Techniques such as adsorption, absorption, cryogenic distillation, and membrane processes are utilized most frequently in order to bring the amount of H2S to an acceptable level. Each approach comes with its own set of benefits and drawbacks; the one chosen will depend primarily on the concentration of H2S present in the mixture as well as the price of the adsorbent or absorbent used in the process. Because of its low cost, high level of safety, and numerous other advantages, adsorption is by far the most popular approach. It makes use of a wide variety of adsorbents, including as metal-organic frameworks (MOFs), activated carbon, and zeolites, and new combinations of these adsorbents are continually being produced and examined.
Tunable diode lasers (TDL) are frequently utilized in the process of measuring the concentrations of the constituents of the gas. The absorption properties of different gases are utilized by the technology so that the concentration of a target gas can be accurately measured. After traveling through the gas sample, the laser light’s intensity is measured by a detector so that the target gas concentration can be derived from this information. Measurements that are exact and exceptionally dependable can be produced by a correctly built TDL analyzer even when the concentration of H2S present is very low.
Hydrogen sulfide is a colorless and flammable gas that has a strong and distinctive odor of rotten eggs. It is also known as hydrosulfuric acid, sewer gas, stink damp, dihydrogen monosulfide, dihydrogen sulfide, sulfane, sulfurated hydrogen, and sulfur hydride. It has a greater density than air and may settle on the ground. The characteristics of H2S that are most important to know are outlined in Table 1.
The zeolites known as Faujasite (FAU) and Linde Type A (LTA) are utilized rather frequently in the separation processes. They are composed of sodalite (SOD) structures that are organized in a pattern that varies depending on the amount of aluminum to silicon (Figure 2).
Sometimes, chemical bonds such as covalent or ionic are formed between the surface of the zeolite and H2S. This process is known as chemisorption, and its interaction is much stronger than physisorption. Chemisorption can, in fact, meet the demand for the selective capture of H2S; however, one drawback is that it results in the development of irreversible bonds, which reduces the potential for regeneration. Therefore, for H2S separation in industrial processes, physisorption is preferred, as the reversible process take place by weak van der Waals forces and electrostatic interaction.
The number of contaminations that the adsorbent needs to remove is an essential factor in determining how successful the operation will be. A decrease in the length of the adsorption cycle results from an increase in the adsorption capacity, which improves the separation of the targeted molecule from the mixture. The adsorption capacity can be determined by calculating the ratio of the amount of the adsorbed molecule to the mass of the adsorbent, and is often expressed in the unit of mmol/g or mg/g.
-
Qtot = total gas flow rate (Nl/h).
-
MW = molecular weight of H2S.
-
Cin = inlet H2S concentration (ppmv).
-
t1= breakthrough time when the outlet concentration is 1 ppmv (h).
-
t0= breakthrough time at the last detection of 0 ppmv (h).
-
Vm = molar volume (24,414 Nl/mol). m = mass of adsorbent material (g).
2. Natural Zeolites
Although natural zeolites have adsorption properties that are several times higher than those of synthetic zeolites, very few natural zeolites have been studied in the context of the removal of hydrogen sulfide from a variety of gases.
A 94% hydrogen sulfide adsorption performance was reached by Pourzolfaghar et al.
[39] from biogas using virgin zeolite without activation. This particular zeolite had a high Si/Al ratio of 5:99, which resulted in a higher adsorption capacity but was lower than the adsorption capacity of the modified zeolite. A number of experiments showed that virgin zeolite had natural regeneration.
The influence of CO
2 and moisture content on the removal of H
2S and SO
2 from biogas using naturally pure zeolite covered with TiO
2 utilizing ultrasonic-calcination investigated by Liu et al.
[14]. Sintering for 2 h at 400 °C was found to be the best condition for obtaining maximum removal capacity and improved mechanical properties. To regenerate utilized TiO
2/zeolite, it was washed at 60 °C for 5 h, dried at 110 °C for 12 h, and then calcined at 400 °C for 2 h. As the amount of TiO
2 on zeolite increases, the formation of SO
2 rises. That is why 5% of TiO
2 onto zeolite demonstrated the best adsorption properties, with an adsorption capacity of 0.13 mmol/g (4.42 mg H
2S/g). As the competitive adsorption takes place in the presence of CO
2, H
2S adsorption capacity has decreased. It was found that moisture content decreased the adsorption capacity of the zeolite whereas adsorption capacity of TiO
2/zeolite increased due to TiO
2 photocatalysis.
