Submitted Successfully!
Thank you for your contribution! You can also upload a video entry or images related to this topic.
Ver. Summary Created by Modification Content Size Created at Operation
1 Content edited + 2160 word(s) 2160 2020-11-26 07:39:09 |
2 Format correct -75 word(s) 2085 2020-12-07 07:18:59 |

Video Upload Options

Do you have a full video?


Are you sure to Delete?
If you have any further questions, please contact Encyclopedia Editorial Office.
Mandal, S.; Mallapur, S.; Reddy, M.; Singh, J.K.; Lee, D.; Park, T. Graphene-Metal Oxide Semiconductor Nanocomposite. Encyclopedia. Available online: (accessed on 30 November 2023).
Mandal S, Mallapur S, Reddy M, Singh JK, Lee D, Park T. Graphene-Metal Oxide Semiconductor Nanocomposite. Encyclopedia. Available at: Accessed November 30, 2023.
Mandal, Soumen, Srinivas Mallapur, Madhusudana Reddy, Jitendra Kumar Singh, Dong-Eun Lee, Taejoon Park. "Graphene-Metal Oxide Semiconductor Nanocomposite" Encyclopedia, (accessed November 30, 2023).
Mandal, S., Mallapur, S., Reddy, M., Singh, J.K., Lee, D., & Park, T.(2020, December 07). Graphene-Metal Oxide Semiconductor Nanocomposite. In Encyclopedia.
Mandal, Soumen, et al. "Graphene-Metal Oxide Semiconductor Nanocomposite." Encyclopedia. Web. 07 December, 2020.
Graphene-Metal Oxide Semiconductor Nanocomposite

Graphene is one of the most favorite materials for materials science research owing to its distinctive chemical and physical properties, such as superior conductivity, extremely larger specific surface area, and good mechanical/chemical stability with the flexible monolayer structure. Graphene is considered as a supreme matrix and electron arbitrator of semiconductor nanoparticles for environmental pollution remediation.

Graphene-Metal Oxide Semiconductor Nanocomposite Aqueous Medium environmental remediation

1. Introduction

Graphene is a 2-D material composed of layers of carbon atoms crammed into a honeycomb network and has become an escalating star on the prospect of materials science in the past many years [1][2][3]. Graphene can be used to produce 0-D fullerene, 1-D and 3-D graphitic carbon nanotubes that had been intensively studied for the last ten years [4][5]. Graphene exhibits enthralling assets such as extraordinary conductivity, maximum surface-area-to-volume ratio, a fluorescence-quenching competence by electron or energy-allocation, a quantum Hall effect at room temperature, a bipolar electric field effect laterally with the surface conduction of charge carriers and a tunable band gap [6][7]. Narrow band gap metal oxides are of great interest, due to their efficient utilization of solar energy which signifies an auspicious technology to resolve the global energy and eco-friendly challenges [5][8][9][10]. Furthermore, graphene sheets decorated with metal oxide nanoparticles exhibit the outstanding properties because of the synergetic effect between them [11].

The growth of graphene-based composites provides a significant milestone to multiply the application enactment of metal oxide nanomaterials in photocatalysis, as the hybrids have adaptable and suitable properties with superior performances over the individual oxide nanomaterials. With keeping this in mind, considerable efforts have been made on decorating graphene with metal oxides [12]. Graphene-based materials have also been used as the catalyst in the reactions pertaining to environmental remediation [13]. Graphene oxide-based (GO-based)/reduced graphene oxide-based (rGO-based) materials are used as photocatalysts for pollutant abatement [14][15][16][17].

