Dynamic Emerging Glazing Technologies

Version	Summary	Created by	Modification	Content Size	Created at	Operation
1		Michalis Michael	--	2775	2023-10-23 11:10:15	\|
2	format correct	Catherine Yang	Meta information modification	2775	2023-10-24 03:11:06	\|

This entry is adapted from the peer-reviewed paper 10.3390/en16145357

The development of the existing dynamic glazing technologies enables modulating the g-value (thus, the amount of heat) and VT (thus, the light) penetrated through the glazing while ensuring outside vision. These dynamic glazing technologies, in particular the electrochromic ones, have been proven to be more effective than traditional static glazing regarding the reduction of energy demand for air conditioning and lighting. In addition, they provide occupants’ comfort of a higher level and quality. However, the prohibitively high cost does not allow their widespread dissemination and application in the building industry. Hence, new emerging dynamic glazing technologies are currently under research or development.

building envelopes dynamic glazing technologies emerging glazing technologies

1. Electrochromic Evacuated Glazing (ECEVG)

Recently, a combination of electrochromic and vacuum glazing in a single unit has been investigated ^[1]^[2]. To show the potential of this technology, ^[3] examined and evaluated ECEVG prototypes with VT of 0.63, in the transparent state, and U-values of 0.86 W/m²K. Figure 1 illustrates the layout of an ECEVG.

Figure 1. Schematic illustration of an ECEVG (retrieved from ^[2]).

According to ^[4], an ECEVG glazing system can be switched between clear and opaque states by applying a DC voltage. This occurs since the applied voltage modifies the density of the electrochromic layer’s electrons, leading to a change in the optical properties and state of the system, and consequently, entering solar energy can be modulated. A significant advantage of ECEVG is that it combines the transmittance of electrochromic glazing, which varies with the low heat loss characteristics of evacuated glazing. Therefore, optimal thermal comfort is achieved while energy consumption is reduced. Work on the energy performance of ECEVG showed that, due to the EC layer, about 10% of incident solar energy in the transparent state and 60–80% in the opaque state is absorbed ^[2]. Investigation of the energy performance of ECEVG was performed with EC layer facing outdoor or indoor environment. This investigation revealed that the temperature difference between the inside and outside glass pane, when the electrochromic layer was facing the indoor environment, was dangerously high, resulting in the breakdown of the glazing system. In the case of an ECEVG, the electrochromic layer must be placed facing the outdoor instead of the indoor environment.

2. Integrated Micro-Blinds and Nanocrystals EC

An emerging dynamic glazing technology with incorporated micro-blinds and nanocrystals-based electrochromic materials promises possible future applications in architecture. Integrated micro-blinds consist of inorganic prestressed curling electrodes with a size of the order of 100 µm. They are invisible to the naked eye being able to unwind when they are triggered by a weak electrostatic stimulus ^[5]. Light passes through when no voltage is applied because the blinds are curled. However, when a voltage is applied, the micro-blinds are stretched under the electrostatic forces induced by the applied voltage, and light is blocked. The performance of this glazing is comparable to that of conventional dynamic electric control glazing ^[6]. Currently, a few institutions, such as the University of Kassel, Germany ^[7], the University of Tokyo, Japan, and the Institut National d’Optique, Canada ^[8] are working on developing this technology.

The main advantages of this glazing technology are: (i) conductive layers of expensive indium-tin oxide are not required, (ii) very small (in the order of milliseconds) activation and deactivation times, and (iii) for further performance improvement in the unwound state, highly reflective materials are used ^[9]. Current development aims to create market-sized glazing that can independently modulate visible light and infrared solar radiation.

3. Localised Plasmon Resonance (LPR)

For energy-saving purposes, the reflection of solar radiation at near-infrared wavelengths is vital to prevent heat transfer into space and decrease cooling energy consumption. Therefore, for near-infrared light, reflecting coatings attached to glazing are important ^[10]^[11]^[12]. On the other hand, achieving high light transmission in the visible range is also significant to ensure good visibility and decrease electricity consumption for lighting the space. According to ^[13], Fujifilm Co. Ltd. has developed a spectrally selective film ( Nano Silver Pavement, NASIP), which satisfies the above requirements. It consists of randomly distributed silver nanoparticles with disk shapes that reflect near-infrared light. The physical principle of its operation is attributed to plasmon resonances between the nanostructured matter and the incoming light ^[10].

