Yuri P Sukhorukov
 -- 2590 2022-12-19 11:37:05 |
2 layout
Camila Xu
 Meta information modification 2590 2022-12-20 07:30:42 |

Video Upload Options

Do you have a full video?
Send video materials Upload full video

Confirm

Are you sure to Delete?
Yes No
Cite
If you have any further questions, please contact Encyclopedia Editorial Office.
Telegin, A.;  Sukhorukov, Y. Nanocrystalline Magnetic Semiconductors for Spintronics. Encyclopedia. Available online: https://encyclopedia.pub/entry/38954 (accessed on 08 May 2024).
Telegin A,  Sukhorukov Y. Nanocrystalline Magnetic Semiconductors for Spintronics. Encyclopedia. Available at: https://encyclopedia.pub/entry/38954. Accessed May 08, 2024.
Telegin, Andrei, Yurii Sukhorukov. "Nanocrystalline Magnetic Semiconductors for Spintronics" Encyclopedia, https://encyclopedia.pub/entry/38954 (accessed May 08, 2024).
Telegin, A., & Sukhorukov, Y. (2022, December 19). Nanocrystalline Magnetic Semiconductors for Spintronics. In Encyclopedia. https://encyclopedia.pub/entry/38954
Telegin, Andrei and Yurii Sukhorukov. "Nanocrystalline Magnetic Semiconductors for Spintronics." Encyclopedia. Web. 19 December, 2022.
Nanocrystalline Magnetic Semiconductors for Spintronics
Edit
This entry is adapted from the peer-reviewed paper 10.3390/magnetochemistry8120173

Сhallenge for spintronics is to find new ways for the control of electronic phenomena and magnetic properties of solids at nanoscale. Some promising aspects are connected with developing new materials. The research highlights the areas devoted to the creation of new functional materials for spintronics based on magnetic semiconductors and demonstrates the technical possibilities of creating various devices, in particular, a maser, a p-n junction with a colossal magnetoresistance, a spin valve, a magnetic lens, modulators, spin wave amplifier, etc. A magnetic semiconductor is a magnetic material that, in terms of specific conductivity, occupies an intermediate position between a conductor and an insulator, and has a band gap comparable to ~kBT. Most known magnetic semiconductors (SC) are either oxides or chalcogenides (sulfides, selenides and tellurides) of 3d transition metals, rare earth 4f metals or a combination. Spintronics (spin electronics) studies spin current transfer (spin-polarized transport) in condensed media, including contact structures, heterostructures, superlattices and multilayers. Much attention is paid to the mechano-physical methods of obtaining of high-density transparent nanoceramics based on magnetic semiconductors. The potential possibility of using nanoceramics as an absorber of solar energy, as well as in modulators of electromagnetic radiation, is also presented. The THz magneto-optics in magnetic semiconductors is shown to be beneficial to the intensively developing fields of spintronics – ultrafast magnetooptics and magnetophotonics in magnetic semiconductors.