Ahmad et al.
[40] examined natural diatomite, which is a low-cost silica material, and tested its water and acid-treated modification in biogas purification. In order to prepare the treated diatomite, washing was done at a variety of temperatures, and sulfuric acid was applied in a variety of concentrations. Samples of diatomite that had been treated with water and those that had been treated with sulfuric acid were both dried in an oven at 105 °C for 24 hr. According to the findings, acid treatment made it easier to modify the surface area and functional group of the diatomite, which led to an increase in the adsorption capacity to 6.87 mg H
2S/g. On the other hand, water hydration reduced the contaminants and improved the diatomite pore volume, which led to an increase in the adsorption capacity to 3.82 mg H
2S/g. During the process of water purification, an increase in temperature results in a greater capacity for adsorption. It was discovered that a concentration of 5M H
2SO
4 produced the best results when purifying diatomite in order to acquire a high adsorption capacity.
Prasetyo and Soegijono Prasetyo and Soegijono
[37] modified Bayah natural zeolites, which are high silica zeolites, in the ferric chloride hexahydrate solution using high-intensity ultrasonic waves. They then examined the H
2S adsorption performance of the modified Bayah natural zeolites. Minerals found in Bayah are primarily composed of clinoptilolite, with traces of mordenite that contain a variety of elements, including carbon, sodium, magnesium, potassium, calcium, and iron. Sonification was applied to a number of different time lapses. Based on the findings, it is possible to draw the conclusion that the time of sonification has no bearing on the distribution of particle sizes. The chemical modification of Bayah natural zeolite increased its adsorption ability by 70% to 117%.
In many situations, the zeolitic imidazolate framework ZIF-8 was used in CO
2 capture. Jameh et al.
[41] investigated ZIF-8 synthesis and modification using methanol and toluene for CO
2 and H
2S removal from natural gas. The specific surface area and microporous pore volume of ZIF-8 increased as a result of methanol modification, demonstrating a high adsorption capability.
According to the abovementioned research, natural zeolites are also good at separating H2S. Various procedures, including as high-temperature calcination, the addition of various metals, and acid processing, can be employed to improve their efficacy in H2S removal. Table 4 highlights methods for removing H2S using natural zeolites.
Table 4. Studies based on natural zeolites.
3. Synthetic Zeolites and Their Modifications
Because natural zeolites are insufficient for commercial use as catalysts and adsorbents, synthesized zeolites are utilized instead. It is necessary to improve the characteristics of zeolites. To that end, metals can be added, calcination temperatures can be changed, and the composition of zeolites can be altered in other ways. Metal ions are introduced into the zeolite structure by two methods: ion exchange and impregnation.
In order to remove hydrogen sulfide from the air at 100, 200, and 300 °C, Jafari et al.
[43] examined Y and ZSM-5 (MFI), which are considered intermediate and high silica zeolites modified with 3% and 5% of magnetite nanoparticles. Drying and calcination were carried out at 105 °C for 10 h and 450 °C for 4 h, respectively, to purify and activate. After adding magnetite nanoparticles and calcining them, the modified zeolites’ surface area, volume, and diameter decreased. On the other hand, the crystal structure was unaffected by either magnetite or calcination. Due to the presence of magnetite nanoparticles, zeolite Y’s meso/micro-porosity increased when compared to ZSM-5. A weight ratio of 5% was determined to be the ideal loading percentage since a high loading percentage lengthens the breakthrough time. At an H
2S concentration of 120 ppm, a 5% -Y/Fe
3O
4 adsorbent was used to produce the greatest adsorption capacity, which was equal to 69.92 mg H
2S/g. This phenomenon can be explained through the chemisorption of H
2S by iron oxide.
Interesting research was carried out by Yokogawa et al.
