Bone damage leading to bone loss can arise from a wide range of causes, including those intrinsic to individuals such as infections or diseases with metabolic (diabetes), genetic (osteogenesis imperfecta), and/or age-related (osteoporosis) etiology, or extrinsic ones coming from external insults such as trauma or surgery. Although bone tissue has an intrinsic capacity of self-repair, large bone defects often require anabolic treatments targeting bone formation process and/or bone grafts, aiming to restore bone loss. The current bone surrogates used for clinical purposes are autologous, allogeneic, or xenogeneic bone grafts, which although effective imply a number of limitations: the need to remove bone from another location in the case of autologous transplants and the possibility of an immune rejection when using allogeneic or xenogeneic grafts.

  • MSCs
  • bone regeneration
  • tissue engineering
  • scaffold
  • composite
  • hydrogel
  • cell therapy

Note: The following contents are extract from your paper. The entry will be online only after author check and submit it.

1. Introduction

Bone, a dynamic natural composite, is constantly remodeled by fine-tuned bone formation and bone resorption processes, carried out by osteoblasts and osteoclasts, respectively, throughout an individual’s lifespan [1]. Bone tissue usually presents self-repairing ability after an injury, regaining the damaged part its original structure and mechanical strength. In fact, bone fracture healing relying on mesenchymal stem cells (MSCs) derived osteoblasts performance, can occur through two different mechanisms: intramembranous (involved in the formation of flat bones such as skull bones and clavicles) and endochondral (in long bones such as femur and tibia) bone formation. While the intramembranous ossification directly forms the bone from MSCs that are differentiated into osteoblasts, for endochondral bone formation, there are two key players required; the presence of cartilage, and the vascularization process [2,3][2][3]. Indeed, angiogenesis (the formation of new blood vessels from pre-existing ones) is a key component in bone repair, since blood vessels bring oxygen and nutrients to the regenerating tissue [4]. Moreover, blood vessels supply inflammatory cells, cartilage, and bone precursor cells to reach the injury site, along with the ions necessary for mineralization in a later phase [5].
However, bone loss (such as osteoporosis), bone defects of a critical size (defined as those that will not heal spontaneously within a patient’s lifetime [6,7][6][7]), lack of vascularization, infections and tumors remain key challenges for successful bone healing [8] and require clinical intervention. In fact, osteoporosis, a highly prevalent bone disease associated to aging and characterized by bone fragility, represents a considerable socio-economic problem whose incidence is irremediably increasing as a consequence of aging of the population. In 2010 there were estimated to be 158 million individuals at high fracture risk worldwide, and demographic shifts mean that this figure is likely to double by 2040 [9]. Current clinical approaches to treat bone defects mainly contemplate natural bone grafts, which although effective present several serious limitations [10,11][10][11]. Therefore, alternatives focused on developing synthetic bone tissue surrogates, with scaffolds as central players, are being explored in order to circumvent these disadvantages [12]. An ideal scaffold with bone regeneration purposes should mimic the extracellular matrix (ECM) of natural bone tissue, providing the cells an adequate substrate for adhesion, proliferation, migration, and differentiation [13]. This ECM-cell interaction (including osteoblasts, endothelial cells (EC) and immune cells) will direct the cells fate and control bone repair and regeneration [14]. Taking the ECM interactions into account, the scaffold must fulfill a series of requirements to ensure a proper bone regeneration: first, the scaffold must induce the recruitment and osteogenic differentiation of MSCs in order to form bone (osteoinductivity), and it has to be capable of supporting bone formation (osteoconductivity). Second, the optimal scaffold should ensure the development of vascular networks to warrant a positive suitable microenvironment for tissue engineering [15]. Osteointegration is finally needed, in which the stable anchorage of the scaffold is achieved by direct bone-to-implant contact [16].
Until today, numerous strategies have been developed with the purpose of improving bone tissue regeneration. The current review will summarize recent approaches addressing this aim, either by promoting the mobilization and differentiation of endogenous bone progenitor cells or by treating bone defects with the exogenous addition of different agents (scaffolds, biomolecules, MSCs).

2. Strategies Promoting Bone Healing through an Endogenous Response

Bone, a heterogeneous composite material, involves living cells embedded in a mineralized ECM consisting of inorganic and organic phases in addition to water [17]. While the inorganic phase is composed of a combination of calcium and phosphorus salts, (predominantly in the form of hydroxyapatite (HA; Ca10(PO4)6(OH)2), the organic fraction comprises mainly collagen type I, and other non-collagenous proteins. The amount, proper arrangement, and characteristics of each of these components (quantity and quality) define the properties of bone. However, the relative amount and characteristics of each of these phases present in a given bone varies with age [18], location (bone tissue composition varies across anatomic sites in the proximal femur and the iliac crest), gender [19], and health status [20]. One of the main challenges of bone tissue engineering is to develop scaffolds using materials that emulate the properties of the native bone, composed of unidirectionally aligned collagen fibrils, and densely mineralized with HA crystals.