spintronics magnetic semiconductors complex magnetic oxides

1. Introduction

A magnetic semiconductor is a magnetic material that, in terms of specific conductivity, occupies an intermediate position between a conductor and an insulator, and has a band gap comparable to ~kBT. Most known magnetic semiconductors (SC) are either oxides or chalcogenides (sulfides, selenides and tellurides) of 3d transition metals, rare earth 4f metals or a combination. The strong interaction of mobile charge carriers with the localized magnetic moments of the d- and f-shells leads to a number of features of the electrical and optical properties of magnetic SC that are absent in non-magnetic semiconductor [1][2][3][4][5][6][7][8][9].
There are several properties typical only for magnetic SC. For example, in ferromagnetic semiconductors (europium chalcogenides, chromium chalcogenide spinel, etc.), with either a decrease in temperature, application of an external magnetic field or both, a giant (up to ~0.5 eV) shift towards long wavelengths of the edge of optical absorption and photoconductivity is observed, the so-called giant red shift of the absorption edge. Meanwhile, near the Curie temperature they can exhibit a colossal magnetoresistance (CMR) effect and a metal-insulator (MI) transition. Giant magneto-optical (MO) effects were found in magnetic SCs in a wide visible and infrared (IR) spectral range (Faraday and Kerr effects, magnetotransmission, magnetoreflection, magnetic linear and circular dichroism, etc.) [10][11][12][13][14]. Moreover, magnetic SCs are the basis of high-temperature superconductors and without considering the properties of magnetic semiconductors, it would be impossible to construct a theory of high temperature superconductivity (HTSC). By changing the concentration of current carriers (by temperature, doping, light irradiation, application of electric field, current injection, etc.), it is possible to easily change the magnetic properties of SCs [1][2][3][4][5][6][7][15][16][17][18][19][20]. On the contrary, their electrical and optical properties can be controlled by an external magnetic field, which in relation to the intense development of electronics and magnetophotonics is of high practical interest [21][22][23][24][25]. For example, the presence of a large magnetocaloric effect in manganites makes magnetic SCs promising materials for creating refrigerators [26]. Large MO effects and the presence of the MI transition in magnetic oxides made it possible to create a wide range of optoelectronic devices, such as modulators, magnetic field visualization sensors, MO filters, shutters, attenuators, bolometers, thermochromic materials, etc. [27][28][29][30][31][32][33]. The electrical properties of perovskites and cobaltites allowed for using them as cathodes in solid oxide fuel cells, opening new possibilities for creating alternative energy sources with a high efficiency of ~90% [34][35]. The medical direction of using magnetic SCs is also very important, for example, as a material for artificial local heating of a selected area of the body-hyperthermia [36][37][38][39][40].
Unlike non-magnetics, magnetic semiconductors have the important property of dependence of the band structure on the orientation of the electron spin. In other words, in magnetic SCs, the band gap is not the same for electrons with different spin orientations (Figure 1).
Magnetochemistry 08 00173 g001
Figure 1. Schematic representation of changes in the band structure of a magnetic SCs depending on the orientation of the electron spin (right), which are absent in the band structure of a non-magnetic semiconductor (left).
The presence of bands with different orientations of the of charge carriers’ spins (spin-polarized bands) made it possible to control the charge current in magnetic SCs, depending on the mutual orientation of the magnetic field, current direction and an applied voltage. It is important that the flow of spin-oriented (spin-polarized) charged particles retains its properties not only in magnetic SCs, but also in other magnetic or non-magnetic media at a sufficiently level. In non-magnetic semiconductors, spins with different orientations compensate each other, thus the full spin current is zero and there is only the current of charged particles. The possibility of creating and manipulating a flow of spin-polarized charge carriers in magnetic SCs has opened broad prospects for creating new functional materials and various electronic devices. Spintronics (spin electronics) studies spin current transfer (spin-polarized transport) in condensed media, including contact structures, heterostructures, superlattices and multilayers. In all these cases, the source of spin-polarized electrons (spin injector) is a ferromagnet (metal or semiconductor), which in the magnetized state has the spontaneous spin ordering of the current carriers [15][16][17][18][19][20][21][22][23][24][25]. In ferromagnetic SCs, the levels of spin polarization can reach higher values (up to almost 100%) than in metals (up to 10%) [41]. In non-magnetic SCs in an external magnetic field, the Zeeman splitting of the conduction band occurs with the formation of two energy sublevels. When spin-polarized electrons are injected from a magnetic SC into a non-magnetic SC, controlled transitions to both the upper and lower energy levels become possible, which allows controlling the charge current by an external influence. This area of physics has been intensively developed over the past 30 years [42][43][44][45][46][47][48][49].
At the same time, current spintronic devices or their components are generally extremely small (~10−7 m) and can be classified as nanomaterials. When the dimensions of device components or a material are reduced to a nanometer scale (for example, films, thin-film structures, fibers, powders and high-density ceramics), their mechanical properties are changed significantly, thermal conductivity is increased and a change of fundamental characteristics such as the melting temperature and Debye temperature were also reported. In a magnetic SC, during the transition to the nanoscale, the electronic structure is drastically changed followed by the appearance of various anomalies in its magnetic and transport properties [50][51].

2. Nanocrystalline Magnetic Semiconductors—New Functional Materials for Spintronics

Nanocrystalline magnetic SCs are of interest both for fundamental problems of condensed matter physics and for practical applications, due to the appearance of new properties, when the particle size of a SC is reduced to the nanometer scale [52][53][54]. For the past decade the development of magnetic materials, particularly manganites and ferrites in nano-form, has undergone a fast evolutionary growth as strategic materials in spintronics and sensor applications [55][56][57][58]. At the same time, the concentration of defects in nanomaterials is much higher than in equilibrium single or polycrystals. This factor also significantly determines the properties of nanomaterials, transforming nanosized magnetic SCs into multifunctional materials. The features and the possibility of using nanosized ferromagnetic SCs as functional materials are well studied. Meanwhile, similar features are also manifested in nanosized antiferromagnetic SCs. For example, the presence of linear dichroism (~50%) allows for the use of antiferromagnetic semiconductor CuO as polarizers of infrared radiation [59]. Electron-field emission in CuO nanofibers is recommended for use in displays [60]. Irradiated nanocrystalline CuO oxides can accelerate reaction-catalytic effects in the production, for example, of alcohols. Moreover, the synthesis rate, for example, of copper phthalocyanine, can be controlled by a magnetic field at room temperature [61][62]. Nanocrystalline CuO is used in electronics as a buffer layer in complex thin-film electronic nanodevices [63]. Moreover, it can enhance an electrochemical activity, which is promising for use as electrodes in lithium current sources [64] and as an analyzer of carbon dioxide concentration [65]. However, there are problems in obtaining high-quality optically transparent SC nanomaterials of various types (powder, ceramic, fiber, and film).