An LPR film with silver nanoparticles is shown in Figure 2a, whereas Figure 2b depicts a scanning electron microscope (SEM) image of disk-shaped silver nanoparticles ^[11]. The nanoparticles, which are in disc shape have an average diameter in the range of 100–120 nm, and their thickness is about 10 nm. Furthermore, from Figure 2b, the shape and layout of nanoparticles vary randomly. The fabricated film’s spectral properties (reflectance and transmittance), which were observed experimentally, are depicted in Figure 2c.

Figure 2. (a) LPR film (b) image indicating the silver nanoparticles (c) measured transmittance and reflectance of the LPR film (retrieved from ^[13]).

It can be shown that the reflectance is high for near-infrared light whereas, in the visible and far-infrared regions, the transmittance maintains high. In Figure 2c, particles resonate at frequencies of light with wavelengths of about 900 nm. At this wavelength, light is reflected and scattered, whereas, at the other values of the light wavelength, it is transmitted. The reflectivity and transparency of the film can be modulated by tuning the resonant frequency by controlling the size and shape of nanoparticles.

4. Electrically Tunable Glazing

According to ^[14], a device has been designed to control the light transmitted through significant areas, such as glazing surfaces. The main feature of this device is that without affecting its colour its transparency is tunable. Its operation is based on the distortion of the soft dielectrics caused by a voltage applied between the two electrodes on either side of the elastomer ^[15].

5. Nanocrystal in-Glass Composites Glazing (NCCG)

Among electrochromic glazing, nanocrystal in-glass composites (NCCG) are the most promising emerging technology for improving the glazing’s overall performance (thermal and visual). It allows separate and independent regulation of the transparency of visible light (VL) and near-infrared (NIR) wavelengths, and, therefore, it is characterised as dual-band dynamic glazing technology ^[16].

NCCGs technology was initially developed by the University of California, Berkeley, using nanocrystals of Indium-tin-oxide (ITO) in a niobium oxide (NbOx) matrix called NIR-switching electrochromic glazing ^[17]. This technology, without blocking visible light transmission, allows controlling NIR radiation from a bright mode (fully transparent) to a cool mode (state without VL control), and finally, a no-tinted state (dark mode) controlling both heat and natural light.

The energy performance of this glazing technology has been investigated using simulations for various types of buildings and weather conditions in the USA and compared to electrochromic glazing ^[18]. This investigation/comparison shows that dual-band dynamic glazings are the best energy savers for cooling and heating-dominated climates.

6. Elastomer-Deformation Tunable Glazing

This emerging dynamic glazing technology can vary from a clear to an opaque state, able to diffuse light similarly to LCD glazing. It has different properties and uses from electrochromic. It is based on a mechanical rather than an electrochemical approach to light control ^[14]. A schematic illustration of the composition and principle of operation of an elastomer-deformation tunable glazing is illustrated in Figure 3. The glass pane is located between two transparent soft dielectrics on which electrically conducting silver nanowires are sprayed. These nanowires do not significantly affect light transmission. They are invisible to the naked eye, and they react to electromagnetic stimuli.

Figure 3. Schematic illustration of composition and principle of operation of elastomer-deformation tunable glazing (retrieved from ^[16]).

The basis of the operation of this glazing technology is the geometric alteration of the glazed surface, which leads to control light scattering. Thus, the optical state of the glazing changes to any state between transparent and opaque. According to ^[16], without voltage applied to the system, the glazing is at the clear state, as shown in Figure 3 as nanowires are not energised. On the contrary, by applying a voltage to the system, the nanowires are energised, become electrodes, and, due to Coulomb forces, they move toward each other. Under this movement, the two layers are squeezed and deformed, leading to an irregular surface roughness since nanowires are unevenly distributed. This results in light refraction reducing the glazing VT ^[19].

Remarkably, the time required for the complete process is less than a second, while the value of the applied voltage can control the irregular surface roughness of the elastomer, and thus, according to this value, tuning of VT is achievable. This is an advantage compared to conventional LCD glazing, which allows only altering from a transparent to an opaque state. The manufacturing process of the subject glazing technology uses elastomer sheets available in large rolls; therefore, it is cheaper compared to the more expensive vacuum deposition process used by chemical-based dynamic glazing technologies currently used. The best potential of this technology is the possibility of glare control while maintaining an adequate level of diffused light indoors. However, the energy performance of this technology in real-time has not been defined yet.