2.1. Additive-Free Scaffolds: Calcium Phosphate-Based Scaffolds

Osteoblasts begin the mineralization process with the secretion of vesicles filled with amorphous calcium phosphate (ACP), a calcium phosphate (CaP) precipitate of variable composition that acts as a precursor of mineralized bone matrix. ACP granules are deposited into the collagen fibrils, which subsequently, at a pH above 9, are transformed into HA crystals, resulting in the matured, mineralized collagen matrix [21]. However, between 7 and 9 pH range, ACP is transformed into octacalcium phosphate (OCP) phase that, in turn, spontaneously converts to stable HA. Depending on the chemical conditions of the environment (pH and ion concentrations) other CaP phases can be found such as dicalcium phosphate dihydrate (brushite) or tricalcium phosphate (TCP) phases. Therefore, the use of CaP-based scaffolds with different formulations (HA, α- and β-TCPs, OCP, ACP, biphasic CaPs or a mixture of HA and β-TCP at varying ratios) have been considered an ideal artificial bone substitute. Their success relies on their biocompatibility, bioactivity, osteoinductivity and osteoconductivity abilities [22,23][22][23]. The mechanism behind the osteoinductive capacity of CaP-based composites has been addressed by a proteomic analysis, which revealed the implication of plasma cell glycoprotein 1 (PC-1), encoded by the ectonucleotide pyrophosphatase/phosphodiesterase 1 gene (ENPP1), which regulates the mineralization process by hydrolyzing adenosine triphosphate into adenosine monophosphate and pyrophosphate (PPi) [24]. In fact, only the cells in direct contact with CaP ceramics showed an increase in the expression of ENPP1 and PC-1 synthesis when compared to non-osteoinductive ceramics, together with other osteogenic markers (bone morphogenetic protein 2 (BMP-2) and Osteopontin), but without affecting the expression of alkaline phosphatase (ALP) [25]. Extracellular PPi levels are key in regulating the mineralization process; thus, PPi is hydrolyzed by ALP to yield inorganic phosphate, a precursor of bone mineral, but excess PPi inhibits bone mineralization and soft tissue calcification by binding to nascent HA crystals, preventing them from continuing to grow. The increased production of PPi by PC-1 in cells cultured in CaP-based scaffolds negatively regulates tissue mineralization, which draws attention to the modulation of ENPP1 expression as a regulatory response to CaP-induced human MSCs (hMSCs) differentiation to restrict further mineralization [24]. Moreover, the fact that EPNN1/PC-1 over-expression occurs only in cells with direct contact with the ceramic, suggests that a chemically-driven process was occurring at the surface involving the exchange of calcium and phosphate ions between the medium and the material. Thus, in this type of intrinsic osteoinduction, which is also known as material induced heterotropic ossification, calcium and phosphate ions precipitate at the surface of the scaffold, forming an apatite layer generating a local depletion of these ions that triggers cellular differentiation into osteogenic lineage [26].
Several studies have underlined the fragility of CaP scaffolds (which are highly porous), pointing them out as not suitable for weight-bearing bone defects. Therefore, in order to improve CaP mechanical and structural properties, different combinations have been attempted by adding other components with viscoelastic properties (tolerating high levels of strain or deformation and able to fill irregular-shaped bone defects) such as collagen [27], alginate [28], chitosan [29[29][30],30], polylactic acid (PLA) [31], and polyglycolic acid [32], giving rise to injectable hydrogel systems. They are typically biocompatible due to their large water content, and less prone to provoke an immune response [33]. The hydrogel CaP scaffolds seem to be a suitable option for early tissue regeneration since they serve as a temporary matrix, providing mechanical stability and traction for migrating cells from adjacent tissues that gradually degrade the scaffold, replacing it with new bone. Attempts to develop ACP-based scaffolds have also been carried out, due to the fact that ACP particles are easily resorbed, releasing calcium and phosphate ions as they are required for new bone formation. However, since ACP is highly instable and tends to crystallize into brushite and HA minerals, the inhibition of this process has been addressed by generating an ACP hydrogel with PEG, plus the addition of both citrate and zinc, showing the latter the greatest stabilization [34]. This result paves the way for the future development of stable ACP scaffolds, which could be injected at the lesion site and function as a precursor material for new bone synthesis.
Another noteworthy approach to improve scaffold biomechanical properties rely on the addition of metal traces such as strontium, which is naturally found in bone ECM [35,36][35][36] or non-naturals such us barium titanate [37,38][37][38]. Either one in combination with CaP composites seems to produce a good response regarding not only cellular adherence and proliferation, but promoting osteogenic differentiation. Barium titanate, similar to other solid materials (crystals, certain ceramics, or even bone itself), presents piezoelectric properties, meaning it accumulates electric charge in response to applied mechanical stress. Therefore, these types of materials can be deformed with physiological movements and consequently, provide an electrical stimulation to the tissue microenvironment, enhancing the tissue regeneration without any external source [39]. Several piezoelectric ceramics including potassium sodium niobate [40], lithium sodium potassium niobate [41], zinc oxide [42], or polymers such as polyvinylidene fluoride and PLA, are being studied to determine which material offers the best properties in terms of developing efficient electroactive prosthetic implants for bone repair [43,44][43][44].
Finally, the combination of CaP-based composites with different components of human bone tissue is also being explored. Over the last 20 years, autografts have been established as the gold standard in bone regeneration procedures, ensuring native structure and properties of bone ECM along with avoiding rejection from the immune system. However, the autologous bone supply is limited and the need to perform an additional surgery leads to the increased possibility of infections and donor site morbidity. The alternative focuses on using xenografts (usually from pigs or bovines [45,46][45][46]), or allografts from healthy donors [47,48,49][47][48][49]), which although solve the problem of availability, carry the risk of pathogen transmission and may induce the rejection by the recipient. Thus, a successful usage of allografts and xenografts in vivo requires a thorough removal of the component inducing the immune response such as elimination of the donor cells by decellularization [50,51][50][51] while maintaining the composition and functionality of ECM intact, vital for osteogenic induction [13]. Pulverized human bone and chitosan (a polysaccharide derived from chitin, a natural biopolymer) in combination with a β-TCP scaffold has been shown to promote cellular viability and osteogenic differentiation in vitro [52]. Even more, ALP activity was increased in the bone-containing sample compared to the control scaffold with only chitosan and CaP. Sargolzaei and coworkers assessed the effect of OCP granules and rat bone matrix gelatin (a polymer derived from the hydrolysis of collagen), alone or in combination, in critical-sized tibia defect in rats [53]. All three implants exhibited similar positive results, improving bone repair, and showing a good resorption of implanted materials in the early stages of bone formation. However, in the combinatorial scaffold, both type of particles, especially the bone matrix gelatin, were absorbed more rapidly compared to implants of each material alone, which could explain the lack of synergistic effect between OCP and bone matrix gelatin. The same study was performed in a rat mandibular defect model and the combination of OCP and bone matrix gelatin showed significantly better results than each material alone in terms of newly formed bone volume [54].
In addition to the composition of the material, the osteoinductive capacity of a scaffold designed for bone tissue engineering is highly dependent of the pore microarchitecture. Thus, high porosity and interconnectivity between the pores is essential not only for the correct transport of oxygen, nutrients, and essential factors, but to promote cellular infiltration and vascularization of the tissue. Scaffolds can have pores of different sizes ranging from macropores (>100 μm), which induce the cellular infiltration (such as macrophages to eliminate bacteria) and vascularization, to micropores (<50 µm). Osteoblasts, with an own size of 10–50 μm, prefer larger pores in the range 100–200 μm [55]. Even more, recent evidences have indicated that a bigger pore size (300–800 µm) leads to better osteoblast colonization, vascularization, and bone formation [56], accordingly with natural trabecular bone, which presents a pore size of up to 1 mm [57]. Besides, the morphology and porosity of the graft also influences the degradability and the mechanical properties of the implant. Therefore, when designing the pore size and distribution in a scaffold, it is also necessary to consider the degradability of the material, since high porosity and interconnectivity accelerates the degradation, compromising the mechanical and structural properties of the implant before it is completely substituted by new bone [57].
The simultaneous addition of micropores together with macropores in CaP-based scaffolds, improves bone growth in the macropores and provides them with better mechanical properties. New bone growth into the micropores improves the load transfer, decreases crack propagation and provides a toughening mechanism due to the chemical bond that forms between CaPs and bone [58]. The CaP-based materials enable a chemical bond between bone and scaffold through the formation of an apatite layer at the interface of both. Such a strong chemical bond in micropores, which are well-connected with macropores, provides a larger anchoring area that improves the stability and load transfer, resulting in better crack arrests. Definitely, both macro and micropores increase the total surface of the bone-scaffold interface leading to better mechanical integrity and osteointegration of the scaffold within the defect. Besides, micropores can induce capillary forces that enhance the cells to infiltrate and attach to the scaffold, promoting a homogeneous bone distribution [59]. The increased surface area can therefore offer more protein adsorption sites and accelerate the release of degradation products (calcium, strontium, or magnesium), which facilitate several cellular processes: attachment, proliferation, differentiation, biomineralization, etc. [60]. In agreement with this line, recently, it has been demonstrated that high microporosity (39%) indirectly enhances osteoconduction in wide-open porous CaP-based scaffolds [61]. The increased specific surface area facilitate bone ingrowth by increased Ca2+ ion release, which stimulate the cells for new bone synthesis.
In conclusion, the current trend in the field of tissue engineering focuses on the design of large-scale highly reproducible synthetic scaffolds, with CaP as a key component, which meets the properties that we have discussed, such as osteoconduction, osteoinduction, biocompatibility, and having a degradation rate equal to the new bone formation rate, so that it can be gradually replaced by host tissue. These composites can have different presentations, granules, scaffolds, or hydrogels, with different pore microarchitectures. Moreover, the combination of several materials and micropore sizes favors a synergy between the different components, enhancing the bone regenerative properties of the scaffolds, and compensating their possible weaknesses. Overall, these diverse materials can be further supplemented with active molecules to improve their osteoinductive capacity and promote faster bone healing, which will be discussed in the following section.

2.2. Supplemented Scaffolds

During the healing process, bone ECM provides biophysical and biochemical support to the bone cells by dynamically interacting with osteoclasts and osteoblasts, regulating resorption and new bone formation. In that way, the composition and structure of inorganic and organic bone matrix may directly affect bone quality [13] and determine the fate of the progenitors of bone cells. Different strategies to closely mimic the bone microenvironment focus on adding bioactive factors to scaffolds [62,63][62][63]; as surface modification of scaffolds or via the addition of bioactive molecules and drugs that regulate bone tissue homeostasis.

2.2.1. Surface Modifications

The attachment of a bioactive domain to the surface of the scaffold has been recently proposed as a strategy to improve cell adhesion, proliferation, and osteogenic differentiation of MSCs. We will now state several novel strategies such as silk fibroin (SF), hydrogels, and demineralized bone matrix (DBM), based on this approach.

Silk Fibroin

SF, a fibrous protein produced by the domestic silk moth, Bombyx mori, is a promising natural organic material for use in biomedical applications, thanks to its biocompatibility and biodegradability properties. However, its weak gelation performance and the current lack of biochemical cues to trigger cell proliferation and differentiation, significantly limits its clinical application. To solve this problem, Yan Y. and collaborators developed novel hydrogels from SF containing abundant residues of RGD (arginine-glycine-aspartate tri-amino acid sequence; the most widely studied adhesive peptide in the biomaterials field [64]), which besides acting as cell adhesive peptides, are also responsible for signal transduction and osteogenic differentiation of MSCs [65,66][65][66]. Moreover, an improved version consisting of the addition of a small peptide gelator (NapFFRGD; Nap- phenylalanine- Phenylalanine-RGD) to the SF solution through cooperative molecular self-assembly resulted in a more stable SF hydrogel at a much lower gelation concentration plus much shorter gelation time [67,68][67][68].
Another novel strategy to improve the cell adhesion, proliferation and differentiation into SF scaffold is the adhesion of an elastin-like polypeptide (ELP, Val-Pro-Gly-Xaa-Gly) [69] via simple and green dehydrothermal (DHT) treatment, which represents an environment-friendly strategy and possesses high reproducibility [70,71][70][71]. Chen and coworkers demonstrated that bone marrow-derived MSCs (BM-MSCs) exhibited not only improved spreading and proliferation on the SF-ELP-DHT scaffolds, but also showed enhanced mature bone tissue formation compared to the naked SF scaffolds [72]. These results pointed out recombinant ELP modified silk scaffold as a promising candidate material for bone regeneration, given that it could mimic the required bone 3-dimensional (3D) microenvironment.