2. Photocatalytic Evaluation

Pristine TiO2 and ZnO exhibited good photocatalytic activity in UV light due to their wide band gap. These two metal oxides are stable in aqueous conditions during photocatalysis. Further, coupling of graphene with TiO2 and ZnO increases the photocatalytic activity due to increases in the photogenerated charge carriers. Metal oxides with magnetic properties of metal ferrites (MFe2O4) offer an added advantage as photocatalysts since they can be recovered by applying an external magnetic field after catalysis. Metal ferrites (MFe2O4, M = Co, Ni, Mn, Zn, etc.) materials are proven to be excellent candidates for visible light photocatalytic H2 generation through water splitting. Recycling ability for metal ferrites are far better compared to nano semiconductors like TiO2 and ZnO. MFe2O4 is a class of semiconductor with narrow band gap, which exhibits characteristic visible light response, possess good photochemical stability, and exhibits excellent optical properties.

MFe2O4 absorbs 42–45% of sunlight, whereas TiO2 and ZnO absorbs 4% of sunlight. MFe2O4 are efficient for the degradation of dye degradation and organic pollutant degradation compared to the other metal oxides (SnO2, CeO2, BaTiO3, and SrTiO3), with respect to the catalyst and the light source. In MFe2O4 context, recombination of photogenerated charge carriers is the major limitation in semiconductor photocatalysis as it reduces the overall quantum efficiency. In order to enhance the photocatalytic activity, graphene material is coupled with MFe2O4, where the graphene channels the electrons. Comparison of degradation rate for various photocatalytic reaction systems is incongruous since the nature of catalyst and substrate pollutant molecules are different in each reaction. Ferrite nanoparticles have a strong magnetic property, which can be easily used for magnetic separation after photo-mineralization.

The photocatalytic efficiency depends on the ratio of the photogenerated charge-carrier transfer rate to the rate of electron-hole recombination. For composite structure, M2+ ion easily bonds with oxygen by giving an electron and super oxide radical. This super oxide radical can oxidize the organic substrate molecule. The Fe3+ ion and Fe2+ ions can show photo-Fenton reactions in presence of in-situ-generated H2O2. This H2O2 generates hydroxyl-free radicals, which are involved in the degradation of pollutants. Predicted mechanism for the rGO-CoFe2O4 composite is shown in Equations (1)–(4).

rGO-BiO6 composite shows better photocatalyst compared to other catalysts prepared from hydrothermal method (Table 1). The enhanced photocatalytic activity could be endorsed to the negative shift in the Fermi level of graphene-Bi2WO6 (G-BWO), decrease the conduction band potential, and elevate migration efficiency of photo-induced electrons, which may restrain the charge recombination efficiently. Superior contact between BiVO4 and rGO scaffold subsidizes to photo-response augmentation compared to other electrochemical methods in the rGO-BiO4 composite.

Table 1. Photocatalysts and their typical synthetic methods used for the preparation from GO/rGO-supported composites.