2.1. High-Density Magneto-Optical Nanoceramics

For creating ceramics from a nanocrystalline material, important conditions are the preservation of the composition and size of compacted particles. Since magnetic SCs are multicomponent compounds, the production of high-density nanoceramics is rather complicated. To create nanoceramics, dynamic and static loading methods for obtaining high-density bulk nanomaterials are used. Static loading refers to the method of severe plastic deformation—shearing under pressure of at least 8 GPa. In this method, the number of distortions is determined not only by the applied high static pressure, but also by the angle of rotation of the anvils. For the creation of nanoceramics based on magnetic SCs, special high-pressure chambers were developed [66][67]. For example, using the static deformation method, LaMnO3+y nanoceramics with a density of 99% and grain sizes close to those of a nanopowder can be obtained [68]. It was also found that at high degrees of deformation and small crystallite sizes, the magnitude of micro-deformations in nanoceramics decreases, which may be due to more efficient relaxation of lattice stresses by grain boundary sliding with a decrease in crystallite size.
Dynamic loading refers to the method of explosive action on a low-density (polycrystalline powder compact) coarse-grained material made of a magnetic SC by spherically converging shock waves, as well as pressing axially-symmetric workpieces under the action of an explosion [69][70]. When exposed to spherically converging shock waves, the material is placed in a spherical steel hermetic case, in which, at the moment of a spherical explosion, the material is simultaneously compressed in all ways and a nanostructure is formed. During explosive pressing of axially-symmetric workpieces, the material is placed in a steel cylinder, in which, at the moment of explosion, the detonation wave propagates along the generatrix axis. The integrity of specially designed metal covers is not violated, which protects the resulting nanoceramics from contamination. The created nanoceramics show high temperature- and time-stability. As a result, the advantage of the developed methods is the ease of implementation, the combination of the creation of a nanostructure and material compaction in a single process, the production of high-density (~99%) stable nanosized materials and the absence of external contaminants. The results can be used for obtaining nanoceramics from a wide range of materials. Some fragments of real SC nanoceramics prepared by various methods are shown in Figure 2. It can be seen that the described methods allow obtaining dense nanomaterials of quite large geometrical sizes.
Magnetochemistry 08 00173 g017
Figure 2. High-density nanoceramics obtained (1) by the method of spherically converging shock waves (CuO); (2) by the method of cylindrical explosive loading (LaMnO3+y); (3) by the method of static pressure with shear (Y3Fe5O12).
The promising technological process for creating high-quality dense nanoceramics of magnetic SC based on binary and even ternary compounds, such as CuO, Cu2O, Mn3O0, ZrO2, ZnSe, LaMnO3+y, FeBO3, Y3Fe5O12, etc., has been developed at the Institute of Metal Physics UB of RAS, Russia. The average particle size varies from 10 to 100 nm. The crystal structure, microstructure, imperfection, microhardness, magnetic, optical and other properties of the obtained nanomaterials have been studied in [71][72][73][74][75][76]. It has been established that the specific defectiveness of nanoceramics of magnetic oxides is ascribed to either the high concentration of oxygen vacancies, their agglomerates concentrated at the boundaries of crystallites or both, which determines (along with the nanostructure) the nonequilibrium nature of nanoceramics and the features of their mechano-chemical properties. For example, anomalies in the magnetic properties, a decrease of the forbidden band gap and a negative thermal expansion for nanoceramics were found.
In the creation of new functional nanomaterials, the production of transparent nanoceramics is very important. The aforementioned techniques made it possible to create transparent nanoceramics with a high Faraday effect, i.e., the rotation of the plane of polarization of linearly polarized light passing through nanoceramics under the influence of an external magnetic field.

2.2. Nanocrystalline Y3Fe5O12 as a New Magneto-Optical Material

An optically transparent high-density (density 99.6%) Y3Fe5O12 (YIG) nanoceramic (Figure 2) was obtained by means of a sheared static pressure of ~50 GPa. The authors of [77][78] showed that the absorption coefficient of nanoceramic Y3Fe5O12 in the transparency window is below 50 cm–1. It is mainly due to light scattering by crystallites and varies slightly with reduction of grain size. As the degree of deformation of YIG nanoceramics increases, the concentration of defects changes and the magnitude of micro-deformations decreases. However, these factors have only little effect on the absorption coefficient in the transparency window. Figure 3 shows that the value of the Faraday rotation for nanoceramics of YIG is only 1.5 times less than that for the YIG single crystals and exceeds 50 deg/cm. It is important that as the grain size decreases, the Faraday effect increases, and then, starting from a grain size of 21 nm, the effect decreases again. The observed increase of the Faraday effect in nanosized magnetic SCs was theoretically explained in [79]. It was shown that electric dipole transitions in clusters of mixed valences of 3d ions in nanosized magnetic materials with the structure of perovskite and garnet can lead to a resonant enhancement of the MO activity in the limited area of deformations. Finally, transparent high-density nanoceramics based on magnetic SCs can be widely used for creation of various high-frequency and microwave sensors and shields and MO devices, in particular, IR radiation modulators, displays, etc.
Magnetochemistry 08 00173 g018
Figure 3. Specific Faraday rotation of nanostructured YIG samples with different crystallite sizes, SC–YIG single crystal.