Hydrogel

Bioactive hydrogels have also been a focal point in the field of bone regeneration due to their ability to mimic the natural ECM microenvironment of the bone [73]. However, biopolymer-based hydrogels suffer from low mechanical properties, uncontrolled degradation, plus insufficient osteogenic activity, which limits their applications in bone regeneration. To overcome these drawbacks, hybrid gelatin/oxidized chondroitin sulfate (OCS) hydrogels have been developed as bioactive fillers [74]; while chondroitin sulfate is a glycosaminoglycan found in the bone ECM that increases the efficacy of arrangement of certain growth factors (GFs) involved in bone regeneration, gelatin, a water-soluble biocompatible biopolymer, facilitates cell adhesion and biomolecules deposition. Moreover, the incorporation of mesoporous (contains pores with diameters between 2 and 50 nm) bioactive glass nanoparticles (MBGNs) in the hydrogels significantly improve their mechanical properties, as has been demonstrated both in vitro and in vivo through the proliferation and osteogenic differentiation of rat BM-MSCs and rat cranial defect restoration, respectively. Therefore, the hybrid Gelatin-OCS/MBGN hydrogels is another interesting option to consider as injectable biomaterials or scaffolds for bone regeneration/repair applications.
Other approaches that aim to recapitulate the complexity and signaling properties of bone ECM are focused on the development of microporous (pores smaller than 2 nm in diameter) and nanofibrous hydrogels exhibiting multiple bioactive epitopes [75]. The supramolecular environment is created by orthogonal enzymatic cross-linking that comprises hyaluronic acid modified with tyramine (derived from the amino acid tyrosine; HA-Tyr) and peptides amphiphiles (peptide-based molecules that comprises a hydrophilic peptide sequence attached to a lipid tail; PAs), designed to promote cell adhesion (RGDs-PA), osteogenesis (Osteo-PA), and angiogenesis (Angio-PA). Results confirmed the capacity of the HA-Tyr/RGDs-PA/Osteo-PA/Angio-PA hydrogel to promote cell adhesion as well as osteogenic and angiogenic differentiation. This strategy looks encouraging not only for bone tissue regeneration in vivo, but for lifelike bone tissue engineering in vitro. For instance, since the hydrogel recreates key structural and signaling elements of the native bone environment, in vitro drug screening could be a promising application.

Demineralized Bone Matrix

As mentioned before, DBM a polyporous bioscaffold commonly used for bone regeneration must be processed before being used for bone engineering purposes, losing its cell adhesion and osteoinductive abilities. Selective cell retention technology, based on the functionalization of DBM with molecules known to bind cells, has been used to improve the MSCs adhesion to the DBM and therefore the osteoinductive abilities of these scaffolds. Thus, DBM scaffolds with collagen-binding domains (CBD) have been recently designed, containing IKVAV (isoleucine-lysine-valine-alanine-valine) and RGD sequences, which are the core functional amino acid sequences of laminin and RGD-containing ECM proteins, respectively [76]. As expected, this DBM/CBD-IKVAV-cRGD composites increased the MSC adhesion capacity in vitro and osteogenesis in vivo. In this line, other scaffolds with the same approach have also shown promising results, such as a DBM scaffold with a CBD containing the core functional amino acid sequences of laminin α4 (CBD-LN peptide) [77]. In vivo, this DBM/CBD-LN scaffold promoted not only rapid bone formation but also angiogenesis, establishing its reputation as a new potential biomaterial in bone tissue engineering.
In addition to cellular adhesion and differentiation, the recruitment of a sufficient number of MSCs and ECs to the bone defect area is critical for bone repair. For instance, the regulation of protein tyrosine phosphatase 1B (PTP1B; a protein localized at the cytoplasmic face of the endoplasmic reticulum which is a negative regulator of the insulin signaling pathway) has been closely related to the stable residence of these MSCs and ECs in their niches. It has been suggested that the phosphorylation state of PTP1B tyrosine-152 (Y152) plays a central role in initiating the departure of MSCs and ECs from their niches and their subsequent recruitment to bone defects. In fact, the peptide 152RM (PTP1B Y152 region-mimicking peptide) loaded onto DMB scaffolds with mesoporous silica nanoparticles (MSNs) [78] significantly inhibited the phosphorylation of PTP1B Y152 [79], enhanced MSCs migration and osteogenic differentiation. Moreover, in vivo studies showed that this scaffold coupled the osteogenesis and angiogenesis processes, by inducing bone formation and the expansion of a certain type of blood vessels adjacent to the growth plate, closely related to the speed of bone healing [80].

2.2.2. Addition of Bioactive Molecules

As mentioned above, in addition to its structural role, ECM provides a complex network of biochemical and physiological signals that affect cellular proliferation and differentiation [81]. Although bone ECM is mainly composed by collagen type I, there have been identified more than 100 ECM proteins other than collagen type I [82]. For this reason, several approaches based on the addition of different bioactive molecules (such as hormones and GFs) to novel scaffolds have been carried out in order to promote osteogenic differentiation of MSCs and in consequence, bone formation [83].
MSCs are the common progenitors of osteoblasts and adipocytes; hence, it is not surprising that MSCs’ fate is delicately balanced and regulated by a number of signaling pathways involving different players. The identification of specific molecular switches that govern MSC lineage commitment has been crucial to promote osteogenic differentiation of MSCs. Tribbles homolog 3 (Trb3), a member of tribbles family pseudokinases, exhibits essential roles in cellular differentiation by regulating the activity of various transcription factors and GFs such as BMPs [84]. Since Trb3 stimulates osteoblastic differentiation in vitro and in vivo [85], Fan and coworkers designed a novel gelatin-conjugated caffeic acid-coated apatite/PLGA scaffold to induce its local delivery in vivo [86]. They demonstrated that Trb3 really acts as a key molecular switch determining MSC lineage fate, suggesting that it could be a treatment option to improve bone repair, by promoting osteoblastic commitment of MSCs at the expense of adipocyte differentiation. On the other hand, ECM remodeling has also been proposed as a novel strategy to control MSCs fate during self-healing, given that the regulation of the expression of matrix metalloproteinases (MMPs), metallopeptidases responsible for the cleavage of the protein components of ECM, may induce MSCs differentiation into osteogenic lineage. For instance, growth of MSCs on a remodeled Col I matrix by MMP13 stimulates osteogenic differentiation and self-healing of bone tissue [87].
Another compelling alternative focuses on bioactive materials containing hormones which regulate bone homeostasis. Parathyroid hormone (PTH) mediates calcium and phosphate homeostasis, thus regulating bone growth. In fact, the 1–34 amino acid fragment of PTH (PTH(1–34), also known as teriparatide), is the active sequence responsible for the bone remodeling function of PTH [88] and it has been approved for its use as an osteoanabolic drug in the clinical treatment of bone defects, such as osteoporosis [89]. PTH(1–34) along with nano-HA (nHA) and hydrogel combinations (to emulate the natural structures of bone) have been integrated to facilitate osteogenic differentiation of BM-MSCs [90]. The nanofibers and porous structure of the Gel-nHA-PTH scaffolds enhanced cell adhesion and showed good binding with bone tissue. Furthermore, with the PTH(1–34) addition, the scaffold nanofibers became finer, which increased its conducive to bone regeneration. Predictably, implantation of the hydrogel into a rat cranial defect model led to efficient bone regeneration, revealing the simultaneous therapeutic effect of nHA and PTH during the treatment process.
At last, the combination of osteoinductive GFs with osteoconductive biomaterials remains a promising approach to promote bone regeneration [91]. GFs are the most influential bioactive molecules and mediators of the natural bone repair process. Although these soluble factors have approved applications in bone regeneration, they present several limitations that could restrict their clinical usage [92,93][92][93]. For instance, early GF delivery approaches [94] resulted in low availability of bioactive GFs due to their rapid degradation in vivo, short half-life in physiological conditions, and deactivation by enzymes [95]. In fact, the poor pharmacokinetics of these proteins has led to the delivery of high doses, with the consequent increase in the risk of serious side effects. To solve this problem, the development of novel vehicles able to control the release of GFs is the goal to be achieved [96].