Order Photocatalyst Preparation References
A.Hydrothermal method for the synthesis of GO/rGO-NCs photocatalyst
1 rGO-WO3 Na2WO4·2H2O and 0.05 g NaCl were dissolved in the above dispersion and kept stirring for 1 h. The pH was adjusted to 2 by using HCl solution. [6]
2 rGO-WO3 Preset amounts of Na2WO4·2H2O (100, 200, and 400 mg, respectively) were dissolved in 10 mL above GO suspension. 5 mL 35% HCl was added slowly. Transferred to autoclave heated at 140 °C for 8 h. [18]
3 rGO_Co3O4 GO dispersed into 24 mL of alcohol, sonicating for 60 min in an ultrasonic cleaner. Then, 0.2 M of Co(Ac)2 was added to the mixture followed by 1.2 mL of water, and continued to be stirred for 10 h at a temperature of 80 °C. The resulting solution was then transferred into a 40 mL autoclave for hydrothermal reaction at 150 °C for 3 h. [19]
4 rGO_Co3O4 GO dispersed in the Co (C2H3O2)2·4H2O. 10 mL with 28% ammonia solution were added to solution, and transferred into an autoclave for hydrothermal action at 180 °C for 12 h. [20]
5 rGO/ZnFe2O4-Ag The composite was synthesized by the co-precipitation of Zn (NO3)2·6H2O, Fe (NO3)3.9H2O, and AgNO3 in the presence of the GO powder. [21]
6 GO-NiFe2O4 GO in NiFe2O4 was dispersed in deionized water. Then, NiSO4H2O and FeCl36H2O (0.02 mol) were dissolved in 15 mL water. Transferred into autoclave and kept under high pressure. [22]
7 GO-MnFe2O4 GO and 60 mL of ethanol with sonication for 1 h and Mn(NO3)2 solution and Fe (NO3)3 9H2O were dissolved. The resulting mixture was transferred into a 100 mL Teflon-lined stainless-steel autoclave and heated to 180 °C for 20 h under autogenous pressure. [23]
8 rGO-Bi2WO6 GO by using Hammer method GO was reduced by ethylene glycol. Bi(NO3)3 5H2O was dispersed into 5 mL of 4 M nitric acid solution. Na2WO4 2H2O was dissolved in 5 mL of de-ionized water and then Na2WO4 was added dropwise to the solution. [24]
B.Sol-gel method for the synthesis of GO/rGO-NCs photocatalysts
9 rGO-TiO2 An aqueous solution of Ti(OH)4 was added into an aqueous suspension of GO. [25]
10 rGO-ZnO An aqueous solution of Zn (AcO)2·3H2O was added into an aqueous suspension of GO. [26]
C.Solvothermal technique for the GO/rGO-NCs photocatalysts
11 GO/CoFe2O4/CdS Gr–CoFe2O4 nanohybrids were sonicated in 60 mL of ethylene glycol for 10 min. The cadmium source containing 0.1431 g of Cd(NO3)24H2O and10 mL of ethylene glycol was added to the mixture containing Gr–CoFe2O4 nanohybrids. The mixture of 0.0348 g of thiourea, 0.0514 g of PVP, and 10 mL of ethyleneglycol was transferred into the above mixture. [27]
12 rGO-ZnFe2O4 GO dispersed in ZnOx(OH)y and FeOx solutions were put into a 50 mL autoclave. [28]
D.Colloidal method for the synthesis of GO/rGO-NCs photocatalyst
13 rGO-ZnFe2O4 C2H6O2 solution is containing 2M FeCl36H2O, and 1M ZnCl2 was gradually added. Then, 1MCH3COONa was introduced into the solution and magnetically stirred for 1 h. Then, transferred to autoclave heated at 1800 °C. [29]
E.Thermal treatment for the synthesis of GO/rGO-NCs photocatalyst
14 rGO-WO3 Na2WO4·2H2O was dissolved in 30 mL water. Then, nitric acid was added to the solution drop by drop until the precipitate was formed. Dried at 160 °C for 2 h and annealed at 500 °C for 5 h. [30]
15 rGO-WO3 Na2WO4·2H2O (0.5 g), H2C2O4 (1 g), and Na2SO4 (4 g) were added into subsequent solution and stirred for 3 h. The pH of the solution was maintained at 1.5 by adding 3M HCl and stirring was continued for 3 h. Then, transferred to autoclave maintained at 180 °C for 24 h. [31]
16 FGS/ZnO GO, Zn(NH3)4CO3, and poly(vinyl pyrrolidone) as an intermediate to combine zinc with carbon material [32]
F.Ball-milling method for the synthesis of GO/rGO-NCs photocatalyst  
17 rGO-CoFe2O4 Co (NO3)2·6H2O and of Fe (NO3)3·9H2O were added to GO (2.5 wt%). The pH is maintained 10 [33]
18 rGO-CoFe2O4 [33]
19 rGO-CoFe2O4 [33]
G.Liquid phase deposition method for the synthesis of GO/rGO-NCs photocatalyst
20 rGO-TiO2 TiO2 powder (P25, Degussa) was dispersed in deionized water and subsequently added to the graphene oxide solution [34]
H.Microwave irradiation method for the synthesis of GO/rGO-NCs photocatalyst
21 rGO-CoFe2O4 (Co(NO3)2·6H2O and Fe(NO3)3 9H2O and glucose as oxidizer and fuel. GO, nitrates, and glucose were added in water for 30 min ultrasonic treatment. [35]
22 rGO-CoFe2O4 [35]
23 rGO-CoFe2O4 [35]
24 rGO/CoFe2O4/Ag GO, AgNO3, and CoFe2O4 were dissolved in deionized water and stirred for 2 h. Then, solution was further stirred for 2 h under the UV irradiation of a 22 W low-pressure mercury lamp. The product is washed with distilled water and ethanol in an oven at 60 °C for 12 h. [36]
I.In situ co-precipitation method for the synthesis of GO/rGO-NCs photocatalyst
25 rGO-ZnO GO dispersed in aqueous solution containing Zn(CH3COO)2, DMSO, and H2O [37]
J.Annealing NH3 atmosphere method for the synthesis of GO/rGO-NCs photocatalyst
26 rGO/N-TiO2 GO and 300 mg of P90 TiO2 was added and stirred for 3 h. GO and P90 TiO2 and a few drops of tetrabutyltitanate were added. [38]