2.3. Nanocrystalline CuO as a Material for Selective Solar Energy Absorbers

In relation to the problem of energy saving, great interest has arisen in alternative green energy sources, in particular, in selective absorbers of EM radiation and thermal converters of solar energy with coatings based on selective absorbers [80]. A selective solar energy absorber must meet certain requirements. For example, it should have a large absorption coefficient and a low reflection coefficient in the spectral range of solar radiation—in the energy range E > 0.5 eV. On the other hand, the absorber should have low electromagnetic energy emission or high reflectance at E < 0.5 eV. In other words, a selective absorber must absorb the energy of the radiation source as efficiently as possible but minimally re-emit it back into the atmosphere in the IR region of the spectrum. It was shown that copper oxides [81][82][83] can be used as selective absorbers in solar energy collectors with working temperatures up to T~500 °C. However, these materials do not meet the above conditions well, since they have a large forbidden gap. The authors of [84][85] demonstrated that this problem can be solved by changing the absorption spectrum of CuO practically without changing the refractive index when the copper oxide is transferred to the nanocrystalline state. Figure 4 shows the optical density (absorption) spectra for CuO single-crystal, nanopowder and nanoceramic, respectively.
Magnetochemistry 08 00173 g019
Figure 4. Optical density spectra of CuO samples at T = 295 K: SC—single crystal, NP—nanopowder, NC—nanoceramics.
The reasons for such strong changes in the spectra of CuO nanopowders and nanoceramics in the region of the main fundamental absorption edge were associated with a high level of defects and micro-deformations as well as with the behavior of strongly correlated materials in the nanocrystalline state. In CuO nanoceramics the observed energy changes that result in a significant decrease in the effective high-energy edge of the transparency window from 1.5 to 0.5 eV are the most pronounced [52][53].
It is necessary to note that there are many other directions in the development of technologies for obtaining nanoceramics and nanocomposites based on magnetic SCs and their possible applications in spintronics, nanophotonics, biology and medicine [86][87][88][89][90].