BMP-2

Multiple GFs have been identified to be involved in bone regeneration, including platelet-derived growth factor, transforming growth factor-beta (TGFβ), fibroblast growth factors, insulin-like growth factors and BMPs. Among them, BMP signaling pathway, and in particular the signaling elicited by BMP-2, has been the most extensively studied due to its role in osteoblastic differentiation [97], angiogenesis [98], and cell signaling during fracture healing [99]. In fact, BMP-2 is considered the most remarkable bone-related GF due to its ability to increase the expression of osteogenic markers [100], such as ALP and osteocalcin [101], besides its role in the early stage of bone formation and repair [99].
However, these proteins are so potent that they can induce undesired bone formation in other tissues, and accordingly they require a vehicle to guide them to the damaged area [102]. For instance, products containing recombinant human BMP-2 (rhBMP2) [103] loaded in bovine absorbable collagen-type-I matrix scaffold have been used clinically to treat open tibia fracture [104], spine and craniofacial defects in the last decade [105]. These and other rhBMP2 based products, however, have shown controversial results in terms of efficacy and adverse effects [106]. Despite delivery of supraphysiological doses of BMP-2 being needed to induce bone formation, those doses seem to induce pathological events [107]. To cope with these limitations, intensive research studies are still ongoing in order to determine the best material carrier of BMP-2 [108], which can deliver the minimum required dose for improving bone repair and thus diminish side effects. To this aim, a large number of material carriers and delivery systems have been investigated for controlled, localized, and sustained release of BMP-2 [109,110][109][110].
Physiologically, BMP-2 bioavailability and signaling is regulated by either low or high binding affinity to ECM components [111]. In fact, some tissue-engineering strategies combine recombinant BMPs with naturally occurring ECM components (derived from MSCs [112]), in such a way that it modulates BMP-2 release and therefore enhances bone formation. For instance, Larochette and coworkers compared the efficacy of osteogenic mineralized MSC-derived ECM to the one obtained from ECM from undifferentiated hMSCs, using implanted polycaprolactone scaffolds [113]. The outcomes reflect that the osteoinductive potential of BMP-2 was greater when loaded within an osteogenic mineralized MSC-derived ECM, displaying a higher sequestration capacity of BMP-2 over time in vivo.
To improve the system, the encapsulation of BMPs into polymeric microspheres has emerged as one of the most promising methods to provide local and controlled delivery of BMP-2. However, fabrication of microspheres requires the use of toxic solvents which limits the bioactivity retention and their commercialization. To solve this problem, a method for solvent-free fabrication of porous microspheres from high internal phase emulsions using a controlled fluids setup (polyHIPE) has been developed [114]. In addition to the advantage of solvent-free fabrication, this method uniquely provides in-line loading of BMP-2 directly into the pores of the microspheres, with high loading efficiencies. Recently, key relationships between microsphere properties and the resulting BMP-2 release kinetics have been established [115]. First, bioactivity retention of encapsulated rhBMP2 was confirmed. Next, it was established that the BMP-2 release from microspheres induced osteogenic differentiation of hMSCs. Finally, the microsphere incorporation had minimal effect on the cure and compressive properties of an injectable polyHIPE bone graft. Overall, this work draws attention to the strong potential that these microsphere-polyHIPE composites present to enhance bone regeneration through controlled release of BMP-2 and other GFs. Moreover, the use of microspheres has demonstrated great advantages when compared with other BMP-2 delivery systems such as hydrogels and surface modified ceramics; typical mesh sizes of hydrogels result in a burst release that does not allow controlling kinetics, while surface-modified ceramics present reduced loading efficiencies during fabrication, which raises scale-up concerns.
Recently, spatiotemporal delivery of BMP-2, along with other factors that play an important role in bone formation, has been proposed to improve bone regeneration. While chemokines (such as Interleukin-(IL)-8) recruit circulating stem cells to the defect site [116], GFs such as BMP-2, induce the recruited cells to undergo chondrogenesis and osteogenesis to form bone [117]. That way, and according to the key steps of natural regenerative process, it is crucial to combine stem cell recruitment and bionic sequential delivery of chemokine and GFs to achieve effective bone regeneration. Therefore, the synergistic effect of BMP-2 and IL-8 on the key processes of bone regeneration was studied and then, a spatiotemporal delivery system for rapid in situ guided bone regeneration was designed [118]. Thus, macroporous (pores larger than 50 nm in diameter)/mesoporous bioactive glass scaffold has been used as matrix, to synergistically achieve a rapid release of IL-8 followed by a long-term sustained release of BMP-2. Outcomes demonstrated efficient stem cell recruitment and a “chondrogenic/osteogenic balance”, thanks to the spatiotemporal delivery of IL-8 and BMP-2. Ultimately the scaffold induced early extensive bone mineralization and an advanced regeneration throughout the repair of large bone defect. Overall, this new delivery system could provide insights toward designing bone-repairing biomaterials with higher regenerative efficiency.
Finally, multicell-mediated bone tissue regeneration has been studied by the use of rhBMP2-loaded trimodal macro/micro/nano-porous bioactive glass scaffold as a substrate model [119]. First, the combination of different porous structures regulates cellular function: while macropores activate migration of cells, micro/nano-scale pores increase the specific surface area generating expedited dissolution-deposition and rapid material biodegradation [120]. Then, the incorporation of BMPs lead to the stimulation of osteoclastogenesis as well as promoting osteogenesis, ensuing osteoclast-regulated material resorption [121,122][121][122]. That way, as results suggested, rhBMP2 facilitated osteoclastogenesis-mediated scaffold degradation and up-regulated osteogenesis. Synchronization of material resorption and new bone formation was vital to achieve harmonious bone regeneration in the treatment of large bone defects.

2.2.3. Addition of Drugs Relevant for Bone Tissue Homeostasis

Some materials, in addition to enhancing the mechanical properties of natural polymers, overactivate osteoclasts and impair proliferation and osteogenic differentiation of MSCs; that is the case of the graphene oxide (GO)-related hydrogels [123,124][123][124]. To address this problem, administration of antiresorptive drugs such as bisphosphonates have been used to rebalance the general bone microenvironment and promote osteogenic differentiation. Hence, Alendronate (Aln), a first-line antiresorptive drug used in clinical treatment of osteoporosis, has been bound to GO-related type I collagen hydrogel, creating a Col-GO-Aln sponge [125] which exhibited active anti-osteoclastogenic and osteogenic ability in vitro and in rat preclinical models of osteoporosis. These results suggest the potential of GO related biomolecule loaded hydrogel in the treatment of osteoporotic bone defects.
Finally, the temporally controlled delivery of biochemical compounds has also been addressed with MSNs designing films that can guide MSCs differentiation towards the osteogenic lineage. These films have been loaded with dexamethasone, a glucocorticoid known to induce osteogenic differentiation of MSCs in vitro [126]. Temporally controlled dexamethasone delivery led to increased ALP levels and matrix mineralization compared to directly supplementing dexamethasone to the medium. Thus, MSN coatings mimic the sequential appearance of bioactive factors during tissue regeneration, which will ultimately lead to biomaterials with improved bioactivity.
The mentioned addressed approaches are summarized in Figure 1.
Ijms 22 07724 g001 550
Figure 1. Regulation of cell fate and induction of osteogenic differentiation of MSCs by supplemented scaffolds. Surface modifications of the scaffolds by the attachment of a bioactive domain (Left), with the aim of improving adhesion, proliferation, and osteogenic differentiation of MSCs. Addition of bioactive molecules or drugs (Right) regulates bone homeostasis to emulate the complex network of biochemical and physiological signals that are representative in bone ECM.

2.3. Macrophages Polarization

In bone tissue engineering, osteointegration of the engineered graft is a key process occurring at the bone-implant interface, prompted by the response of the immune cells to the graft and the subsequent differentiation of osteoprogenitors. In fact, this immune reaction to the scaffolds is of great interest, since it is known to be a crucial factor influencing healing effectiveness. The first immune cell players interacting with bone implants are macrophages, orchestrating the host immune response to the grafted biomaterial. Bone repair can be divided into a first proinflammatory stage and a subsequent regenerative phase [127]. Immediately after a fracture has occurred, immune cells such as platelets, neutrophils, lymphocytes, and macrophages are recruited to the site of bone injury, playing a critical role in bone fracture repair by secreting inflammatory factors. Among them, macrophages and phagocytic cells differentiated from monocytes, take part in these two different stages of bone healing process, taking advantage of their functional plasticity, determined by the molecules they secrete. Thus, proinflammatory M1 macrophages are needed for the first stage of bone repair, facilitating the recruitment and osteogenic priming of MSCs to the injury site. Conversely, anti-inflammatory M2 macrophages, promote bone tissue healing [127]. This polarization of M1 macrophages to the M2 phenotype is a key step not only for bone healing but also for the osteointegration of bone tissue engineered grafts. In fact, chronic inflammatory conditions, such as diabetes, originate in an imbalanced host immune reaction to scaffold, in which the switch from M1 to M2 macrophages does not occur at the bone-implant interface, determining the failure of the tissue engineering graft [128]. Therefore, great efforts are currently being addressed to design immunomodulatory and, at the same time, pro-osteogenic scaffolds capable of regulating and boosting the switch of M1 macrophages to M2 phenotype. The use of pro-osteogenic scaffolds carrying immunomodulatory molecules such as ILs or micro ribonucleic acids (microRNAs) [129,130][129][130] or the modulation of surface topographical cues of the scaffolds [131] are among the strategies currently being used to improve the bone healing facilitated by endogenous macrophages.

2.3.1. Interleukin-4

The combined use of a wide range of pro-osteogenic scaffolds such as decellularized bone matrix, bi-layer hydrogel-porous scaffolds, and calcium-enriched hydrogels [129,132,133][129][132][133] loaded with IL-4, a key anti-inflammatory cytokine secreted by M2 macrophages, is now being explored as a promising strategy for repair of bone defects [129,133][129][133]. Interestingly, calcium-enriched hydrogels loaded with IL-4 showed superior in vitro and in vivo abilities in inducing both M2 macrophages polarization and MSCs osteogenesis by enhancing TGF-β1/Smad pathway. The coordination of these two processes by the sustained release of IL-4 from scaffolds has been pointed out to be a key factor driving bone regeneration [129].

2.3.2. MicroRNAs

MiRNAs, small non-coding ribonucleic acids (RNAs) involved in gene regulation at a post-transcriptional level, have been shown to be key players for the maintenance of bone tissue homeostasis by regulating both bone resorption and bone formation processes [134]. Indeed, a number of miRNAs with anti or pro-osteogenic capabilities have been identified, several of which are dysregulated in bone pathologies such as osteoporosis [135]. Due to the fact that miRNAs possess an intrinsic ability to target multiple genes and pathways, miRNA therapeutics (enhancement of the expression of miRNA with RNA mimics or miRNA expression inhibition by antagomiRs) is being considered as a coming realistic therapeutic strategy to elicit a more pronounced bone regeneration in bone-related pathologies. Since macrophages orchestrate a critical role in mediating host body reaction toward implanted biomaterial, the possibility of adding miRNAs therapeutics to pro-osteogenic scaffolds is being explored to induce M2 macrophage polarization [136].
In this way, the effectiveness of the inhibition of miR133a for bone repair has been recently tested in vivo by a bone tissue engineering approach with encouraging results [130]. Given the known role of miR133a as a negative regulator of osteogenesis in MSCs [137], Castaño and coworkers took advantage of collagen-nanoHA scaffolds loaded with antagomiR-133a, which was efficiently delivered to host cells. Moreover, a prominent bone repair in the antagomiR-treated group compared to the antagomiR-free scaffolds was confirmed by microstructure and histological analysis. Interestingly, an increase of M2 macrophages in the scaffolds loaded with antagomiR-133a was detected, suggesting a causative role of the increased presence of M2 macrophages in the scaffold interface with the accelerated bone healing observed in the antagomiR treatment group. Importantly, this study pointed to a new, understudied interplay between miRNA-mediated bone repair and M2 macrophage polarization which could be exploited in future scaffold-miRNA based strategies.