[37] to assess LTA (Zeolite A) and MFI (ZSM-5) zeolites and their Ag-doped samples to remove volatile sulfur compounds produced in a mouth. LTA and MFI zeolites were synthesized by the wet method and ion exchange of Ag was carried out and dried at 90 °C for 24 h. On both 0.02 g of Ag-doped LTA and MFI, the H
2S concentration was lowered to 24% in 2 h, to almost zero in 4 h, and to be almost zero H
2S concentration for 4 h and 8 h, respectively. In zeolites, experiments showed that adding alkali atoms enhances their capacity to recover hydrogen sulfide, and the Ag-doped LTA zeolite had a better capacity than the Ag-doped MFI. As peaks corresponding to Ag
2S were not identified in the XRD patterns, the authors described this phenomenon as the capture of H
2S by the zeolite pores. The addition of Ag to zeolites helps to increase the affinity toward H
2S.
At a range of temperatures (25–85 °C), Starke et al.
[34] studied the effect of increasing Ca
2+ on the zeolite type of LTA, which is binder free and has a Si/Al ratio of 1. A breakthrough curve was evaluated in a fixed-bed adsorption unit and calcination was carried out before each experiment at 300 °C for 4h under a nitrogen atmosphere. The H
2S concentration was in the range of 50–2000 ppm. It was concluded that increasing the Ca
2+ cations in the zeolite causes physisorption to dominate. Increasing the Ca
2+ in the degree of exchange rises the adsorption capacity due to higher ionic charge of Ca
2+; this because it causes strong interactions to form between the Ca and H
2S molecules. Temperature has a negative effect on the adsorption capacity.
Nguyen and his team
[44] synthesized Faujasite zeolite hydrothermally and ion-exchanged with divalent metal ions (Co
2+, Mn
2+, Ni
2+, Cu
2+, Ca
2+, and Zn
2+). H
2S adsorption was carried out in continuous fixed bed. Ion-exchange modification of NaX with Co, Cu, and Zn considerably enhanced the adsorption capacity. It can be explained by the reaction between the CoO, CuO, and H
2S molecules. When compared to raw X zeolite, the CoX, CuX, and ZnX zeolites showed more than 7, 13, and 24 times the H
2S adsorption capability, respectively, which means the ZnX sample had a higher adsorption capacity of 23.5 mg H
2S /g.
Many researchers are attempting to remove H
2S with the help of the Ag ion. Kumar et al.
[10] examined Ag and Cu modified X and Y zeolites to separate H
2S from gas streams containing He, N
2, CO
2, CO, and H
2O at room temperature and 150 °C. X and Y zeolites had an Al/Si ratio of 1.3 and 2.4. CuX and CuY samples showed high adsorption capacity due to forming new active sites at 150 °C whereas the adsorption capacity of the NaX, AgY, and AgX samples declined. Despite the presence of the various gases in the mixture, AgX and AgY zeolites were able to remove H
2S. However, CuX and CuY were unsuccessful to remove H
2S in the presence of 2% CO. It is possible that the impregnation of copper to zeolite increased CO’s affinity to the adsorbent while Ag attracted H
2S.
Chen et al.
[45] tested an ion-exchanged NaX zeolite with Zn, Co, and Ag to identify the adsorption performance of H
2S and COS from Claus tail gas. CoX, ZnX, and AgX ion-exchanged zeolites were synthesized using their nitrate solution and dried at 100 °C. Characterization of the samples was done by SEM (see
Figure 3), XRD, and FTIR techniques to prove the ion exchanging of the metals. A dynamic adsorption experiment was carried out in a fixed bad adsorption column at 25 °C. Although the BET surface area of the ion-exchanged AgX zeolite decreased to 30% compared to NaX, AgX had the largest H
2S and COS breakthrough capacity, with 1.53 mmol/g (52.02 mg H
2S/g) and 10.5 µmol/g (0.63 mg COS/g), respectively. This can be explained by the chemical adsorption between the AgX zeolite and H
2S.
Figure 3. SEM images of NaX (
a), CoX (
b), ZnX (
c), and AgX (
d), reprinted from
[45], with permission of Elsevier.
Nevertheless, regeneration of the AgX zeolite under various conditions was investigated. Regeneration in the presence of air at 350 °C was better, and the AgX sample exhibited a remarkable thermal stability, retaining its original structure even after six adsorption–regeneration cycles.