Furthermore, the self-redox properties of iron and manganese atoms in MnFe2O4 induced by S2O82− were particularly useful for the generation of SO4. The quenching tests and electron spin resonance (ESR) display that h+, O2−, SO4, and OH are accountable for decomposition of antibiotics. Overall, irrespective of other parameters, the solvothermal method is best and helps in crystal growing and super saturation is achieved by reducing the temperature in the crystal growth zone.

Further, noble metal (Ag, Au, Cu, etc.) exhibits surface plasmon resonance (SPR), which is a characteristic feature. The SPR frequency of the metal particles can be tuned into visible light absorption by shifting the size of the deposited metal particles on the catalyst. Deposited metal is involved in multiple crucial roles, such as serving as a passive electron sink with high capacity to store electrons to suppress photogenerated charge carrier recombination, facilitates rapid dioxygen reduction to generate free radicals and direct excitation of metals, especially under visible light, and vectorial electron transfer to the conduction band (CB) of metal oxide. Thereby, showing improvement in the photocatalysis for the removal of various organic pollutants/dyes.

3. Perspectives and Challenges

Graphene nanosheets act as a substrate to support the metal oxides for photocatalytic activity and graphene-based semiconductor photocatalysts are used for environmental remediation. The morphologies of semiconductors, theoretical electronic-structure calculations, and experimental discovery determinations are necessary on GO to persuade the photocatalytic activity, and composition design is an operative method to enhance the photocatalytic properties. Photocatalytic properties depend on the preparative method, and various parameters like initial concentration, oxidant concentration, pH, particle size, number of GO sheets, and source of light should be explored.

The interface regulates the efficacy of the electron-hole separation. Currently, only few methods succeed in unswervingly depicting the interaction of GR and nanoparticles. Atomic force microscopy (AFM), Surface-enhanced Raman scattering (SERS), and scanning transmission electron microscope (STEM) may be the best techniques for determining the interaction of graphene and nanoparticles. Finally, studies on the preparation of a ternary composite as a photocatalyst for both UV and visible-light-driven pollutant photodegradation have been studied and reported. Especially, for the design of ternary composite, magnetic materials such as Fe, Co, Mn, etc., as a dopant, and possessing unique advantages, show a remarkable photocatalytic activity and photostability.

Further tasks exist in the application of graphene-based composite for the industrial scale. Some innovative applications of the metal oxide-graphene entail specific understanding between the metal oxides and surface of the graphene, which will have a direct impact on the properties of the composite. Designing a structure for the overall photocatalysis process may require further exploiting of GO by chemically modifying methods. A synthetic approach method of GO-based composite structure by using novel materials has not been achieved to date for photocatalysis, but the solutions to the key challenges appear within reach.