2.3.3. Surface Topography Modulation

Modulating the surface topography of biomaterials to induce macrophage polarization has been a strategy widely studied over the last years [138]. Regarding bone-tissue engineering, the use of scaffolds with pore dimensions at the nanoscale level has been shown to be a pro-osteogenic strategy, by enhancing M2 polarization [139,140][139][140]. Recently, the underlying mechanism of how these nano-scale surface topographical cues modulate M2 polarization has been unraveled by transcriptomic approaches. By comparing honeycomb-like titanium dioxide (TiO2) structures with different pore sizes (ranging between 90 and 5000 nm), authors demonstrated the increased osteogenic potential of 90 nm pore scale scaffolds in vitro and in vivo, which enhanced MSCs osteogenic differentiation and M2 macrophage polarization [131]. Interestingly, the more pronounced confinement of macrophages in honeycomb-like TiO2 scaffolds with the smaller pore (90 nm) induced an activation of the RhoA/ROCK signaling pathway linked to an increased formation of filopodia, a mechanism pointed to be the driving cue shifting macrophages toward M2 polarization.

References

  1. Berendsen, A.D.; Olsen, B.R. Bone development. Bone 2015, 80, 14–18.
  2. Blumer, M.J.F. Bone tissue and histological and molecular events during development of the long bones. Ann. Anat. 2021, 235.
  3. Fu, R.; Liu, C.; Yan, Y.; Li, Q.; Huang, R.L. Bone defect reconstruction via endochondral ossification: A developmental engineering strategy. J. Tissue Eng. 2021, 12.
  4. Hankenson, K.D.; Dishowitz, M.; Gray, C.; Schenker, M. Angiogenesis in bone regeneration. Injury 2011, 42, 556–561.
  5. Stegen, S.; van Gastel, N.; Carmeliet, G. Bringing new life to damaged bone: The importance of angiogenesis in bone repair and regeneration. Bone 2015, 70, 19–27.
  6. Schemitsch, E.H. Size Matters: Defining Critical in Bone Defect Size! J. Orthop. Trauma. 2017, 31, S20–S22.
  7. Roddy, E.; DeBaun, M.R.; Daoud-Gray, A.; Yang, Y.P.; Gardner, M.J. Treatment of critical-sized bone defects: Clinical and tissue engineering perspectives. Eur. J. Orthop. Surg. Traumatol. 2018, 28, 351–362.
  8. Winkler, T.; Sass, F.A.; Duda, G.N.; Schmidt-Bleek, K. A review of biomaterials in bone defect healing, remaining shortcomings and future opportunities for bone tissue engineering: The unsolved challenge. Bone Joint. Res. 2018, 7, 232–243.
  9. Odén, A.; McCloskey, E.V.; Kanis, J.A.; Harvey, N.C.; Johansson, H. Burden of high fracture probability worldwide: Secular increases 2010–2040. Osteoporos. Int. 2015, 26, 2243–2248.
  10. Baldwin, P.; Li, D.J.; Auston, D.A.; Mir, H.S.; Yoon, R.S.; Koval, K.J. Autograft, Allograft, and Bone Graft Substitutes: Clinical Evidence and Indications for Use in the Setting of Orthopaedic Trauma Surgery. J. Orthop. Trauma. 2019, 33, 203–213.
  11. Hinsenkamp, M.; Muylle, L.; Eastlund, T.; Fehily, D.; Noël, L.; Strong, D.M. Adverse reactions and events related to musculoskeletal allografts: Reviewed by the World Health Organisation Project NOTIFY. Int. Orthop. 2012, 36, 633–641.
  12. Sheehy, E.J.; Kelly, D.J.; O’Brien, F.J. Biomaterial-based endochondral bone regeneration: A shift from traditional tissue engineering paradigms to developmentally inspired strategies. Mater. Today Bio. 2019, 3, 100009.
  13. Alcorta-Sevillano, N.; Macías, I.; Infante, A.; Rodríguez, C.I. Deciphering the Relevance of Bone ECM Signaling. Cells 2020, 9, 2630.
  14. Murphy, W.L.; McDevitt, T.C.; Engler, A.J. Materials as stem cell regulators. Nat. Mater. 2014, 13, 547–557.
  15. Diomede, F.; Marconi, G.D.; Fonticoli, L.; Pizzicanella, J.; Merciaro, I.; Bramanti, P.; Mazzon, E.; Trubiani, O. Functional Relationship between Osteogenesis and Angiogenesis in Tissue Regeneration. Int. J. Mol. Sci. 2020, 21, 3242.
  16. Albrektsson, T.; Johansson, C. Osteoinduction, osteoconduction and osseointegration. Eur. Spine. J. 2001, 10, S96–S101.
  17. Boskey, A.L. Bone composition: Relationship to bone fragility and antiosteoporotic drug effects. Bonekey Rep. 2013, 2, 447.
  18. Boskey, A.L.; Coleman, R. Aging and bone. J. Dent. Res. 2010, 89, 1333–1348.
  19. Gregson, C.L.; Paggiosi, M.A.; Crabtree, N.; Steel, S.A.; McCloskey, E.; Duncan, E.L.; Fan, B.; Shepherd, J.A.; Fraser, W.D.; Smith, G.D.; et al. Analysis of body composition in individuals with high bone mass reveals a marked increase in fat mass in women but not men. J. Clin. Endocrinol. Metab. 2013, 98, 818–828.
  20. Boskey, A.; Mendelsohn, R. Infrared analysis of bone in health and disease. J. Biomed. Opt. 2005, 10, 031102.
  21. Lotsari, A.; Rajasekharan, A.K.; Halvarsson, M.; Andersson, M. Transformation of amorphous calcium phosphate to bone-like apatite. Nat. Commun. 2018, 9, 4170.
  22. Jeong, J.; Kim, J.H.; Shim, J.H.; Hwang, N.S.; Heo, C.Y. Bioactive calcium phosphate materials and applications in bone regeneration. Biomater. Res. 2019, 23, 4.
  23. Kim, S.E.; Park, K. Recent Advances of Biphasic Calcium Phosphate Bioceramics for Bone Tissue Regeneration. Adv. Exp. Med. Biol. 2020, 1250, 177–188.
  24. Othman, Z.; Fernandes, H.; Groot, A.J.; Luider, T.M.; Alcinesio, A.; Pereira, D.M.; Guttenplan, A.P.M.; Yuan, H.; Habibovic, P. The role of ENPP1/PC-1 in osteoinduction by calcium phosphate ceramics. Biomaterials 2019, 210, 12–24.
  25. Danoux, C.; Pereira, D.; Döbelin, N.; Stähli, C.; Barralet, J.; van Blitterswijk, C.; Habibovic, P. The Effects of Crystal Phase and Particle Morphology of Calcium Phosphates on Proliferation and Differentiation of Human Mesenchymal Stromal Cells. Adv. Healthc. Mater. 2016, 5, 1775–1785.
  26. Bohner, M.; Miron, R.J. A proposed mechanism for material-induced heterotopic ossification. Mater. Today 2019, 22, 132–141.
  27. Inzana, J.A.; Olvera, D.; Fuller, S.M.; Kelly, J.P.; Graeve, O.A.; Schwarz, E.M.; Kates, S.L.; Awad, H.A. 3D printing of composite calcium phosphate and collagen scaffolds for bone regeneration. Biomaterials 2014, 35, 4026–4034.
  28. Soeyono, G.; Dahlan, K.; Purba, M.S.; Widhyari, S.D.; Soesatyoratih, R.; Teng, T.S.; Budiarti, L.; Wai, H.K.; Kosat, A. Assessment of biphasic calcium phosphate 70/30 alginate scaffold on the tibia in pigs. Vet. World 2020, 13, 2635–2642.
  29. Chen, Y.H.; Tai, H.Y.; Fu, E.; Don, T.M. Guided bone regeneration activity of different calcium phosphate/chitosan hybrid membranes. Int. J. Biol. Macromol. 2019, 126, 159–169.
  30. Pinto, R.V.; Gomes, P.S.; Fernandes, M.H.; Costa, M.E.V.; Almeida, M.M. Glutaraldehyde-crosslinking chitosan scaffolds reinforced with calcium phosphate spray-dried granules for bone tissue applications. Mater. Sci. Eng. C Mater. Biol. Appl. 2020, 109.
  31. Backes, E.H.; Fernandes, E.M.; Diogo, G.S.; Marques, C.F.; Silva, T.H.; Costa, L.C.; Passador, F.R.; Reis, R.L.; Pessan, L.A. Engineering 3D printed bioactive composite scaffolds based on the combination of aliphatic polyester and calcium phosphates for bone tissue regeneration. Mater. Sci. Eng. C Mater. Biol. Appl. 2021, 122.