7. Liquid Infill Tunable Glazing Technology

Liquid infill tunable glazing technology belongs to purely mechanical systems in contrast to the electrochemical systems to which most dynamic glazing technologies belong. For this technology, the use of a liquid for shading purposes is employed. The liquid is pumped in or out of the cavity/cavities of insulated glazing systems. The principle of its operation is schematically illustrated in Figure 4 ^[16]. The liquid-based technology was developed at the Universita Politecnica delle Marche ^[20] and includes a triple glazing unit, with one 12 mm cavity used for thermal insulation purposes and a second cavity of 1.5 mm used for the storage tanks of the shading fluid and gas. These tanks are enclosed in the glazing frame, and the circulation of shading fluid is achieved by a pump which, when it is needed, fills the narrow cavity with the shading fluid, whereas the gas is extracted and pumped to the gas tank. Thus, the glazing unit can block unwanted light and heat. Further to the main components described above, the system also employs overflow sensors and valves required for the monitoring of liquid infill.

Figure 4. Schematic illustration of the principle of operation of liquid infill tunable window (retrieved from ^[16]).

Regarding the system’s performance, experimental work revealed that the visual and thermal transmittance, at its clear and filled state, is: 68.3% with 47.2% and 16.0% with 18.3%, respectively ^[16].

The main disadvantage of this technology is the bulky frames needed for the accommodation of piping, pump, and liquid and gas storage tanks. Furthermore, another disadvantage may be the uneven appearance of the glazing in its partly filled state due to the fluid pumping from the bottom of the panes.

8. Electrokinetic Pixel Glazing Technology

Electrokinetic pixel glazing technology is a polarised particle technology, such as LCD technology, that aims to modulate the colour and temperature of the visible light passing through electrochromic glazing. According to ^[21], by controlling the movement of coloured particles via an applied voltage, it is possible to modulate separately the transmission and colour of the light entering the glazing.

Figure 5a shows that the glazing consists of two planar electrodes to control how the particles of 2 complementary colours (Blue-Yellow or Red-Cyan or Green-Magenta) carrying opposite electrical charges are dispersed. The principle of operation is schematically illustrated in Figure 5b. Each electrode can be separately charged, positively or negatively, triggering the coloured particles’ movement towards another electrode.

Figure 5. Schematic illustration of: (a) composition and (b) operation principle of electrokinetic pixel glazing technology (redrawn from ^[16]).

According to ^[16], the movement and final concentration/position of the coloured particles determine the various states/modes characterised by different VT and light colour, as shown in Figure 5b: (i) Dark when electrodes are not charged, and both colour particles are mixed and uniformly dispersed, (ii) Clear state, when outer perimeter electrode is not charged, inner perimeter electrode is negatively charged, hexagonal grid electrode is positively charged and thus colour particles are compacted at the perimeter electrode and the micro-pits without colour dispersion. (iii) Cold hue, when the outer perimeter electrode is negatively charged, the inner perimeter electrode is not charged, hexagonal grid electrode is positively charged, and thus blue particles dispersed. In contrast, yellow particles compacted around the perimeter electrode and, (iv) Warm hue, when the outer perimeter electrode is positively charged, the inner perimeter electrode is not charged, hexagonal grid electrode is negatively charged and thus yellow particles dispersed and blue particles accumulated around the perimeter electrode. A 25 V voltage is required for switching between control states, whereas each state can be maintained with a voltage of ±10 V ^[16].

9. Optofluidic Glazing

The three optical properties, transmission, reflection, and absorption, can be adapted by utilizing the concept of refractive index matching. The optofluidic glazing consists of two transparent layers and an air cavity between the two layers ^[9]. One of the transparent layers is roughened from the inside. The light rays are reflected and scattered due to the roughened surface, and thus, the light transmittance is reduced. The working mechanism of the optofluidic glazing utilizes the total internal reflection between the material-air interfaces. The cube reflectors reflect the light incident upon them back to the source, whereas the light transmittance increases when the intermediate space is filled with fluid. As the fluid’s refractive index increases compared to that of the surrounding material, the refraction decreases, and the transmittance increases.

It is worth mentioning that optofluidic glazing has various maintenance problems. For instance, leakage and low air temperature (less than the freezing point of the liquid) are reported ^[9]. However, recently, sealed modules have been manufactured using Vero Clear photopolymer ^[22]. Due to the capability to modulate reflectance and transmittance, solar loads can be controlled, and consequently, the efficiency of heating, ventilation, and air conditioning increases. Furthermore, privacy panels, dynamic camouflage, and architecture are reported as additional applications of optofluidic glazing ^[22].