References

  1. Methfessel, S.; Mattis, D.C. Magnetic Semiconductors; Wijn, H.P.J., Ed.; Springer: Berlin/Heidelberg, Germany; New York, NY, USA, 1968; pp. 389–562.
  2. Seeger, K. Semiconductor Physics; Springer Science & Business Media: Berlin/Heidelberg, Germany, 2013.
  3. Nagaev, E.L. Physics of Magnetic Semiconductor; Mir Publishers: Moscow, Russia, 1983; p. 388.
  4. Grundmann, M. Physics of Semiconductors; Springer: Berlin/Heidelberg, Germany, 2010; pp. 401–472.
  5. Belov, K.P.; Tretyakov, Y.D.; Gordeev, I.V.; Koroleva, L.I.; Kesler, Y.A. Magnetic Semiconductors—Chalcogenide Spinels; Moscow State University: Moscow, Russia, 1981.
  6. Nagaev, E.L. Colossal Magnetoresistance and Phase Separation in Magnetic Semiconductors; Imperial College Press: London, UK, 2002; p. 1.
  7. Koroleva, L.I. Magnetic Semiconductors; Moscow State University: Moscow, Russia, 2003.
  8. Barner, K. New Trends in the Characterization of CMR-Manganites and Related Materials; Research Signpost: Gottingen, Germany, 2005; p. 1.
  9. Dionne, G.F. Magnetic Oxides; Springer: New York, NY, USA, 2009; p. 15.
  10. Zvezdin, A.K.; Kotov, V.A. Modern Magnetooptics and Magnetooptical Materials; CRC Press: Boca Raton, FL, USA, 1997.
  11. Telegin, A.V.; Sukhorukov, Y.P.; Bessonov, V.D.; Naumov, S.V. The Faraday effect in CoFe2O4 spinel ferrite in the IR range. Tech. Phys. Lett. 2019, 45, 601–604.
  12. Kimel, A.; Zvezdin, A.; Sharma, S.; Shallcross, S.; De Sousa, N.; Garcia-Martin, A.; Vavassori, P. The 2022 magneto-optics roadmap. J. Phys. D Appl. Phys. 2022, 55, 463003.
  13. Fumagalli, P.; Schoenes, J. Magneto-Optics; De Gruyter: Berlin, Germany, 2021.
  14. Telegin, A.V.; Sukhorukov, Y.P.; Loshkareva, N.N.; Mostovshchikova, E.V.; Bebenin, N.G.; Gan’shina, E.A.; Granovsky, A.B. Giant magnetotransmission and magnetoreflection in ferromagnetic materials. JMMM 2015, 383, 104–109.
  15. Morgunov, R.B.; Dmitriev, A.I. Spin dynamics in magnetic semiconductor nanostructures. Phys. Solid State 2009, 51, 1985.
  16. Fetisov, Y.K.; Sigov, A.S. Spintronics: Physical foundations and devices. Radioelektron. Nanosistemy Inf. Tehnol. RENSIT 2018, 10, 343–356.
  17. Sato, K.; Katayama-Yoshida, H. Design of colossal solubility of magnetic impurities for semiconductor spintronics by the Co-doping method. Jpn. J. Appl. Phys. 2007, 46, L1120.
  18. Volkov, N.V. Spintronics: Manganite-based magnetic tunnel structures. Phys. Uspekhi 2012, 55, 250.
  19. Ivanov, V.A. Diluted magnetic semiconductors and spintronics. Bull. Russ. Acad. Sci. Phys. 2007, 71, 1610–1612.
  20. Yamada, Y.; Ueno, K.; Fukumura, T.; Yuan, H.T.; Shimotani, H.; Iwasa, Y.; Kawasaki, M. Electrically induced ferromagnetism at room temperature in cobalt-doped titanium dioxide. Science 2011, 332, 1065–1067.
  21. Rizal, C.; Shimizu, H.; Mejía-Salazar, J.R. Magneto-Optics effects: New trends and future prospects for technological developments. Magnetochemistry 2022, 8, 94.
  22. Awschalom, D.D.; Flatté, M.E. Challenges for semiconductor spintronics. Nat. Phys. 2007, 3, 153–159.
  23. Akinaga, H.; Ohno, H. Semiconductor spintronics. IEEE Trans. Nanotechnol. 2002, 1, 19–31.
  24. Hirohata, A.; Sukegawa, H.; Yanagihara, H.; Žutić, I.; Seki, T.; Mizukami, S.; Swaminathan, R. Roadmap for emerging materials for spintronic device applications. IEEE Trans. Magn. 2015, 51, 1–11.
  25. Bibes, M.; Barthelemy, A. Oxide spintronics. IEEE Trans. Electron Devices 2007, 54, 1003–1023.
  26. Gschneidner, K.A.; Pecharsky, V.K.; Pecharsky, A.O. Recent developments in magnetocaloric materials. Rep. Prog. Phys. 2005, 68, 1479.
  27. Loshkareva, N.N.; Sukhorukov, Y.P.; Gizhevskii, B.A.; Samokhvalov, A.A. Modulator of IR emission on magnetic semiconductors. Pisma V Zhurnal Tekhnicheskoi Fiz. 1989, 15, 83–86. (In Russian)
  28. Loshkareva, N.N.; Sukhorukov, Y.P.; Samokhvalov, A.A.; Shuvalov, V.A.; Kartashev, E.V.; Chebotaev, N.M.; Naumov, S.V.; Aminov, T.G. Magnet-controlled band IR filter. Pisma V Zhurnal Tekhnicheskoi Fiz. 1992, 18, 10–13. (In Russian)
  29. Sukhorukov, Y.P.; Loshkareva, N.N.; Samokhvalov, A.A.; Tugushev, S.N. Magnetooptic infrared modulator in the Voigt geometry. Tech. Phys. Lett. 1996, 22, 43–45.