The performance of the Cu-modified 13X was investigated by Barelli and colleagues
[13] in the separation of H
2S from biogas. Experiments were carried out under a broad spectrum of operational conditions (temperatures ranging from 30 °C to 120 °C, and H
2S concentrations ranging from 200 to 1000 ppm) in order to determine the optimal operating parameters. Temperature has a beneficial effect on performance, as demonstrated by the fact that a higher adsorption capacity of 13X Ex-Cu zeolite was obtained (40 mg H
2S/g) when the temperature was set to 120 °C. When the matrix composition was changed, the adsorption capacity decreased because competitive adsorption took place. The 13X Ex-Cu zeolite had an adsorption capacity of 14mg H
2S/g and 23 mg H
2S/g with the pure CO
2 and CH
4, respectively, due to the increase in Cu
2+ that causes π-complexation between the Cu
2+ ions and sulfur compounds.
Simultaneous removal of H
2S and SO
2 from the Claus tail gas using the 13X zeolite was carried out by Yang et al.
[46]. The adsorption was performed in a simulated Claus gas containing 20,000 ppmv H
2S, 10,000 ppmv SO
2, 15 vol% water vapor, and the balance N
2 gas at 150 °C. According to the breakthrough curve, the fresh 13X zeolite showed an adsorption sulfur capacity of 179.7 mg S/g for H
2S and SO
2. Regeneration was done by purging of N
2 at 490 °C for 120 min with the space velocity of 1000 h
−1. The adsorption sulfur capacity decreased to 148.1 mg S/g after five adsorption–regeneration cycles due to formation of sulfate in the pores of 13X, which causes the blockage of pores.
Modifying the 13X zeolite with Ag and Cu by impregnation, to remove the organic sulfur compounds from natural gas, was investigated by Zhu et al.
[47]. Modification of 13X with Ag increased the adsorption capacity by 1.6 times (64.8 mg S/g) compared to the raw 13X. Calcination at high temperatures improved the performance of the modified zeolite, with 450 °C being the best one. Cu/13X also showed a high adsorption capacity in the following sequence: ethyl mercaptan > methyl sulfide > dimethyl disulfide. The results show that modification of the 13X zeolite with metals such as Ag and Cu increases their adsorption affinity to organic sulfur compounds. The authors assumed that Cu/13X- and Ag/13X-modified zeolites show higher efficiency in H
2S separation. Adding metal ions to zeolite increases the adsorption capacity due to a Metal-S bond.
Bareschino et al.
[48] recently conducted studies to determine the saturation of NaX zeolite with H
2S. The effects of H
2S concentration, temperature, and adsorbent age were investigated, and it was discovered that the adsorbent does not fully saturate since H
2S oxidation occurs:
Recent research conducted by Kulawong et al.
[9] examined the effectiveness of the Ag-exchanged NaX zeolite in removing H
2S from an anaerobic digestion reactor. The preparation of this zeolite required varying concentrations of AgNO
3 (11.5%, 34.1%, 71.6%, 76.7%, and 78.8%) in order to get varying degrees of silver loading on the zeolite by heating it at 40 °C for 2–12 h. As the amount of silver loaded into the system rose, the H
2S concentration dropped, demonstrating that silver makes H
2S more attractive. As a result, an increase in the quantity of Ag loaded was accompanied by an increase in the effectiveness of H
2S removal. Since the maximum content was not statistically significant, the NaX zeolite with a lower Ag concentration of 34.1 wt% labeled as AgX2 would be more cost-effective with an adsorption performance of 97.35%. This is because the maximum content did not meet the criteria for statistical significance.
Manullang et al.
[49] investigated the influence of the Zn/Zeolite ratio and calcination temperature on the separation of hydrogen sulfide from biogas. The impregnation method was used to prepare the samples at concentrations of 10, 20, and 30 wt/v% ZnO. Prepared samples were activated for 3 h by calcination at 200, 300, and 400 °C. The crystal structure of zeolites can be damaged and the surface of a zeolite covered by metal due to the sintering of metal salts at high temperatures, resulting in a loss in adsorption performance. The optimal parameters for separating H
2S from biogas were found: a Zn/Zeolite ratio of 20% and a calcination temperature of 300 °C. Adsorption capacity reached up to 6.36 mg H
2S/g adsorbent under these conditions, and the purification rate was 99%.