The main advantages and disadvantages of emerging glazing technologies are tabulated and presented in Table 1.

Table 1. Features/Advantages and Limitations/Disadvantages of emerging glazing technologies.

Glazing Technology		Features/Advantages	Limitations/Disadvantages	References
Static	Air Sandwich	Reduction of glare U-value and VT vary with the number of air layers Relatively simple process	It has lower thermal performance currently It has not been used for a long time Vulnerable to degradation due to solar radiation	^[23]^[24]^[25]
	Suspended films	Among all the glazing technologies it has the lowest U-value Significantly thinner and lighter	Relatively low g-value (High values are needed for cold climates) Relatively low VT	^[26]
	Heat Insulation Solar Glass (HISG)	It provides thermal insulation, power generation, self-cleaning, and acoustic insulation ( Multi-functional glazing) Lower U-value compared to conventional PV	Very low VT Improvement of its high cost is needed	^[27]^[28]
	Transparent Insulation Material (TIM)	High g-value Significant reduction of heat loss Significant increase in solar gain	Imperfection in the manufacturing process Very high production cost Overheating may occur due to high levels of solar radiation absorption	^[29]^[30]
	Solar absorbing	Reduction of inner pane temperature Room heat gain is decreased Air-conditioning electricity reduction Enhanced thermal and visual comfort	Complicated installation Piping and controls are needed Considerable space is required for piping and feed water tank	^[31]
	Transparent PV	Optimisation of VT and power generation High potential to cover more than 40% of a building’s energy needs	Low efficiency Currently, its cost is very high At an early stage of development	^[32]^[33]^[34]^[35]^[36]^[37]^[38]^[39]
Dynamic	Electrochro-mic evacuated	Optimal thermal comfort Reduction of energy consumption It can be combined with other technologies	High cost A voltage source is needed Longer time to be used is needed	^[1]^[2]^[3]^[4]
	Micro-blinds and nanocrystals electrochro- mic	Small activation and deactivation times Expensive indium-tin oxide is not needed Independent control of visible light and infrared radiation	Electrostatic stimulus is needed Longer time to be used is needed	^[5]^[6]^[7]^[8]^[9]
	Electrically tunable	Tunable transparency without affecting the glazing colour Control of transmittance of light incident Reduction of lighting energy consumption	At the beginning of the development A longer period of use is needed for the validation of its performance	^[14]^[15]
	Nanocrystal in-glass composites	Dual-band dynamic control (independent control of VL and NIR light) Relatively lower cost A wider range of control	Use for longer time is needed for validation of its performance	^[16]^[17]^[18]
	Electrokine-tic pixel	Separate modulation of colour and light transmittance Low switching times Control of privacy Lower cost	VL and IR radiation at a lower control range Use for a longer period is needed for validation of its performance	^[16]^[21]
	Elastomer- deformation tunable	Switching time less than a second Modulation of privacy Lower cost	No view in the opaque state VL and IR radiation at a lower control range	^[14]^[16]^[19]
	Liquid infill tunable	Short switching times Lower cost Shading modulation	VL and IR radiation at a lower control range Uneven appearance at partly filled state Bulky frames are needed for tanks	^[16]^[20]
	Localised Plasmon Resonance	High light transmission in the visible range High reflectance for NIR light Cooling energy consumption is reduced Transparency and reflectivity are modulated	At the beginning of the development A longer period of use is needed for the validation of its performance	^[10]^[11]^[12]^[13]