  30. Sukhorukov, Y.P.; Loshkareva, N.N.; Gan’shina, E.A.; Kaul, A.R.; Gorbenko, O.Y.; Fatieva, K.A. Giant change in the optical absorption of an La0.35Pr0.35Ca0.3MnO3 film near a metal-insulator transition and its possible application. Tech. Phys. Lett. 1999, 25, 551–554.
  31. Sukhorukov, Y.P.; Loshkareva, N.N.; Telegin, A.V.; Mostovshchikova, E.V.; Kuznetsov, V.L.; Kaul, A.R.; Vinogradov, A.N. IR radiation modulator based on the effect of magnetotransmission in lanthanum manganite operating near room temperature. Tech. Phys. Lett. 2003, 29, 904–906.
  32. Goyal, A.; Rajeswari, M.; Shreekala, R.; Lofland, S.E.; Bhagat, S.M.; Boettcher, T.; Kwon, C.; Ramesh, R.; Venkatesan, T. Material characteristics of perovskite manganese oxide thin films for bolometric applications. Appl. Phys. Lett. 1997, 71, 2535–2537.
  33. Heiras, J.; Pichardo, E.; Mahmood, A.; López, T.; Pérez-Salas, R.; Siqueiros, J.M.; Blanco, O.; Castellanos, M. Thermochromism in (Ba,Sr)-Mn oxides. J. Phys. Chem. Solids 2002, 63, 591–595.
  34. Sinitsyn, V.V.; Burmistrov, I.N.; Abrosimova, G.E.; Klinkova, L.A.; Bredikhin, S.I. Phase transitions and ionic conductivity of BaBixO1.5x+1 (x ≥ 5) oxides. Ionics 2006, 12, 69–71.
  35. Burmistrov, I.N.; Droshshin, O.A.; Istomin, S.Y.; Sinitsyn, V.V.; Antipov, E.V.; Bredikhin, S.I. Sr0.75Y0.25Co0.5Mn0.5O3 − y perovskite cathode for solid oxide fuel cells. J. Electrochem. Soc. 2009, 156, 1212.
  36. Martinez-Boubeta, C.; Simeonidis, K.; Oró, J.; Makridis, A.; Serantes, D.; Balcells, L. Finding the limits of magnetic hyperthermia on core-shell nanoparticles fabricated by physical vapor methods. Magnetochemistry 2021, 7, 49.
  37. Moroz, P.; Jones, S.K.; Gray, B.N. Magnetically mediated hyperthermia: Current status and future directions. Int. J. Hyperth. 2002, 18, 267.
  38. Kuznetsov, A.A.; Shlyakhtin, O.A.; Brusentsov, N.A.; Kuznetsov, O.A. Smart mediators for self-controlled inductive heating. Eur. Cells Mater. 2002, 3, 75–77.
  39. Pollert, E.; Knižek, K.; Maryško, M.; Kašpar, P.; Vasseur, S.; Duguet, E. New Tc-tuned magnetic nanoparticles for self-controlled hyperthermia. JMMM 2007, 316, 122–125.
  40. Melnikov, O.V.; Gorbenko, O.Y.; Markelova, M.N.; Kaul, A.R.; Atsarkin, V.A.; Demidov, V.V.; Soto, C.; Roy, E.J.; Odintsov, B.M. Ag-doped manganite nanoparticles: New materials for temperature-controlled medical hyperthermia. J. Biomed. Mater. Res. 2009, 91A, 1048–1055.
  41. Kessler, J. Polarized Electrons; Springer Science & Business Media: Berlin/Heidelberg, Germany, 2013; p. 299.
  42. Gregg, J.F.; Petej, I.; Jouguelet, E.; Dennis, C. Spin electronics—A review. J. Phys. D Appl. Phys. 2002, 35, R121.
  43. Parkin, S.; Jiang, X.; Kaiser, C.; Panchula, A.; Roche, K.; Samant, M. Magnetically engineered spintronic sensors and memory. Proc. IEEE 2003, 91, 661–680.
  44. Borukhovich, A.S. Quantum tunneling in multilayers and heterostructures with ferromagnetic semiconductors. Phys. Uspekhi 1999, 42, 653.
  45. Zutic, I.; Fabian, J.; Das Sarma, S. Spintronics: Fundamentals and applications. Rev. Mod. Phys. 2004, 76, 323.
  46. Ziese, M. Extrinsic magnetotransport phenomena in ferromagnetic oxides. Rep. Prog. Phys. 2002, 65, 143.
  47. Dorr, K. Ferromagnetic manganites: Spin-polarized conduction versus competing interactions. J. Appl. Phys. 2006, 39, R125.
  48. Haghiri-Gosnet, A.-M.; Renard, J.-P. CMR manganites: Physics, thin films and devices. J. Appl. Phys. 2003, 36, R127.
  49. Ohring, M. Materials Science of Thin Films: Depositon & Structure; Elsevier: Amsterdam, The Netherlands, 2001.
  50. Kodama, R.H. Magnetic nanoparticles. JMMM 1999, 200, 359–372.
  51. Arbuzova, T.I.; Gizhevskii, B.A.; Naumov, S.V.; Korolev, A.V.; Arbuzov, V.L.; Shal’nov, K.V.; Druzhkov, A.P. Temporal changes in magnetic properties of high-density CuO nanoceramics. JMMM 2003, 258, 342–344.
  52. Nasirpouri, F.; Nogaret, A. (Eds.) Nanomagnetism and Spintronics: Fabrication, Materials, Characterization and Applications; World Scientific: Singapore, 2010; 400p.