In order to evaluate the effect of silver on NaA zeolite for the removal of hydrogen sulfide, Bahraminia et al.
[50] studied synthesized NaA nano zeolite and its Ag-exchanged sample. NaA zeolite was synthesized hydrothermally and AgNaA was prepared by ion-exchange and both dried at 60 °C for 12 h. The structure of the samples was confirmed by XRD and SEM techniques. The adsorption capacity of the NaA zeolite with Ag
+ ions was found to have increased (33.24 mg H
2S/g). In addition, the regeneration of AgNaA was carried out five times at a temperature of 350 °C. As a result of the development of sulfur on the surface of the zeolite, the adsorption capacity showed a modest decrease of 5%.
The equilibrium and dynamic behaviors of natural gas separation, using Na-SSZ-13 zeolite, were studied by Thomson
[51]. The adsorption process was carried out in a dynamic column breakthrough (DCB) apparatus. A feed gas mixture of CH
4, C
2H
6, CO
2, and H
2S at different concentrations was used. Binary, ternary, and quaternary DCB experiments were carried out to assess the adsorption performance of Na-SSZ-13. COS formation has occurred because of the presence of CO
2 and H
2S in the feed gas. Ideal Adsorption Solution Theory (IAST) is applied to obtain the mixture adsorption data. When the IAST was used to simulate the gas adsorption mixtures on the Na-SSZ-13 zeolite, the adsorption behavior and experimental breakthrough curves matched well.
The effects of temperature, H
2S inlet concentration, gas matrix, and adsorption/desorption cycles of the adsorption of H
2S on the industrial molecular sieves (IMS) were studied by Georgiadis et al.
[52] theoretically and practically. The LTA-type zeolite structure framework was proved by characterization of IMS, which had a BET surface area of 590 m
2 g
−1. Adsorption was done at 35, 50, and 100 °C, and reduction in the adsorption capacity occurred as physical adsorption took place, which is exothermic. IMS had the highest adsorption capacity of 122.8 mg H
2S/g at 35 °C. Studies at different concentrations of H
2S have shown that the higher the concentration, the higher the adsorption capacity. The adsorption capacity was reduced due to the presence of CO
2 in the gas composition and its competitive adsorption with H
2S. Although adsorption/desorption cycles were carried out 15 times, no significant changes were observed on the H
2S uptake.
At room temperature, Rezaei et al.
[53] compared the ETS-2 adsorbent exchanged with Ag, Ca, Cu, and Zn metals to a commercially available adsorbent, R3-11G. In comparison to R3-11G, the metal-exchanged ETS-2 zeolite showed better effective adsorption properties. The Cu-exchanged ETS-2 zeolite had the highest H
2S capacity as an absorbent, 29.7 mg H
2S/g.
For the sake of safety, H
2S was removed from the simulated gases containing nitrogen and other inert gases in many studies. Heck et al.
[54] conducted pressure swing adsorption of concentrated H
2S (0.1–0.7%) and CO
2 from a feed gas containing CH
4, CO
2, and H
2S, which is similar to natural gas using commercially available zeolites, namely, 4A, 5A, and 13X. The effect of the concentration of H
2S and pressure were studied by a number of experiments. 13X and 5A zeolites may remove H
2S to a nearly zero concentration. A 100% recovery of H
2S was achieved by desorption in 13X and 4A. It was concluded that the PSA method can be used industrially for the removal of H
2S from natural gas.
Bowen et al.
[55] investigated hydrogen sulfide removal from natural gas using titanosilicite zeolite (TS-1) in the presence of hydrogen peroxide and examined the effect of reaction temperature and H
2O
2 concentration on the catalytic oxidation. The result showed that increasing the reaction temperature and H
2O
2 concentration increase the catalytic oxidation of TS-1 towards H
2S. In
Table 5, studies based on modification of synthetic zeolites are summarized.
Table 5. Studies based on modification of synthetic zeolites.
4. Zeolite-Based Adsorbents Synthesized from Various Sources
In recent years, zeolite-based adsorbents used in the separation of H2S from gas mixtures have been synthesized from various cheap raw materials because they are widely available and have a low production cost.
Jalil R. Ugal et al.