References

Fang, Y.; Hyde, T.; Hewitt, N.; Eames, P.C.; Norton, B. Thermal Performance Analysis of an Electrochromic Vacuum Glazing with Low Emittance Coatings. Sol. Energy 2010, 84, 516–525.
Fang, Y.; Hyde, T.J.; Hewitt, N. Predicted Thermal Performance of Triple Vacuum Glazing. Sol. Energy 2010, 84, 2132–2139.
Papaefthimiou, S.; Leftheriotis, G.; Yianoulis, P.; Hyde, T.J.; Eames, P.C.; Fang, Y.; Pennarun, P.Y.; Jannasch, P. Development of Electrochromic Evacuated Advanced Glazing. Energy Build. 2006, 38, 1455–1467.
Ghoshal, S.; Neogi, S. Advance Glazing System-Energy Efficiency Approach for Buildings a Review. Energy Procedia 2014, 54, 352–358.
Lamontagne, B.; Fong, N.R.; Song, I.-H.; Ma, P.; Barrios, P.; Poitras, D. Review of Microshutters for Switchable Glass. J. Micro/Nanolithography MEMS MOEMS 2019, 18, 040901.
Casini, M. Smart Windows for Energy Efficiency of Buildings. Int. J. Civ. Struct. Eng. IJCSE 2015, 2, 230–238.
Hillmer, H.; Al-Qargholi, B.; Khan, M.M.; Worapattrakul, N.; Wilke, H.; Woidt, C.; Tatzel, A. Optical MEMS-Based Micromirror Arrays for Active Light Steering in Smart Windows. Jpn. J. Appl. Phys. 2018, 57, 08PA07.
Mori, K.; Misawa, K.; Ihida, S.; Takahashi, T.; Fujita, H.; Toshiyoshi, H. A MEMS Electrostatic Roll-Up Window Shade Array for House Energy Management System. IEEE Photonics Technol. Lett. 2016, 28, 593–596.
Brzezicki, M. A Systematic Review of the Most Recent Concepts in Smart Windows Technologies with a Focus on Electrochromics. Sustainability 2021, 13, 9604.
Nanoparticles, D.S.; Kiyoto, N.; Hakuta, S.; Tani, T.; Naya, M.; Kamada, K. Development of a Near-Infrared Reflective Film Using Disk-Shaped Silver Nanoparticles. Fujifilm Res. Dev. 2013, 58, 55–58.
Tani, T.; Hakuta, S.; Kiyoto, N.; Naya, M. Transparent Near-Infrared Reflector Metasurface with Randomly Dispersed Silver Nanodisks. Opt. Express 2014, 22, 9262.
Granqvist, C.G. Smart Windows. Adv. Sci. Technol. 2008, 55, 205–212.
Naruse, M.; Tani, T.; Yasuda, H.; Tate, N.; Ohtsu, M.; Naya, M. Randomness in Highly Reflective Silver Nanoparticles and Their Localized Optical Fields. Sci. Rep. 2014, 4, 6077.
Shian, S.; David, R.; Clarke, D.R. Electrically tunable window device. Opt. Lett. 2016, 41, 1289–1292.
Rezaei, S.D.; Shannigrahi, S.; Ramakrishna, S. A Review of Conventional, Advanced, and Smart Glazing Technologies and Materials for Improving Indoor Environment. Sol. Energy Mater. Sol. Cells. 2017, 159, 26–51.
Casini, M. Active Dynamic Windows for Buildings: A Review. Renew. Energy 2018, 119, 923–934.
Llordés, A.; Garcia, G.; Gazquez, J.; Milliron, D.J. Tunable Near-Infrared and Visible-Light Transmittance in Nanocrystal-in-Glass Composites. Nature 2013, 500, 323–326.
DeForest, N.; Shehabi, A.; Selkowitz, S.; Milliron, D.J. A Comparative Energy Analysis of Three Electrochromic Glazing Technologies in Commercial and Residential Buildings. Appl. Energy 2017, 192, 95–109.
Zeng, S.; Zhang, D.; Huang, W.; Wang, Z.; Freire, S.G.; Yu, X.; Smith, A.T.; Huang, E.Y.; Nguon, H.; Sun, L. Bio-Inspired Sensitive and Reversible Mechanochromisms via Strain-Dependent Cracks and Folds. Nat. Commun. 2016, 7, 11802.
Carbonari, A.; Fioretti, R.; Naticchia, B.; Principi, P. Experimental Estimation of the Solar Properties of a Switchable Liquid Shading System for Glazed Facades. Energy Build. 2012, 45, 299–310.
Mukherjee, S.; Hsieh, W.L.; Smith, N.; Goulding, M.; Heikenfeld, J. Electrokinetic Pixels with Biprimary Inks for Color Displays and Color-Temperature-Tunable Smart Windows. Applied Optics. 2015, 54, 5603–5609.
Wolfe, D.; Goossen, K.W. Evaluation of 3D Printed Optofluidic Smart Glass Prototypes. Opt. Express 2017, 26, A85–A98.
