silica precipitation in acidic medium, and (iii) by pyrolysis of acid-leached rice husk followed by NaOH dissolution and silica precipitation in acidic medium. Pathways (i) and (iii) are recommended to obtain higher silica purity and high surface area. They can be easily functionalized and transformed into other mesoporous silica featuring very high surface areas, such as MCM-41 (1000 m2/g), or into composites with other metals. These properties provide it with an excellent adsorption capacity, which can be applied to medicine as drug carriers or into catalysis as metal support, among others. When silica nanoparticles are extracted from biomass, they have been proven to have excellent biocompatibility and properties similar to silica produced by traditional methods but with a significant decrease in chemicals and energy consumption. SiO2 derived from secondary agricultural waste such as rice husk is also advantageous since they are considered to be the major contributors in the future for sustainably sourced energy and materials since their growth does not compete with food crops. With the intent of harvesting most of the rice husk, applying circular economy to SiO2 extraction through methods such as combined pyrolysis and calcination can lead to the obtention of valuable by-products such as bio-oil and pyrolysis gas. By varying processing parameters, SiO2 nanoparticles can be tailored for specific applications.

References

  1. Imperial College London. Sustainable Biomass Availability in the EU, to 2050. 2021. Available online: https://www.concawe.eu/publication/sustainable-biomass-availability-in-the-eu-to-2050/ (accessed on 27 September 2022).
  2. An, D.; Guo, Y.; Zhu, Y.; Wang, Z. A green route to preparation of silica powders with rice husk ash and waste gas. Chem. Eng. J. 2010, 162, 509–514.
  3. Ng, E.-P.; Awala, H.; Tan, K.-H.; Adam, F.; Retoux, R.; Mintova, S. EMT-type zeolite nanocrystals synthesized from rice husk. Microporous Mesoporous Mater. 2015, 204, 204–209.
  4. Zhang, H.; Ding, X.; Chen, X.; Ma, Y.; Wang, Z.; Zhao, X. A new method of utilizing rice husk: Consecutively preparing d-xylose, organosolv lignin, ethanol and amorphous superfine silica. J. Hazard. Mater. 2015, 291, 65–73.
  5. Chen, H.; Wang, W.; Martin, J.C.; Oliphant, A.J.; Doerr, P.A.; Xu, J.F.; DeBorn, K.M.; Chen, C.; Sun, L. Extraction of Lignocellulose and Synthesis of Porous Silica Nanoparticles from Rice Husks: A Comprehensive Utilization of Rice Husk Biomass. ACS Sustain. Chem. Eng. 2013, 1, 254–259.
  6. Gebretatios, A.G.; Pillantakath, A.R.K.K.; Witoon, T.; Lim, J.-W.; Banat, F.; Cheng, C.K. Rice husk waste into various template-engineered mesoporous silica materials for different applications: A comprehensive review on recent developments. Chemosphere 2023, 310, 136843.
  7. Steven, S.; Restiawaty, E.; Bindar, Y. Routes for energy and bio-silica production from rice husk: A comprehensive review and emerging prospect. Renew. Sustain. Energy Rev. 2021, 149, 111329.
  8. Rao, G.R.; Sastry, A.R.K.; Rohatgi, P.K. Nature and reactivity of silica available in rice husk and its ashes. Bull. Mater. Sci. 1989, 12, 469–479.
  9. Chen, P.; Gu, W.; Fang, W.; Ji, X.; Bie, R. Removal of metal impurities in rice husk and characterization of rice husk ash under simplified acid pretreatment process. Environ. Prog. Sustain. Energy 2017, 36, 830–837.
  10. Lu, Q.; Yang, X.-L.; Zhu, X.-F. Analysis on chemical and physical properties of bio-oil pyrolyzed from rice husk. J. Anal. Appl. Pyrolysis 2008, 82, 191–198.
  11. Nawaz, S.; Jamil, F.; Akhter, P.; Hussain, M.; Jang, H.; Park, Y.-K. Valorization of lignocellulosic rice husk producing biosilica and biofuels—A review. J. Physics Energy 2023, 5, 012003.