[56] studied the adsorption capacity values of 3A, 4A, and 5A zeolites prepared from Iraqi kaolin by the ion-exchange method. Characterization results of the prepared samples proved that 3A, 4A, and 5A molecular sieves were successfully synthesized and they had a similar structure as the standard type. 4A has a high affinity for H
2S according to the values of the Langmuir isotherm, which best describes the gas–solid face adsorption. 5A zeolite showed an adsorption capacity of 79.384 µmol/g (2.7 mg H
2S/g). The H
2S adsorption capacity increased with a decrease in temperature from 55 °C to −5 °C. This is explained by the authors in that a rise in temperature weakens the adsorption interactions between the adsorbent and the adsorbate. This indicates that the synthesized molecular sieves on the basis of kaolin are suitable to use in the H
2S separation.
Liu et al.
[57] carried out hydrogen sulfide removal using 4A zeolite synthesized from naturally abandoned zeolite, namely, attapulgite (ATP). 4A zeolite was synthesized under various ratios. The effects of the ratio of silicon to aluminum, ratio of sodium to silicon, ratio of water to sodium, crystallization temperature, and time were investigated in the removal of H
2S. From the breakthrough curves of experiments under various conditions and ratios (see
Figure 4), it can be seen that there is competitive adsorption between H
2S and N
2 at the beginning. The ratio of silicon to aluminum has a substantial influence on the performance of H
2S removal, as demonstrated in the figures; however, the ratio of sodium to silicon has a weak impact on the performance of H
2S removal. When considering both factors, a ratio of 1.5 might be the best possible figure. A low ratio of water to sodium was ideal since ATP naturally contains elements such as magnesium, calcium, and iron. These elements can form their oxides, which have a favorable impact on the removal of H
2S. From these findings, it can be concluded that the zeolite 4A synthesized under the following conditions: n (SiO
2)/n (Al
2O
3)) = 1.5, n (Na
2O)/n (SiO
2) = 1.5, crystallization at 90 °C for 4 h, n (H
2O)/n (Na
2O) = 30) showed a high adsorption capacity of 8.36 mg H
2S/g sorbent and a saturation sulfur sorption capacity (that is complete adsorption capacity that can no longer adsorb H
2S) of 12.4 mg H
2S/g at 50 °C. Because of its distinguished properties, 4A zeolite synthesized from attapulgite is proposed as a promising material for H
2S adsorption. Furthermore, the 4A was regenerated at 350 °C for 2 h using nitrogen purging at a flow rate of 200 mL/min. Characterization analyses showed no significant changes in BET surface area, crystal structure, and surface group after regeneration.
Figure 4. H
2S adsorption breakthrough curves at 25 °C under different synthesis conditions: (
a) at various (SiO
2)/n (Al
2O
3) ratios (
b) at various (Na
2O)/n (SiO
2) ratios, (
c) at various temperatures, (
d) at various crystallization time, (
e) at various (H
2O)/n (Na
2O) ratios, reprinted from
[57], with permission of Elsevier.
Oliveira et al.
[58] examined H
2S adsorption on NaY zeolite in equilibrium and fixed bed conditions. NaY zeolite was prepared using kaolin clay and examined its adsorption properties for the H
2S removal from natural gas in continuous PSA. The Si/Al ratio of NaY was 2.8. Adsorption isotherms obtained at temperatures of 20, 30, and 40 degrees Celsius, up to a partial pressure of 1.2 bars of hydrogen sulfide, are advantageous and offer maximum adsorption capacities that are greater than 6.0 mol kg
−1 (204 mgH
2S/g).
Abdullah et al.
[59] studied the influence of ZnO on Na-A zeolite synthesized by impregnation from Malaysian kaolin in biogas desulfurization. ZnO was employed to increase the adsorption capacity of zeolite and because its low cost compared to other oxides. When the loading rate was increased from 10 to 20 wt%, both the micropore area and the micropore volume decreased. However, there was no substantial change found even after increasing the loading rate from 20 to 30 wt%, which indicates that the loading rate was exceeded. It was noticed that the highest adsorption capacity of 15.75 mg S/g sorbent H
2S when 20 wt% ZnO was loaded onto Na-A. The fact that the characteristics of the used adsorbent were not recovered as a result of regeneration at temperatures of 100 and 200 °C is evidence that chemical adsorption took place by the following equation:
Table 6. Studies on synthetic zeolitic adsorbents from various sources.