  32. Yeo, T.; Ko, Y.G.; Kim, E.J.; Kwon, O.K.; Chung, H.Y.; Kwon, H.O. Promoting bone regeneration by 3D-printed poly (glycolic acid)/hydroxyapatite composite scaffolds. J. Ind. Eng. Chem. 2021, 94, 343–351.
  33. Naahidi, S.; Jafari, M.; Logan, M.; Wang, Y.; Yuan, Y.; Bae, H.; Dixon, B.; Chen, P. Biocompatibility of hydrogel-based scaffolds for tissue engineering applications. Biotechnol. Adv. 2017, 35, 530–544.
  34. Schweikle, M.; Bjørnøy, S.H.; van Helvoort, A.T.J.; Haugen, H.J.; Sikorski, P.; Tiainen, H. Stabilisation of amorphous calcium phosphate in polyethylene glycol hydrogels. Acta Biomater. 2019, 90, 132–145.
  35. Luo, Y.; Chen, S.; Shi, Y.; Ma, J. 3D printing of strontium-doped hydroxyapatite based composite scaffolds for repairing critical-sized rabbit calvarial defects. Biomed. Mater. 2018, 13.
  36. Mansour, A.; Abu Nada, L.; El-Hadad, A.A.; Mezour, M.A.; Ersheidat, A.; Al-Subaie, A.; Moussa, H.; Laurenti, M.; Kaartinen, M.T.; Tamimi, F. Biomimetic trace metals improve bone regenerative properties of calcium phosphate bioceramics. J. Biomed. Mater. Res. A 2021, 109, 666–681.
  37. Tang, Y.; Wu, C.; Wu, Z.; Hu, L.; Zhang, W.; Zhao, K. Fabrication and in vitro biological properties of piezoelectric bioceramics for bone regeneration. Sci. Rep. 2017, 7.
  38. Draghici, A.D.; Busuioc, C.; Mocanu, A.; Nicoara, A.I.; Iordache, F.; Jinga, S.I. Composite scaffolds based on calcium phosphates and barium titanate obtained through bacterial cellulose templated synthesis. Mater. Sci. Eng. C Mater. Biol. Appl. 2020, 110.
  39. Tandon, B.; Blaker, J.J.; Cartmell, S.H. Piezoelectric materials as stimulatory biomedical materials and scaffolds for bone repair. Acta Biomater. 2018, 73, 1–20.
  40. Chen, W.; Yu, Z.; Pang, J.; Yu, P.; Tan, G.; Ning, C. Fabrication of Biocompatible Potassium Sodium Niobate Piezoelectric Ceramic as an Electroactive Implant. Materials 2017, 10, 345.
  41. Wang, Q.; Yang, J.; Zhang, W.; Khoie, R.; Li, Y.M.; Zhu, J.G.; Chen, Z.Q. Manufacture and cytotoxicity of a lead-free piezoelectric ceramic as a bone substitute-consolidation of porous lithium sodium potassium niobate by cold isostatic pressing. Int. J. Oral. Sci. 2009, 1, 99–104.
  42. Xia, Y.; Fan, X.; Yang, H.; Li, L.; He, C.; Cheng, C.; Haag, R. ZnO/Nanocarbons-Modified Fibrous Scaffolds for Stem Cell-Based Osteogenic Differentiation. Small 2020, 16.
  43. Khare, D.; Basu, B.; Dubey, A.K. Electrical stimulation and piezoelectric biomaterials for bone tissue engineering applications. Biomaterials 2020, 258.
  44. Zheng, T.; Huang, Y.; Zhang, X.; Cai, Q.; Deng, X.; Yang, X. Mimicking the electrophysiological microenvironment of bone tissue using electroactive materials to promote its regeneration. J. Mater. Chem. B 2020, 8, 10221–10256.
  45. Bracey, D.N.; Jinnah, A.H.; Willey, J.S.; Seyler, T.M.; Hutchinson, I.D.; Whitlock, P.W.; Smith, T.L.; Danelson, K.A.; Emory, C.L.; Kerr, B.A. Investigating the Osteoinductive Potential of a Decellularized Xenograft Bone Substitute. Cells Tissues Organs. 2019, 207, 97–113.
  46. Gardin, C.; Ricci, S.; Ferroni, L.; Guazzo, R.; Sbricoli, L.; De Benedictis, G.; Finotti, L.; Isola, M.; Bressan, E.; Zavan, B. Decellularization and Delipidation Protocols of Bovine Bone and Pericardium for Bone Grafting and Guided Bone Regeneration Procedures. PLoS ONE 2015, 10.
  47. Liu, G.; Sun, J.; Li, Y.; Zhou, H.; Cui, L.; Liu, W.; Cao, Y. Evaluation of partially demineralized osteoporotic cancellous bone matrix combined with human bone marrow stromal cells for tissue engineering: An in vitro and in vivo study. Calcif. Tissue Int. 2008, 83, 176–185.
  48. Mauney, J.R.; Blumberg, J.; Pirun, M.; Volloch, V.; Vunjak-Novakovic, G.; Kaplan, D.L. Osteogenic differentiation of human bone marrow stromal cells on partially demineralized bone scaffolds in vitro. Tissue Eng. 2004, 10, 81–92.
  49. Smith, C.A.; Board, T.N.; Rooney, P.; Eagle, M.J.; Richardson, S.M.; Hoyland, J.A. Human decellularized bone scaffolds from aged donors show improved osteoinductive capacity compared to young donor bone. PLoS ONE 2017, 12.
  50. Mendibil, U.; Ruiz-Hernandez, R.; Retegi-Carrion, S.; Garcia-Urquia, N.; Olalde-Graells, B.; Abarrategi, A. Tissue-Specific Decellularization Methods: Rationale and Strategies to Achieve Regenerative Compounds. Int. J. Mol. Sci. 2020, 21, 5447.
  51. Emami, A.; Talaei-Khozani, T.; Vojdani, Z.; Zarei Fard, N. Comparative assessment of the efficiency of various decellularization agents for bone tissue engineering. J. Biomed. Mater. Res. B Appl. Biomater. 2021, 109, 19–32.
  52. Kowalczyk, P.; Podgórski, R.; Wojasiński, M.; Gut, G.; Bojar, W.; Ciach, T. Chitosan-Human Bone Composite Granulates for Guided Bone Regeneration. Int. J. Mol. Sci. 2021, 22, 2324.
  53. Sargolzaei Aval, F.; Arab, M.R.; Sargolzaei, N.; Barfrushan, S.; Mir, M.; Sargazi, G.H.; Sargolzaeiaval, F.; Arab, M. Histomorphometric Analysis of Newly-formed Bone Using Octacalcium Phosphate and Bone Matrix Gelatin in Rat Tibial Defects. Arch. Bone Jt. Surg. 2019, 7, 182–190.
  54. Sargolzaei-Aval, F.; Saberi, E.A.; Arab, M.R.; Sargolzaei, N.; Zare, E.; Shahraki, H.; Sanchooli, T.; Sargolzaeiaval, F.; Arab, M. Reconstruction of mandibular defects using synthetic octacalcium phosphate combined with bone matrix gelatin in rat model. Dent. Res. J. 2020, 17, 10–18.
  55. Bobbert, F.S.L.; Zadpoor, A.A. Effects of bone substitute architecture and surface properties on cell response, angiogenesis, and structure of new bone. J. Mater. Chem. B 2017, 5, 6175–6192.
  56. Hayashi, K.; Munar, M.L.; Ishikawa, K. Effects of macropore size in carbonate apatite honeycomb scaffolds on bone regeneration. Mater. Sci. Eng. C Mater. Biol. Appl. 2020, 111.
  57. Iviglia, G.; Kargozar, S.; Baino, F. Biomaterials, Current Strategies, and Novel Nano-Technological Approaches for Periodontal Regeneration. J. Funct. Biomater. 2019, 10, 3.
  58. Rustom, L.E.; Poellmann, M.J.; Wagoner Johnson, A.J. Mineralization in micropores of calcium phosphate scaffolds. Acta Biomater 2019, 83, 435–455.
  59. Rustom, L.E.; Boudou, T.; Lou, S.; Pignot-Paintrand, I.; Nemke, B.W.; Lu, Y.; Markel, M.D.; Picart, C.; Wagoner Johnson, A.J. Micropore-induced capillarity enhances bone distribution in vivo in biphasic calcium phosphate scaffolds. Acta Biomater 2016, 44, 144–154.
  60. Zhang, K.; Fan, Y.; Dunne, N.; Li, X. Effect of microporosity on scaffolds for bone tissue engineering. Regen Biomater 2018, 5, 115–124.
  61. Ghayor, C.; Chen, T.H.; Bhattacharya, I.; Özcan, M.; Weber, F.E. Microporosities in 3D-Printed Tricalcium-Phosphate-Based Bone Substitutes Enhance Osteoconduction and Affect Osteoclastic Resorption. Int. J. Mol. Sci. 2020, 21, 9270.
  62. Amiryaghoubi, N.; Fathi, M.; Pesyan, N.N.; Samiei, M.; Barar, J.; Omidi, Y. Bioactive polymeric scaffolds for osteogenic repair and bone regenerative medicine. Med. Res. Rev. 2020, 40, 1833–1870.