  12. Mahmad-Toher, A.-S.; Govender, N.; Dorairaj, D.; Wong, M.-Y. Comparative evaluation on calcium silicate and rice husk ash amendment for silicon-based fertilization of Malaysian rice (Oryza sativa L.) varieties. J. Plant Nutr. 2021, 45, 1336–1347.
  13. Jeelani, P.G.; Mulay, P.; Venkat, R.; Ramalingam, C. Multifaceted Application of Silica Nanoparticles. A Review. Silicon 2020, 12, 1337–1354.
  14. Möller, K.; Kobler, J.; Bein, T. Colloidal suspensions of mercapto-functionalized nanosized mesoporous silica. J. Mater. Chem. 2007, 17, 624–631.
  15. Zhang, A.; Gu, L.; Hou, K.; Dai, C.; Song, C.; Guo, X. Mesostructure-tunable and size-controllable hierarchical porous silica nanospheres synthesized by aldehyde-modified Stöber method. RSC Adv. 2015, 5, 58355–58362.
  16. Lou, F.; Zhang, A.; Zhang, G.; Ren, L.; Guo, X.; Song, C. Enhanced kinetics for CO2 sorption in amine-functionalized mesoporous silica nanosphere with inverted cone-shaped pore structure. Appl. Energy 2020, 264, 114637.
  17. Akinjokun, A.I.; Ojumu, T.V.; Ogunfowokan, A.O. Biomass, Abundant Resources for Synthesis of Mesoporous Silica Material. In Microporous and Mesoporous Materials; BoD—Books on Demand: Norderstedt, Germany, 2016; pp. 105–177.
  18. James, J.; Rao, M. Silica from rice husk through thermal decomposition. Thermochim. Acta 1986, 97, 329–336.
  19. Kapur, P. Production of reactive bio-silica from the combustion of rice husk in a tube-in-basket (TiB) burner. Powder Technol. 1985, 44, 63–67.
  20. Salavati-Niasari, M.; Javidi, J.; Dadkhah, M. Ball milling synthesis of silica nanoparticle from rice husk ash for drug delivery application. Comb. Chem. High Throughput Screen. 2013, 16, 458–462.
  21. Sankar, S.; Sharma, S.K.; Kaur, N.; Lee, B.; Kim, D.Y.; Lee, S.; Jung, H. Biogenerated silica nanoparticles synthesized from sticky, red, and brown rice husk ashes by a chemical method. Ceram. Int. 2016, 42, 4875–4885.
  22. Benassi, L.; Bosio, A.; Dalipi, R.; Borgese, L.; Rodella, N.; Pasquali, M.; Depero, L.E.; Bergese, P.; Bontempi, E. Comparison between rice husk ash grown in different regions for stabilizing fly ash from a solid waste incinerator. J. Environ. Manag. 2015, 159, 128–134.
  23. Chandrasekhar, S.; Pramada, P.N.; Praveen, L. Effect of organic acid treatment on the properties of rice husk silica. J. Mater. Sci. 2005, 40, 6535–6544.
  24. Liou, T.-H. Evolution of chemistry and morphology during the carbonization and combustion of rice husk. Carbon 2004, 42, 785–794.
  25. Wang, W.; Martin, J.C.; Zhang, N.; Ma, C.; Han, A.; Sun, L. Harvesting silica nanoparticles from rice husks. J. Nanoparticle Res. 2011, 13, 6981–6990.
  26. Liou, T.-H.; Yang, C.-C. Synthesis and surface characteristics of nanosilica produced from alkali-extracted rice husk ash. Mater. Sci. Eng. B 2011, 176, 521–529.
  27. Hsu, C.-P.; Huang, A.-N.; Kuo, H.-P. Analysis of the Rice Husk Pyrolysis Products from a Fluidized Bed Reactor. Procedia Eng. 2015, 102, 1183–1186.