5. Newly Developed Adsorbents from Wastes
One of the most important things that contributes to successful and feasible development is the utilization of inexpensive raw materials on an industrial scale. As a result, a number of research initiatives have been abandoned on the development of novel compounds derived from less expensive and obsolete basic materials. The production of zeolites requires the utilization of a number of different minerals, including kaolinite, fly ash, sludge, asbestos, and rice husk. The investigation of wastes as an adsorbent in the separation of H2S would open up a new sector.
Cebula et al.
[61]] synthesized a universal adsorbent, namely, Halloyfill, from a halloysite mineral—which is an aluminosilicate clay mineral belonging to the kaolin group—and applied it to the removal of various pollutants such as siloxanes, H
2S, and NH
3 generated from biotechnological processes. The results showed that it can remove NH
3 (95–99%), H
2S (above 99%-21.3 mg H
2S/g), and volatile organic compounds (70–81%). The authors also proposed that the spent adsorbent can be used as a fertilizer in agriculture and gardening.
CaCO
3 was the primary component of two kinds of the waste solids that Awe and colleagues
[62] investigated as potential H
2S adsorbents. Fresh calcite and commercially activated carbon (AC) were utilized as comparative materials in order to validate the adsorption performance of the synthesized adsorbent. In addition, AC-CaCO
3 waste mixtures with a variety of different ratios were researched. In 540 min, 15 mg H
2S was adsorbed when the weight ratio of AC to CaCO
3 was 3:1, whereas AC only absorbed 14 mg H
2S over that same time period. It is possible to explain the presence of a variety of metals in the solid waste, including Ca, Mg, and Fe. The findings demonstrated that using wastes containing CaCO
3 as an adsorbent for H
2S removal was more effective than using activated carbon or calcite, which are both available for purchase in the marketplace.
Three waste-derived adsorbent materials (wood-derived biochar (WDB), sludge-derived activated carbon (SDC), and activated ash) were studied by Zhu et al.
[63] for the separation of H
2S from simulated biogas (CH
4-to-CO
2 ratio at 1.5 and H
2S concentration at 200 ppm). WDB and activated ash were activated at 700 °C, while SDC was activated at 600 °C. Characterizations of the pre-treated adsorbent were analyzed by TGA, XRF, SEM, and BET. The outlet concentration of H
2S was measured using a mass spectrometer to determine the adsorption capacity. Activated ash showed the highest adsorption capacity, at 3.22 mg H
2S/g, among the materials; this was because chemisorption occurred as a result of the presence of alkaline mineral species such Fe, Cu, and Mn, which have a tendency to react with H
2S. Wood-derived biochar has an adsorption capability of 2.2 mg H
2S/g due to its high surface area of 210.18 m
2/g. To demonstrate the existence of physical adsorption, the surface area of WDB decreased from 210.18 m
2 g
−1 to 96.95 m
2 g
−1. This occurred because high porosity was responsible for capturing the H
2S molecules. Physical adsorption was proved by reducing the surface area of WDB, as the H
2S molecules are captured by the high porosity.
Coal fly ash and blast furnace cement were used in the synthesis of H
2S adsorbent by Asaoka et al.
[64] With a component ratio of 87:13 and a calcination temperature of 700°C, it was possible to achieve adsorption capacities of 650 g-H
2Sm
−3 (62.15 mg H
2S/g, calculated according to the density of average coal fly ash
[65] and blast furnace cement
[66]) under dry conditions and 730 g-H
2Sm
−3 (71,71 mg H
2S/g) under humid conditions. These results were achieved as a result of H
2S oxidation to sulfate, which is chemisorption. The adsorbent is capable of removing up to 99.1 % of H
2S in both dry and humid conditions.
Mbugua et al.
[67] investigated the use of zeolitic rock from the Eburru deposit as well as other materials (maize cobs, steel wire, desulphurizer, and worn-out tyres) for the purpose of upgrading of biogas by removing CO
2 and H
2S. As a result of the polarity of CO
2, zeolite rock demonstrated excellent performance; in contrast, desulfurizer was able to remove H
2S at a rate of 97.78%. The presence of metals such as manganese, magnesium, iron, and zinc in zeolitic rock can be regarded as having certain characteristics.