  63. Safari, B.; Aghanejad, A.; Roshangar, L.; Davaran, S. Osteogenic effects of the bioactive small molecules and minerals in the scaffold-based bone tissue engineering. Colloids Surf. B Biointerfaces 2021, 198.
  64. Bellis, S.L. Advantages of RGD peptides for directing cell association with biomaterials. Biomaterials 2011, 32, 4205–4210.
  65. Lam, J.; Segura, T. The modulation of MSC integrin expression by RGD presentation. Biomaterials 2013, 34, 3938–3947.
  66. Schwab, E.H.; Halbig, M.; Glenske, K.; Wagner, A.S.; Wenisch, S.; Cavalcanti-Adam, E.A. Distinct effects of RGD-glycoproteins on Integrin-mediated adhesion and osteogenic differentiation of human mesenchymal stem cells. Int. J. Med. Sci. 2013, 10, 1846–1859.
  67. Cheng, B.; Yan, Y.; Qi, J.; Deng, L.; Shao, Z.W.; Zhang, K.Q.; Li, B.; Sun, Z.; Li, X. Cooperative Assembly of a Peptide Gelator and Silk Fibroin Afford an Injectable Hydrogel for Tissue Engineering. ACS Appl. Mater. Interfaces. 2018, 10, 12474–12484.
  68. Yan, Y.; Cheng, B.; Chen, K.; Cui, W.; Qi, J.; Li, X.; Deng, L. Enhanced Osteogenesis of Bone Marrow-Derived Mesenchymal Stem Cells by a Functionalized Silk Fibroin Hydrogel for Bone Defect Repair. Adv. Healthc. Mater. 2019, 8.
  69. Engler, A.J.; Sen, S.; Sweeney, H.L.; Discher, D.E. Matrix elasticity directs stem cell lineage specification. Cell 2006, 126, 677–689.
  70. Bruno, B.; Romina, C.; Alicia, S.N.; Paula, C.M. Three-dimensional printing of collagen and hyaluronic acid scaffolds with dehydrothermal treatment crosslinking. Compos. Commun. 2020, 19, 1–5.
  71. Chen, X.; Zhou, L.; Xu, H.; Yamamoto, M.; Shinoda, M.; Kishimoto, M.; Tanaka, T.; Yamane, H. Effect of the Application of a Dehydrothermal Treatment on the Structure and the Mechanical Properties of Collagen Film. Materials 2020, 13, 377.
  72. Chen, Z.; Zhang, Q.; Li, H.; Wei, Q.; Zhao, X.; Chen, F. Elastin-like polypeptide modified silk fibroin porous scaffold promotes osteochondral repair. Bioact. Mater. 2021, 6, 589–601.
  73. Bai, X.; Gao, M.; Syed, S.; Zhuang, J.; Xu, X.; Zhang, X.Q. Bioactive hydrogels for bone regeneration. Bioact. Mater. 2018, 3, 401–417.
  74. Zhou, L.; Fan, L.; Zhang, F.M.; Jiang, Y.; Cai, M.; Dai, C.; Luo, Y.A.; Tu, L.J.; Zhou, Z.N.; Li, X.J.; et al. Hybrid gelatin/oxidized chondroitin sulfate hydrogels incorporating bioactive glass nanoparticles with enhanced mechanical properties, mineralization, and osteogenic differentiation. Bioact. Mater. 2021, 6, 890–904.
  75. Derkus, B.; Okesola, B.O.; Barrett, D.W.; D’Este, M.; Chowdhury, T.T.; Eglin, D.; Mata, A. Multicomponent hydrogels for the formation of vascularized bone-like constructs in vitro. Acta Biomater. 2020, 109, 82–94.
  76. Luo, K.; Gao, X.; Gao, Y.; Li, Y.; Deng, M.; Tan, J.; Gou, J.; Liu, C.; Dou, C.; Li, Z.; et al. Multiple integrin ligands provide a highly adhesive and osteoinductive surface that improves selective cell retention technology. Acta Biomater. 2019, 85, 106–116.
  77. Tang, Y.; Luo, K.; Tan, J.; Zhou, R.; Chen, Y.; Chen, C.; Rong, Z.; Deng, M.; Yu, X.; Zhang, C.; et al. Laminin alpha 4 promotes bone regeneration by facilitating cell adhesion and vascularization. Acta Biomater. 2021, 126, 183–198.
  78. Tang, Y.; Luo, K.; Chen, Y.; Zhou, R.; Chen, C.; Tan, J.; Deng, M.; Dai, Q.; Yu, X.; Liu, J.; et al. Phosphorylation inhibition of protein-tyrosine phosphatase 1B tyrosine-152 induces bone regeneration coupled with angiogenesis for bone tissue engineering. Bioact. Mater. 2021, 6, 2039–2057.
  79. Luo, K.; Tang, Y.; Gao, X.; Tan, J.; Yu, B.; Xu, J.; Luo, F. Inhibition of protein-tyrosine phosphatase 1B phosphorylation enhances early adhesion of mesenchymal stem cells to facilitate fabrication of tissue-engineered bone. J. Tissue Eng. Regen. Med. 2020, 14, 575–587.
  80. Zhang, J.; Pan, J.; Jing, W. Motivating role of type H vessels in bone regeneration. Cell Prolif. 2020, 53.
  81. Kim, S.H.; Turnbull, J.; Guimond, S. Extracellular matrix and cell signalling: The dynamic cooperation of integrin, proteoglycan and growth factor receptor. J. Endocrinol 2011, 209, 139–151.
  82. Salmon, C.R.; Tomazela, D.M.; Ruiz, K.G.; Foster, B.L.; Paes Leme, A.F.; Sallum, E.A.; Somerman, M.J.; Nociti, F.H. Proteomic analysis of human dental cementum and alveolar bone. J. Proteomics 2013, 91, 544–555.
  83. Safari, B.; Davaran, S.; Aghanejad, A. Osteogenic potential of the growth factors and bioactive molecules in bone regeneration. Int. J. Biol. Macromol. 2021, 175, 544–557.
  84. Chan, M.C.; Nguyen, P.H.; Davis, B.N.; Ohoka, N.; Hayashi, H.; Du, K.; Lagna, G.; Hata, A. A novel regulatory mechanism of the bone morphogenetic protein (BMP) signaling pathway involving the carboxyl-terminal tail domain of BMP type II receptor. Mol. Cell Biol. 2007, 27, 5776–5789.
  85. Fan, J.; Guo, M.; Im, C.S.; Pi-Anfruns, J.; Cui, Z.K.; Kim, S.; Wu, B.M.; Aghaloo, T.L.; Lee, M. Enhanced Mandibular Bone Repair by Combined Treatment of Bone Morphogenetic Protein 2 and Small-Molecule Phenamil. Tissue. Eng. Part. A 2017, 23, 195–207.
  86. Fan, J.; Lee, C.S.; Kim, S.; Zhang, X.; Pi-Anfruns, J.; Guo, M.; Chen, C.; Rahnama, M.; Li, J.; Wu, B.M.; et al. Trb3 controls mesenchymal stem cell lineage fate and enhances bone regeneration by scaffold-mediated local gene delivery. Biomaterials 2021, 264.
  87. Arai, Y.; Choi, B.; Kim, B.J.; Park, S.; Park, H.; Moon, J.J.; Lee, S.H. Cryptic ligand on collagen matrix unveiled by MMP13 accelerates bone tissue regeneration via MMP13/Integrin α3/RUNX2 feedback loop. Acta Biomater 2021, 125, 219–230.
  88. Mao, M.; Hirotugu, M.; Keisuke, M.; Keiichi, K.; Toshiaki, S. Parathyroid Hormone (1–34) Enhances Bone Regeneration in Rats with Cranial Bone Defects. J. Hard. Tissue Biol. 2018, 27, 303–308.
  89. Neer, R.M.; Arnaud, C.D.; Zanchetta, J.R.; Prince, R.; Gaich, G.A.; Reginster, J.Y.; Hodsman, A.B.; Eriksen, E.F.; Ish-Shalom, S.; Genant, H.K.; et al. Effect of parathyroid hormone (1–34) on fractures and bone mineral density in postmenopausal women with osteoporosis. N. Eng. J. Med. 2001, 344, 1434–1441.
  90. Zou, Z.; Wang, L.; Zhou, Z.; Sun, Q.; Liu, D.; Chen, Y.; Hu, H.; Cai, Y.; Lin, S.; Yu, Z.; et al. Simultaneous incorporation of PTH(1–34) and nano-hydroxyapatite into Chitosan/Alginate Hydrogels for efficient bone regeneration. Bioact. Mater. 2021, 6, 1839–1851.
  91. Giannoudis, P.V.; Einhorn, T.A.; Marsh, D. Fracture healing: The diamond concept. Injury 2007, 38, S3–S6.
  92. Lee, K.; Silva, E.A.; Mooney, D.J. Growth factor delivery-based tissue engineering: General approaches and a review of recent developments. J. R. Soc. Interface 2011, 8, 153–170.
  93. Mitchell, A.C.; Briquez, P.S.; Hubbell, J.A.; Cochran, J.R. Engineering growth factors for regenerative medicine applications. Acta Biomater. 2016, 30, 1–12.
  94. Oliveira, É.; Nie, L.; Podstawczyk, D.; Allahbakhsh, A.; Ratnayake, J.; Brasil, D.L.; Shavandi, A. Advances in Growth Factor Delivery for Bone Tissue Engineering. Int. J. Mol. Sci. 2021, 22, 903.