In view of this, graphene-based composites possess diverse potential applications, individually having dissimilar desires concerning material properties, and it can be projected that the research on graphene-composite materials will have an optimistic future.


  1. Deng, X.; Lü, L.; Li, H.; Luo, F. The adsorption properties of Pb(II) and Cd(II) on functionalized graphene prepared by electrolysis method. J. Hazard. Mater. 2010, 183, 923–930.
  2. Yang, S.-T.; Chang, Y.; Wang, H.; Liu, G.; Chen, S.; Wang, Y.; Liu, Y.; Cao, A. Folding/aggregation of graphene oxide and its application in Cu2+ removal. J. Colloid Interface Sci. 2010, 351, 122–127.
  3. Zhang, N.; Qiu, H.; Si, Y.; Wang, W.; Gao, J. Fabrication of highly porous biodegradable monoliths strengthened by graphene oxide and their adsorption of metal ions. Carbon 2011, 49, 827–837.
  4. Yeh, T.-F.; Syu, J.-M.; Cheng, C.; Chang, T.-H.; Teng, H. Graphite Oxide as a Photocatalyst for Hydrogen Production from Water. Adv. Funct. Mater. 2010, 20, 2255–2262.
  5. Zhao, G.; Wen, T.; Chen, C.; Wang, X. Synthesis of graphene-based nanomaterials and their application in energy-related and environmental-related areas. RSC Adv. 2012, 2, 9286–9303.
  6. Li, F.; Tian, X.; Yuhong, Z.; Jun, Y.; Aiwu, W.; Zhong, W. Preparation of WO3–reduced graphene oxide nanocomposites with Enhanced Photocatalytic Property. Ceram. Int. 2015, 41, 5903–5908.
  7. Lorestani, F.; Shahnavaz, Z.; Mn, P.; Alias, Y.; Manan, N.S.A. One-step hydrothermal green synthesis of silver nanoparticle-carbon nanotube reduced-graphene oxide composite and its application as hydrogen peroxide sensor. Sens. Actuators B-Chem. 2015, 208, 389–398.
  8. Yu, B.; Xu, J.; Liu, J.-H.; Yang, S.-T.; Luo, J.; Zhou, Q.; Wan, J.; Liao, R.; Wang, H.; Liu, Y. Adsorption behavior of copper ions on graphene oxide–chitosan aerogel. J. Environ. Chem. Eng. 2013, 1, 1044–1050.
  9. Fu, Y.; Wang, J.; Liu, Q.; Zeng, H. Water-dispersible magnetic nanoparticle–graphene oxide composites for selenium removal. Carbon 2014, 77, 710–721.
  10. Li, B.; Liu, T.; Wang, Y.; Wang, Z. ZnO/graphene-oxide nanocomposite with remarkably enhanced visible-light-driven photocatalytic performance. J. Colloid Interface Sci. 2012, 377, 114–121.
  11. Wu, S.; Wang, P.; Cai, Y.; Liang, D.; Ye, Y.; Tian, Z.; Liu, J.; Liang, C. Reduced graphene oxide anchored magnetic ZnFe2O4 nanoparticles with enhanced visible-light photocatalytic activity. RSC Adv. 2015, 5, 9069–9074.
  12. Tan, L.-L.; Chai, S.-P.; Mohamed, A.R. Synthesis and Applications of Graphene-Based TiO2 Photocatalysts. Chem. Sus. Chem. 2012, 5, 1868–1882.
  13. Li, Y.; Du, Q.; Liu, T.; Peng, X.; Wang, J.; Sun, J.; Wang, Y.; Wu, S.; Wang, Z.; Xia, Y.; et al. Comparative study of methylene blue dye adsorption onto activated carbon, graphene oxide, and carbon nanotubes. Chem. Eng. Res. Des. 2013, 91, 361–368.