Sekisui. Co. Air Sandwich. Available online: https://www.sekisui.co.jp/products/ (accessed on 1 April 2019).
Sekisui. Co. Light-collecting & Insulation Building Materials for Construction Use. Available online: https://www.jase-w.eccj.or.jp/technologies/ (accessed on 2 April 2019).
Sekisui Chemical Group. Environment-Contributing Products. 2019. Available online: www.se-kisui.co.jp/ (accessed on 7 April 2019).
Cuce, E.; Riffat, S.B. A State-of-the-Art Review on Innovative Glazing Technologies. Renew. Sustain. Energy Rev. 2015, 41, 695–714.
Cuce, E.; Cuce, P.M.; Young, C.H. Energy Saving Potential of Heat Insulation Solar Glass: Key Results from Laboratory and in-Situ Testing. Energy 2016, 97, 369–380.
Young, C.H.; Chen, Y.L.; Chen, P.C. Heat Insulation Solar Glass and Application on Energy Efficiency Buildings. Energy Build. 2014, 78, 66–78.
Favoino, F.; Loonen, R.C.G.M.; Michael, M.; De Michele, G.; Avesani, S. 5—Advanced fenestration—Technologies, performance and building integration. In Rethinking Building Skins; Gasparri, E., Brambilla, A., Lobaccaro, G., Goia, F., Andaloro, A., Sangiorgio, A., Eds.; Woodhead Publishing Series in Civil and Structural, Engineering; Woodhead Publishing: Cambridge, UK, 2022; pp. 117–154. ISBN 9780128224779.
Lien, A.G.; Hestnes, A.G.; Aschehoug, Ø. The Use of Transparent Insulation in Low Energy Dwellings in Cold Climates. Sol. Energy 1997, 59, 27–35.
Chow, T.t.; Li, C.; Lin, Z. Innovative Solar Windows for Cooling-Demand Climate. Sol. Energy Mater. Sol. Cells 2010, 94, 212–220.
PV-tech.org. Available online: https://www.pv-tech.org/editors-blog/making-pv-trans-parent-the-ultimate-bipv-solution (accessed on 23 August 2021).
Solarpanelscompany.com. Available online: https://solarpanelscompany.com/blog/turning-windows-into-solar-panels/ (accessed on 23 August 2021).
Kawashima, T.; Ezure, T.; Okada, K.; Matsui, H.; Goto, K.; Tanabe, N. FTO/ITO Double-Layered Transparent Conductive Oxide for Dye-Sensitized Solar Cells. J. Photochem. Photobiol. A Chem. 2004, 164, 199–202.
Zeng, K.; Zhu, F.; Hu, J.; Shen, L.; Zhang, K.; Gong, H. Investigation of Mechanical Properties of Transparent Conducting Oxide Thin Films. Thin Solid Film. 2003, 443, 60–65.
Baek, W.H.; Choi, M.; Yoon, T.S.; Lee, H.H.; Kim, Y.S. Use of Fluorine-Doped Tin Oxide Instead of Indium Tin Oxide in Highly Efficient Air-Fabricated Inverted Polymer Solar Cells. Appl. Phys. Lett. 2010, 96, 133506.
Roldán-Carmona, C.; Malinkiewicz, O.; Betancur, R.; Longo, G.; Momblona, C.; Jaramillo, F.; Camacho, L.; Bolink, H.J. High Efficiency Single-Junction Semitransparent Perovskite Solar Cells. Energy Environ. Sci. 2014, 7, 2968–2973.
Zhao, Y.; Meek, G.A.; Levine, B.G.; Lunt, R.R. Near-Infrared Harvesting Transparent Luminescent Solar Concentrators. Adv. Opt. Mater. 2014, 2, 606–611.
Henion, A.; Lunt, R. Transparent Solar Technology Represents Wave of the Future, Text It Michigan State University. Available online: https://msutoday.msu.edu/news/2017/transparentsolar-technology-represents-wave-of-the-future (accessed on 30 April 2019).

© Text is available under the terms and conditions of the Creative Commons Attribution (CC BY) license; additional terms may apply. By using this site, you agree to the Terms and Conditions and Privacy Policy.

Upload a video for this entry

Information

Subjects: Engineering, Civil

Contributors MDPI registered users' name will be linked to their SciProfiles pages. To register with us, please refer to https://encyclopedia.pub/register :

Michalis Michael

Fabio Favoino

Qian Jin

Alessandra Luna-Navarro

Mauro Overend

View Times: 328

Update Date: 24 Oct 2023

Table of Contents

Video Upload Options

Confirm