  28. Manasa, K.; Naresh, G.; Kalpana, M.; Sasikumar, B.; Velisoju, V.K.; Chary, K.V.; Michalkiewicz, B.; Venugopal, A. Improved H2 yields over rice husk derived SiO2 nanoparticles supported Ni catalyst during non-oxidative methane cracking. J. Energy Inst. 2021, 99, 73–81.
  29. Choudhary, P.; Sharma, R.; Kumar, V.; Singh, A.; Sharma, N. Synthesis, Characterization and Catalytic Activity of Bio-MCM-41 for Production of Bio Crude Oil via Pyrolysis of Rice Straw. Waste Biomass Valorization 2023, 14, 4173–4186.
  30. Alyosef, H.A.; Uhlig, H.; Münster, T.; Kloess, G.; Einicke, W.-D.; Gläser, R.; Enke, D. Biogenic silica from rice husk ash-Sustainable sources for the synthesis of value-added silica. Chem. Eng. Trans. 2014, 37, 667–672.
  31. Costa, J.A.S.; Sarmento, V.H.V.; Romão, L.P.C.; Paranhos, C.M. Adsorption of organic compounds on mesoporous material from rice husk ash (RHA). Biomass Convers. Biorefinery 2020, 10, 1105–1120.
  32. Kamari, S.; Ghorbani, F. Extraction of highly pure silica from rice husk as an agricultural by-product and its application in the production of magnetic mesoporous silica MCM–41. Biomass Convers. Biorefinery 2021, 11, 3001–3009.
  33. Bahrami, A.; Simon, U.; Soltani, N.; Zavareh, S.; Schmidt, J.; Pech-Canul, M.I.; Gurlo, A. Eco-fabrication of hierarchical porous silica monoliths by ice-templating of rice husk ash. Green Chem. 2017, 19, 188–195.
  34. Athinarayanan, J.; Periasamy, V.S.; Alhazmi, M.; Alatiah, K.A.; Alshatwi, A.A. Synthesis of biogenic silica nanoparticles from rice husks for biomedical applications. Ceram. Int. 2015, 41, 275–281.
  35. Prabha, S.; Durgalakshmi, D.; Rajendran, S.; Lichtfouse, E. Plant-derived silica nanoparticles and composites for biosensors, bioimaging, drug delivery and supercapacitors: A review. Environ. Chem. Lett. 2021, 19, 1667–1691.
  36. Huang, S.-S.; Tung, M.T.; Huynh, C.D.; Hwang, B.-J.; Bieker, P.M.; Fang, C.-C.; Wu, N.-L. Engineering Rice Husk into a High-Performance Electrode Material through an Ecofriendly Process and Assessing Its Application for Lithium-Ion Sulfur Batteries. ACS Sustain. Chem. Eng. 2019, 7, 7851–7861.
  37. Vijayan, R.; Kumar, G.S.; Karunakaran, G.; Surumbarkuzhali, N.; Prabhu, S.; Ramesh, R. Microwave combustion synthesis of tin oxide-decorated silica nanostructure using rice husk template for supercapacitor applications. J. Mater. Sci. Mater. Electron. 2020, 31, 5738–5745.
  38. Franco, A.; De, S.; Balu, A.M.; Romero, A.A.; Luque, R. Integrated Mechanochemical/Microwave-Assisted Approach for the Synthesis of Biogenic Silica-Based Catalysts from Rice Husk Waste. ACS Sustain. Chem. Eng. 2018, 6, 11555–11562.
  39. Madduluri, V.R.; Mandari, K.K.; Velpula, V.; Varkolu, M.; Kamaraju, S.R.R.; Kang, M. Rice husk-derived carbon-silica supported Ni catalysts for selective hydrogenation of biomass-derived furfural and levulinic acid. Fuel 2020, 261, 116339.
  40. An, D.; Guo, Y.; Zou, B.; Zhu, Y.; Wang, Z. A study on the consecutive preparation of silica powders and active carbon from rice husk ash. Biomass Bioenergy 2011, 35, 1227–1234.
  41. Kumar, P.S.; Joshiba, G.J.; Femina, C.C.; Varshini, P.; Priyadharshini, S.; Karthick, M.A.; Jothirani, R. A critical review on recent developments in the low-cost adsorption of dyes from wastewater. Desalination Water Treat. 2019, 172, 395–416.