  14. Zhang, H.; Lv, X.; Li, Y.; Wang, Y.; Li, J. P25-Graphene Composite as a High Performance Photocatalyst. ACS Nano 2010, 4, 380–386.
  15. An, X.; Yu, J.C. Graphene-based photocatalytic composites. RSC Adv. 2011, 1, 1426–1434.
  16. Du, J.; Lai, X.; Yang, N.; Zhai, J.; Kisailus, D.; Su, F.; Wang, D.; Jiang, L. Hierarchically Ordered Macro−Mesoporous TiO2−Graphene Composite Films: Improved Mass Transfer, Reduced Charge Recombination, and Their Enhanced Photocatalytic Activities. ACS Nano 2011, 5, 590–596.
  17. Wang, D.; Choi, D.; Li, J.; Yang, Z.; Nie, Z.; Kou, R.; Hu, D.; Wang, C.; Saraf, L.V.; Zhang, J.; et al. Self-Assembled TiO2–Graphene Hybrid Nanostructures for Enhanced Li-Ion Insertion. ACS Nano 2009, 3, 907–914.
  18. Wenyu, Z.; Faqian, S.; Ronn, G.; Yan, Z. Facile fabrication of RGO-WO3 composites for effective visible lightphotocatalytic degradation of sulfamethoxazole. Appl. Catal. B 2017, 207, 93–102.
  19. Wang, W.; Levi, G.; Tade, M.O.; Li, Q. April. Evaluation of Photocatalytic Activity of Co3O4/Graphene Composite. In 2015 International Conference on Materials, Environmental and Biological Engineering; Atlantis Press: Paris, France, 2015; pp. 561–564.
  20. Yao, Y.; Yang, Z.; Sun, H.; Wang, S. Hydrothermal synthesis of Co3O4–graphene for heterogeneous activation of peroxymonosulfate for decomposition of phenol. Ind. Eng. Chem. Res. 2012, 51, 14958–14965.
  21. Khadgi, N.; Li, Y.; Upreti, A.R.; Zhang, C.; Zhang, W.; Wang, Y.; Wang, D. Enhanced Photocatalytic Degradation of 17α-Ethinylestradiol Exhibited by Multifunctional ZnFe2O4–Ag/rGO Nanocomposite Under Visible Light. Photochem. Photobiol. 2016, 92, 238–246.
  22. Liu, S.-Q.; Xiao, B.; Feng, L.-R.; Zhou, S.-S.; Chen, Z.-G.; Liu, C.-B.; Chen, F.; Wu, Z.-Y.; Xu, N.; Oh, W.-C.; et al. Graphene oxide enhances the Fenton-like photocatalytic activity of nickel ferrite for degradation of dyes under visible light irradiation. Carbon 2013, 64, 197–206.
  23. Fu, Y.; Xiong, P.; Chen, H.; Sun, X.; Wang, X. High Photocatalytic Activity of Magnetically Separable Manganese Ferrite–Graphene Heteroarchitectures. Ind. Eng. Chem. Res. 2012, 51, 725–731.
  24. Gao, E.; Wang, W.; Shang, M.; Xu, J. Synthesis and enhanced photocatalytic performance of graphene-Bi2WO6 composite. Phys. Chem. Chem. Phys. 2011, 13, 2887–2893.
  25. Pastrana-Martínez, L.M.; Morales-Torres, S.; Likodimos, V.; Figueiredo, J.L.; Faria, J.L.; Falaras, P.; Silva, A.M. Advanced nanostructured photocatalysts based on reduced graphene oxide–TiO2 composites for degradation of diphenhydramine pharmaceutical and methyl orange dye. Appl. Catal. B 2012, 123, 241–256.
  26. Li, B.; Cao, H. ZnO@graphene composite with enhanced performance for the removal of dye from water. J. Mater. Chem. 2011, 21, 3346–3349.