  53. Zimnyakova, P.E.; Ignatyeva, D.O.; Karki, D.; Voronov, A.A.; Shaposhnikov, A.N.; Berzhansky, V.N.; Belotelov, V.I. Two-dimensional array of iron-garnet nanocylinders supporting localized and lattice modes for the broadband boosted magneto-optics. Nanophotonics 2022, 11, 119–127.
  54. Omelyanchik, A.; Villa, S.; Singh, G.; Rodionova, V.; Laureti, S.; Canepa, F.; Peddis, D. Magnetic properties of Bi-magnetic core/shell nanoparticles: The case of thin shells. Magnetochemistry 2021, 7, 146.
  55. Gupta, A.; Zhang, R.; Kumar, P.; Kumar, V.; Kumar, A. Nano-structured dilute magnetic semiconductors for efficient spintronics at room temperature. Magnetochemistry 2020, 6, 15.
  56. Dmitriev, A.I.; Talantsev, A.D.; Zaitsev, S.V.; Koplak, O.V.; Morgunov, R.B. Nano-and heterostructures of magnetic semiconductors for spintronics. Russ. Chem. Bull. 2011, 60, 1051–1057.
  57. Silva, A.S.; Guimarães, É.V.; Sales, T.O.; Silva, W.S.; Batista, E.A.; Jacinto, C.; Silva, R.S. Nanostructured magnetic semiconductors. In Fundamentals of Low Dimensional Magnets; CRC Press: Boca Raton, FL, USA, 2022; pp. 23–39.
  58. Kotnala, R.K.; Shah, J. Ferrite materials: Nano to spintronics regime. In Handbook of Magnetic Materials; Elsevier: Amsterdam, The Netherlands, 2015; Volume 23, pp. 291–379.
  59. Loshkareva, N.N.; Sukhorukov, Y.P.; Gizhevskii, B.A.; Naumov, S.V.; Samokhvalov, A.A.; Moskvin, A.S.; Belykh, T.A. Polar-center phase nuclei in He+-irradiated CuO single crystals. Phys. Solid State 1998, 40, 383–388.
  60. Lin, H.H.; Wang, C.Y.; Shih, H.C.; Chen, J.M.; Hsieh, C.T. Characterizing well-ordered CuO nanofibrils synthesized through gas-solid reactions. J. Appl. Phys. 2004, 95, 5889–5895.
  61. Baru, V.G.; Volkenshtein, F.F. Influence of Irradiation on the Surface Properties of Semiconductors; Nauka: Moscow, Russia, 1978.
  62. Yermakov, A.Y.; Feduschak, T.A.; Sedoi, V.S.; Uimin, M.A.; Mysik, A.A. Magneto-modified catalyst on the base of nanocrystalline CuO. JMMM 2004, 272, 2445–2447.
  63. Ohno, H.; Chiba, A.D.; Matsukura, A.F.; Omiya, T.; Abe, E.; Dietl, T.; Ohtani, K. Electric-field control of ferromagnetism. Nature 2000, 408, 944–946.
  64. Morales, J.; Sánchez, L.; Martín, F.; Ramos-Barrado, J.R.; Sánchez, M. Nanostructured CuO thin film electrodes prepared by spray pyrolysis: A simple method for enhancing the electrochemical performance of CuO in lithium cells. Electrochim. Acta 2004, 49, 4589–4597.
  65. Wei, Q.; Luo, W.D.; Liao, B.; Liu, Y.; Wang, G. Giant capacitance effect and physical model of nano crystalline CuO–BaTiO3 semiconductor as a CO2 gas sensor. J. Appl. Phys. 2000, 88, 4818–4824.
  66. Pilyugin, V.P.; Gizhevskii, B.A.; Patselov, A.M.; Chernyshev, E.G.; Lisin, V.L. Plastic deformation Chamber at Low Temperatures. Russian Federation patent No 61882, Bull. No 7, 10 March 2007. Available online: https://rusneb.ru/catalog/000224_000128_0000061882_20070310_U1_RU/ (accessed on 11 September 2022).
  67. Pilyugin, V.P.; Chernyshev, E.G.; Patselov, A.M.; Gizhevskii, B.A. High Pressure Chamber for Spectroscopic Analysis. Russian Federation Patent No 60727, Bull. No 3, 27 January 2007. (In Russian). Available online: https://rusneb.ru/catalog/000224_000128_0000060727_20070127_U1_RU/ (accessed on 11 September 2022).
  68. Arbuzova, T.I.; Voronin, V.I.; Gizhevskii, B.A.; Naumov, S.V.; Arbuzov, V.L. An inhomogeneous paramagnetic state of the LaMnO3+δ nanoceramics prepared by shock-wave loading. Phys. Solid State 2010, 52, 1217–1226.
  69. Samokhvalov, A.A.; Sukhorukov, Y.P. Effect of hot carriers on the Raman spectra of the magnetic semiconductors CdCr2Se4 and HgCr2Se4. JETP Lett. 1982, 35, 212.
  70. Gizhevskii, B.A.; Galakhov, V.R.; Kozlov, E.A. Effects of shock-wave loading in oxides. Petrology 2012, 20, 317–330.
  71. Gizhevskii, B.A.; Sukhorukov, Y.P.; Moskvin, A.S.; Loshkareva, N.N.; Mostovshchikova, E.V.; Ermakov, A.E.; Gaviko, V.S. Anomalies in the optical properties of nanocrystalline copper oxides CuO and Cu2O near the fundamental absorption edge. JETP 2006, 102, 297–302.
  72. Krynetskii, I.B.; Gizhevskii, B.A.; Naumov, S.V.; Kozlov, E.A. Size effect of the thermal expansion of nanostructural copper oxide. Phys. Solid State 2008, 50, 756–758.