  42. Bui, T.X.; Choi, H. Adsorptive removal of selected pharmaceuticals by mesoporous silica SBA-15. J. Hazard. Mater. 2009, 168, 602–608.
  43. Kollarahithlu, S.C.; Balakrishnan, R.M. Adsorption of pharmaceuticals pollutants, Ibuprofen, Acetaminophen, and Streptomycin from the aqueous phase using amine functionalized superparamagnetic silica nanocomposite. J. Clean. Prod. 2021, 294, 126155.
  44. Peralta, M.E.; Mártire, D.O.; Moreno, M.S.; Parolo, M.E.; Carlos, L. Versatile nanoadsorbents based on magnetic mesostructured silica nanoparticles with tailored surface properties for organic pollutants removal. J. Environ. Chem. Eng. 2021, 9, 104841.
  45. Soltani, R.D.C.; Khorramabadi, G.S.; Khataee, A.; Jorfi, S. Silica nanopowders/alginate composite for adsorption of lead (II) ions in aqueous solutions. J. Taiwan Inst. Chem. Eng. 2014, 45, 973–980.
  46. Knight, A.W.; Tigges, A.B.; Ilgen, A.G. Adsorption of copper (II) on mesoporous silica: The effect of nano-scale confinement. Geochem. Trans. 2018, 19, 13.
  47. Chen, W.; Zhang, H.; Liang, Y.; Ding, H.; Sun, S. Adsorption Properties and Mechanism of Cd2+ in Water by Zr-containing Silica Residue Purification. Front. Chem. 2018, 6, 556.
  48. Ebner, A.D.; Ritter, J.A.; Navratil, J.D. Adsorption of Cesium, Strontium, and Cobalt Ions on Magnetite and a Magnetite−Silica Composite. Ind. Eng. Chem. Res. 2001, 40, 1615–1623.
  49. Nguyen, T.T.; Ma, H.T.; Avti, P.; Bashir, M.J.K.; Ng, C.A.; Wong, L.Y.; Jun, H.K.; Ngo, Q.M.; Tran, N.Q. Adsorptive removal of iron using SiO2 nanoparticles extracted from rice husk ash. J. Anal. Methods Chem. 2019, 2019, 6210240.
  50. El-Gazzar, N.; Almanaa, T.N.; Reda, R.M.; El Gaafary, M.; Rashwan, A.; Mahsoub, F. Assessment the using of silica nanoparticles (SiO2NPs) biosynthesized from rice husks by Trichoderma harzianum MF780864 as water lead adsorbent for immune status of Nile tilapia (Oreochromis niloticus). Saudi J. Biol. Sci. 2021, 28, 5119–5130. Available online: https://www.sciencedirect.com/science/article/pii/S1319562X21003958 (accessed on 6 December 2022).
  51. Sobhanardakani, S.; Parvizimosaed, H.; Olyaie, E. Heavy metals removal from wastewaters using organic solid waste—Rice husk. Environ. Sci. Pollut. Res. 2013, 20, 5265–5271.
  52. Priya, A.; Yogeshwaran, V.; Rajendran, S.; Hoang, T.K.; Soto-Moscoso, M.; Ghfar, A.A.; Bathula, C. Investigation of mechanism of heavy metals (Cr6+, Pb2+& Zn2+) adsorption from aqueous medium using rice husk ash: Kinetic and thermodynamic approach. Chemosphere 2022, 286, 131796.
  53. Amirhandeh, S.Z.H.; Salem, A.; Salem, S. Treatment of tannery wastewater by silica nanoparticles produced from rice husk ash via a green route. Environ. Sci. Pollut. Res. 2022, 30, 13039–13047.
More
Information
Contributors MDPI registered users' name will be linked to their SciProfiles pages. To register with us, please refer to https://encyclopedia.pub/register : , , , , ,
View Times: 184
Revisions: 2 times (View History)
Update Date: 22 Dec 2023
1000/1000
Video Production Service