  27. Shi, Y.; Zhou, K.; Wang, B.; Jiang, S.; Qian, X.; Gui, Z.; Yuen, R.K.; Hu, Y. Ternary graphene–CoFe2O4/CdS nanohybrids: Preparation and application as recyclable photocatalysts. J. Mater. Chem. A 2014, 2, 535–544.
  28. Fu, Y.; Wang, X. Magnetically Separable ZnFe2O4–Graphene Catalyst and its High Photocatalytic Performance under Visible Light Irradiation. Ind. Eng. Chem. Res. 2011, 50, 7210–7218.
  29. Jenita Rani, G.; Jothi Rajan, M.A.; Gnana kumar, G. Reduced graphene oxide/ZnFe2O4 nanocomposite as an efficient catalyst for the photocatalytic degradation of methylene blue dye. Res. Chem. Intermed. 2017, 43, 2669–2690.
  30. Hajishafiee, H.; Sangpour, P.; Tabrizi, N.S. Facile Synthesis and Photocatalytic Performance of WO3/rGO Nanocomposite for Degradation of 1-Naphthol. Nano 2015, 10, 1550072.
  31. Hu, X.; Xu, P.; Gong, H.; Yin, G. Synthesis and characterization of WO3/Graphene nanocomposites for enhanced photocatalytic activities by one-step in-situ hydrothermal reaction. Materials 2018, 11, 147.
  32. Yang, Y.; Ren, L.; Zhang, C.; Huang, S.; Liu, T. Facile Fabrication of Functionalized Graphene Sheets (FGS)/ZnO Nanocomposites with Photocatalytic Property. ACS Appl. Mater. Interfaces 2011, 3, 2779–2785.
  33. He, G.; Ding, J.; Zhang, J.; Hao, Q.; Chen, H. One-Step Ball-Milling Preparation of Highly Photocatalytic Active CoFe2O4–Reduced Graphene Oxide Heterojunctions for Organic Dye Removal. Ind. Eng. Chem. Res. 2015, 54, 2862–2867.
  34. Nguyen-Phan, T.D.; Pham, V.H.; Shin, E.W.; Pham, H.D.; Kim, S.; Chung, J.S.; Kim, E.J.; Hur, S.H. The role of graphene oxide content on the adsorption-enhanced photocatalysis of titanium dioxide/graphene oxide composites. Chem. Eng. J. 2011, 170, 226–232.
  35. Zhang, D.; Pu, X.; Gao, Y.; Su, C.; Li, H.; Li, H.; Hang, W. One-step combustion synthesis of CoFe2O4–graphene hybrid materials for photodegradation of methylene blue. Mater. Lett. 2013, 113, 179–181.
  36. Chen, X.; Zhao, Q.; Li, X.; Wang, D. Enhanced photocatalytic activity of degrading short chain chlorinated paraffins over reduced graphene oxide/CoFe2O4/Ag nanocomposite. J. Colloid Interface Sci. 2016, 479, 89–97.
  37. Luo, Q.-P.; Yu, X.-Y.; Lei, B.-X.; Chen, H.-Y.; Kuang, D.-B.; Su, C.-Y. Reduced Graphene Oxide-Hierarchical ZnO Hollow Sphere Composites with Enhanced Photocurrent and Photocatalytic Activity. J. Phys. Chem. C 2012, 116, 8111–8117.
  38. Yin, X.; Zhang, H.; Xu, P.; Han, J.; Li, J.; He, M. Simultaneous N-doping of reduced graphene oxide and TiO2 in the composite for visible light photodegradation of methylene blue with enhanced performance. RSC Adv. 2013, 3, 18474–18481.
Contributors MDPI registered users' name will be linked to their SciProfiles pages. To register with us, please refer to : , , , , ,
View Times: 705
Revisions: 2 times (View History)
Update Date: 07 Dec 2020