Although iron has a tendency to chemically react with H
2S, Salimi et al.
[68] studied the modification of adsorbents, namely, bentonite and sludge, with iron and copper to remove H
2S and mercaptans from a refinery outlet gas. Depositions of Fe and Cu metals onto bentonite and sludge were proved by SEM–EDS analysis. The authors also explored the effect of the flow rate on the adsorption performance, concluding that a low flow rate is preferred. Regeneration of the adsorbent was done using gas and steam at 200 °C after three time cycles, with an adsorption capacity reduction observed. Iron-modified bentonite demonstrated a high adsorption capacity for H
2S (32.256 mg H
2S/g) and mercaptan (0.98 mg/g), whereas the copper-modified sludge had an adsorption capacity for H
2S (11.18 mg H
2S/g) and mercaptan (0.81 mg/g).
Gasquet et al.
[69] has recently attempted to examine and improve the H
2S adsorption properties of sewage sludge-derived ash (SSA) and its modification with sand and activated carbon. Modification of SSA with 20% activated carbon showed an increase in the adsorption capacity of up to 186 mg H
2S/g. Since elemental sulfur was observed by characterization techniques, the authors explained this by chemical adsorption due to reactional sites between HS- and oxygen that were created by the microporosity of the activated carbon.
Various materials, such as sand (S) silica blue (SB), iron-exchanged sand (IES), zeolite 13X (Z), iron-exchanged zeolites (IEZ), and the waste material acid mine drainage sludge (AMDS), were investigated as H
2S adsorbents in previous research
[70]. Experiments were done using a gaseous mixture containing 100–1000 ppmv of H
2S in N
2 in a pilot lab setup at 25 °C. Characterization of adsorbents were analyzed before and after adsorption. AMDS showed a high H
2S adsorption capacity of 312.73 g H
2S/g compared to other adsorbents at a flow rate of 0.5 L/min, when the initial concentration of H
2S was 1000 ppmv. However, as the flow rate increased, the H
2S adsorption capacity decreased.
The majority of waste-based adsorbents are composed of metals such as Fe, Cu, and Mg, all of which have a tendency toward chemisorption. Studies on the waste-based adsorbents were summarized in Table 7.
Table 7. Studies on the waste-based adsorbents.
6. Conclusions
In the separation of H2S gas from gas mixtures, the presence of other gases in the mixture, such as CO2, H2O, and CO, complicates the process because of competitive adsorption. Therefore, it is very important to find and synthesize efficient zeolites with a high adsorption capacity, selectivity, and regenerability that can separate H2S under a variety of conditions. Natural and synthetic zeolites, and their modifications, are widely used in the separation of H2S from various gaseous mixtures. It is difficult to find the most effective adsorbent because there are so many different structural types of zeolites, modification possibilities, and conditions to consider when removing H2S. However, by understanding the properties of zeolites and the gas to be removed, the proposed zeolite or its modification can be assumed for the screening in the separation processes. Linde Type A (4A and 5A) and Faujasite (13X) zeolites with a low silica content, and their modifications with Cu and Ag, which have good adsorption properties, are very good candidates in this case.
The adsorption of hydrogen sulfide by zeolites is considered to be physical adsorption in most cases. The modification of zeolites can increase their attraction to H2S, and this can sometimes lead to the development of chemical adsorption. To date, many research attempts have explored the adsorption of H2S by modified zeolites using ion-exchange and impregnation methods, and very promising results are being obtained and their application is being proposed on an industrial scale. In recent studies, a NaX zeolite modified with a Ag+ cation has been suggested as a highly effective adsorbent in H2S removal.
Moreover, adsorbents made from wastes, such as activated ash, bentonite, sewage sludge, and acid mine drainage sludge, have been proposed as effective H
2S adsorbents. The adsorption capacity of AC-modified sewage sludge toward H
2S is high, but their regenerative ability has not been investigated. Although a very high adsorption capacity of 312.73 g H
2S/g of acid mine drainage sludge (AMDS) has been identified by Ahn et al.
[70], this is somewhat far from the expectation. Because an adsorbent with such an adsorption capacity is not known to us, we have requested that the author
[71] verify these statistics.