  73. Vykhodets, V.B.; Vykhodets, E.V.; Gizhevskii, B.A.; Zakharov, R.G.; Kozlov, E.A.; Kurennykh, T.E.; Petrova, S.A.; Trakhtenberg, I.S.; Fishman, A.Y. Grain boundary self-diffusion of tracer 18O atoms in nanocrystalline oxide LaMnO3+δ. JETP Lett. 2008, 87, 115–119.
  74. Arbuzova, T.I.; Naumov, S.V.; Kozlov, E.A.; Arbuzov, V.L.; Shal’nov, K.V.; Gizhevskii, B.A.; Voronin, V.I. Influence of structural defects on magnetic properties of the submicrometer ceramic Mn3O4. JETP 2006, 102, 931–937.
  75. Gizhevsky, B.A.; Kozlov, E.A.; Ermakov, A.E.; Lukin, N.V.; Naumov, S.V.; Samokhvalov, A.A. Microstructure of CuO after shock-loading and milling. Phys. Met. Metallogr. 2001, 92, 153–157.
  76. Druzhkov, A.P.; Gizhevskii, B.A.; Arbuzov, V.L.; Kozlov, E.A.; Shalnov, K.V.; Naumov, S.V.; Perminov, D.A. Electronic and structural properties of micro-and nanometre-sized crystalline copper monoxide ceramics investigated by positron annihilation. J. Phys. Condens. Matter 2002, 14, 7981.
  77. Gizhevskii, B.A.; Sukhorukov, Y.P.; Gan’shina, E.A.; Loshkareva, N.N.; Telegin, A.V.; Lobachevskaya, N.I.; Gaviko, V.S.; Pilyugin, V.P. Optical and magneto-optical properties of nanostructured yttrium iron garnet. Phys. Solid State 2009, 51, 1836–1842.
  78. Makhnev, A.A.; Gizhevskii, B.A.; Nomerovannaya, L.V. Optical spectra of nanoceramics of yttrium-iron garnet Y3Fe5O12 obtained by the method of intense plastic deformation. JETP Lett. 2010, 91, 79–82.
  79. Falkovskaya, L.D.; Fishman, A.Y.; Mitrofanov, V.Y.; Ivanov, M.A. Random fields in disordered magnetics with Jahn-Teller ions. In Proceedings of the Fifth International Conference on Mathematical Modeling and Computer Simulations of Materials Technologies, Ariel, Israel, 21–23 July 2015; pp. 1–202.
  80. Agnihotri, O.P.; Gupta, B.K. Solar Selective Surfaces; Wiley-Interscience: New York, NY, USA, 1981; 232p.
  81. Tesfamichael, T.; Hoel, A.; Wäckelgard, E.; Niklasson, G.A.; Gunde, M.K.; Orel, Z.C. Optical characterization and modeling of black pigments used in thickness-sensitive solar-selective absorbing paints. Sol. Energy 2001, 69, 35–43.
  82. Van Buskirk, O.R. Solar Selective Surfaces. U.S. Patent No 4310596, 12 January 1982. Available online: https://www.freepatentsonline.com/4310596.html (accessed on 11 September 2022).
  83. Karlsson, B.; Ribbing, C.G.; Roos, A.; Valkonen, E.; Karlsson, T. Optical properties of some metal oxides in solar absorbers. Phys. Scr. 1982, 25, 826.
  84. Sukhorukov, Y.P.; Gizhevskii, B.A.; Mostovshchikova, E.V.; Yermakov, A.Y.; Tugushev, S.N.; Kozlov, E.A. Nanocrystalline copper oxide for selective solar energy absorbers. Tech. Phys. Lett. 2006, 32, 132–135.
  85. Ovchinnikov, S.G.; Gizhevskii, B.A.; Sukhorukov, Y.P.; Ermakov, A.E.; Uimin, M.A.; Kozlov, E.A.; Bagazeev, A.V. Specific features of the electronic structure and optical spectra of nanoparticles with strong electron correlations. Phys. Solid State 2007, 49, 1116–1120.
  86. Shabatina, T.I.; Vernaya, O.I.; Shabatin, V.P.; Melnikov, M.Y. Magnetic nanoparticles for biomedical purposes: Modern trends and prospects. Magnetochemistry 2020, 6, 30.
  87. Rempel, A.A. Nanotechnologies. Properties and applications of nanostructured materials. Russ. Chem. Rev. 2007, 76, 435.
  88. Simovski, C.; Tretyakov, S. An Introduction to Metamaterials and Nanophotonics; Cambridge University Press: Cambridge, UK, 2020.
  89. Kumar, C.S. Magnetic Nanomaterials; John Wiley & Sons: Hoboken, NJ, USA, 2009.
  90. Kharat, P.B.; Somvanshi, S.B.; Jadhav, K.M. Multifunctional magnetic nano-platforms for advanced biomedical applications: A brief review. J. Phys. Conf. Ser. 2020, 1644, 012036.
More
© Text is available under the terms and conditions of the Creative Commons Attribution (CC BY) license; additional terms may apply. By using this site, you agree to the Terms and Conditions and Privacy Policy.
Upload a video for this entry
Information
Subjects: Physics, Condensed Matter
Contributors MDPI registered users' name will be linked to their SciProfiles pages. To register with us, please refer to https://encyclopedia.pub/register :
Andrei Telegin
,
Yurii Sukhorukov
View Times: 554
Revisions: 2 times (View History)