  95. Azevedo, H.S.; Pashkuleva, I. Biomimetic supramolecular designs for the controlled release of growth factors in bone regeneration. Adv. Drug Deliv. Rev. 2015, 94, 63–76.
  96. De Witte, T.M.; Fratila-Apachitei, L.E.; Zadpoor, A.A.; Peppas, N.A. Bone tissue engineering via growth factor delivery: From scaffolds to complex matrices. Regen. Biomater. 2018, 5, 197–211.
  97. Cheng, H.; Jiang, W.; Phillips, F.M.; Haydon, R.C.; Peng, Y.; Zhou, L.; Luu, H.H.; An, N.; Breyer, B.; Vanichakarn, P.; et al. Osteogenic activity of the fourteen types of human bone morphogenetic proteins (BMPs). J. Bone Joint. Surg. Am. 2003, 85, 1544–1552.
  98. Deckers, M.M.; van Bezooijen, R.L.; van der Horst, G.; Hoogendam, J.; van Der Bent, C.; Papapoulos, S.E.; Löwik, C.W. Bone morphogenetic proteins stimulate angiogenesis through osteoblast-derived vascular endothelial growth factor A. Endocrinology 2002, 143, 1545–1553.
  99. Tsuji, K.; Bandyopadhyay, A.; Harfe, B.D.; Cox, K.; Kakar, S.; Gerstenfeld, L.; Einhorn, T.; Tabin, C.J.; Rosen, V. BMP2 activity, although dispensable for bone formation, is required for the initiation of fracture healing. Nat. Genet. 2006, 38, 1424–1429.
  100. Sun, J.; Li, J.; Li, C.; Yu, Y. Role of bone morphogenetic protein-2 in osteogenic differentiation of mesenchymal stem cells. Mol. Med. Rep. 2015, 12, 4230–4237.
  101. Marupanthorn, K.; Tantrawatpan, C.; Kheolamai, P.; Tantikanlayaporn, D.; Manochantr, S. Bone morphogenetic protein-2 enhances the osteogenic differentiation capacity of mesenchymal stromal cells derived from human bone marrow and umbilical cord. Int. J. Mol. Med. 2017, 39, 654–662.
  102. James, A.W.; LaChaud, G.; Shen, J.; Asatrian, G.; Nguyen, V.; Zhang, X.; Ting, K.; Soo, C. A Review of the Clinical Side Effects of Bone Morphogenetic Protein-2. Tissue Eng. Part. B Rev. 2016, 22, 284–297.
  103. Jung, R.E.; Glauser, R.; Schärer, P.; Hämmerle, C.H.; Sailer, H.F.; Weber, F.E. Effect of rhBMP-2 on guided bone regeneration in humans. Clin. Oral. Implants. Res. 2003, 14, 556–568.
  104. Wei, S.; Cai, X.; Huang, J.; Xu, F.; Liu, X.; Wang, Q. Recombinant human BMP-2 for the treatment of open tibial fractures. Orthopedics 2012, 35, e847–e854.
  105. Krishnakumar, G.S.; Roffi, A.; Reale, D.; Kon, E.; Filardo, G. Clinical application of bone morphogenetic proteins for bone healing: A systematic review. Int. Orthop. 2017, 41, 1073–1083.
  106. Tannoury, C.A.; An, H.S. Complications with the use of bone morphogenetic protein 2 (BMP-2) in spine surgery. Spine J. 2014, 14, 552–559.
  107. Zara, J.N.; Siu, R.K.; Zhang, X.; Shen, J.; Ngo, R.; Lee, M.; Li, W.; Chiang, M.; Chung, J.; Kwak, J.; et al. High doses of bone morphogenetic protein 2 induce structurally abnormal bone and inflammation in vivo. Tissue Eng. Part. A 2011, 17, 1389–1399.
  108. Czech, T.; Oyewumi, M.O. Overcoming barriers confronting application of protein therapeutics in bone fracture healing. Drug Deliv. Transl. Res. 2021, 11, 842–865.
  109. El Bialy, I.; Jiskoot, W.; Reza Nejadnik, M. Formulation, Delivery and Stability of Bone Morphogenetic Proteins for Effective Bone Regeneration. Pharm. Res. 2017, 34, 1152–1170.
  110. Agrawal, V.; Sinha, M. A review on carrier systems for bone morphogenetic protein-2. J. Biomed. Mater. Res. B Appl. Biomater. 2017, 105, 904–925.
  111. Sánchez-Duffhues, G.; Hiepen, C.; Knaus, P.; Ten Dijke, P. Bone morphogenetic protein signaling in bone homeostasis. Bone 2015, 80, 43–59.
  112. Shakouri-Motlagh, A.; O’Connor, A.J.; Brennecke, S.P.; Kalionis, B.; Heath, D.E. Native and solubilized decellularized extracellular matrix: A critical assessment of their potential for improving the expansion of mesenchymal stem cells. Acta Biomater. 2017, 55, 1–12.
  113. Larochette, N.; El-Hafci, H.; Potier, E.; Setterblad, N.; Bensidhoum, M.; Petite, H.; Logeart-Avramoglou, D. Osteogenic-differentiated mesenchymal stem cell-secreted extracellular matrix as a bone morphogenetic protein-2 delivery system for ectopic bone formation. Acta Biomater. 2020, 116, 186–200.
  114. Moglia, R.; Whitely, M.; Brooks, M.; Robinson, J.; Pishko, M.; Cosgriff-Hernandez, E. Solvent-free fabrication of polyHIPE microspheres for controlled release of growth factors. Macromol. Rapid. Commun. 2014, 35, 1301–1305.
  115. Whitely, M.; Rodriguez-Rivera, G.; Waldron, C.; Mohiuddin, S.; Cereceres, S.; Sears, N.; Ray, N.; Cosgriff-Hernandez, E. Porous PolyHIPE microspheres for protein delivery from an injectable bone graft. Acta Biomater. 2019, 93, 169–179.
  116. Andreas, K.; Sittinger, M.; Ringe, J. Toward in situ tissue engineering: Chemokine-guided stem cell recruitment. Trends Biotechnol. 2014, 32, 483–492.
  117. Hunziker, E.B.; Enggist, L.; Küffer, A.; Buser, D.; Liu, Y. Osseointegration: The slow delivery of BMP-2 enhances osteoinductivity. Bone 2012, 51, 98–106.
  118. Lin, D.; Chai, Y.; Ma, Y.; Duan, B.; Yuan, Y.; Liu, C. Rapid initiation of guided bone regeneration driven by spatiotemporal delivery of IL-8 and BMP-2 from hierarchical MBG-based scaffold. Biomaterials 2019, 196, 122–137.
  119. Niu, H.; Ma, Y.; Wu, G.; Duan, B.; Wang, Y.; Yuan, Y.; Liu, C. Multicellularity-interweaved bone regeneration of BMP-2-loaded scaffold with orchestrated kinetics of resorption and osteogenesis. Biomaterials 2019, 216, 119216.
  120. Wang, Y.; Yuan, X.; Yu, K.; Meng, H.; Zheng, Y.; Peng, J.; Lu, S.; Liu, X.; Xie, Y.; Qiao, K. Fabrication of nanofibrous microcarriers mimicking extracellular matrix for functional microtissue formation and cartilage regeneration. Biomaterials 2018, 171, 118–132.
  121. Zheng, Y.; Wang, L.; Zhang, X.; Gu, Z.; Wu, G. BMP2/7 heterodimer can modulate all cellular events of the in vitro RANKL-mediated osteoclastogenesis, respectively, in different dose patterns. Tissue Eng. Part. A 2012, 18, 621–630.
  122. Kim, R.Y.; Oh, J.H.; Lee, B.S.; Seo, Y.K.; Hwang, S.J.; Kim, I.S. The effect of dose on rhBMP-2 signaling, delivered via collagen sponge, on osteoclast activation and in vivo bone resorption. Biomaterials 2014, 35, 1869–1881.
  123. Chen, Y.; Zheng, Z.; Zhou, R.; Zhang, H.; Chen, C.; Xiong, Z.; Liu, K.; Wang, X. Developing a Strontium-Releasing Graphene Oxide-/Collagen-Based Organic-Inorganic Nanobiocomposite for Large Bone Defect Regeneration via MAPK Signaling Pathway. ACS Appl Mater. Interfaces 2019, 11, 15986–15997.
  124. Choe, G.; Oh, S.; Seok, J.M.; Park, S.A.; Lee, J.Y. Graphene oxide/alginate composites as novel bioinks for three-dimensional mesenchymal stem cell printing and bone regeneration applications. Nanoscale 2019, 11, 23275–23285.
  125. Zeng, Y.; Zhou, M.; Chen, L.; Fang, H.; Liu, S.; Zhou, C.; Sun, J.; Wang, Z. Alendronate loaded graphene oxide functionalized collagen sponge for the dual effects of osteogenesis and anti-osteoclastogenesis in osteoporotic rats. Bioact. Mater. 2020, 5, 859–870.
  126. Andrée, L.; Barata, D.; Sutthavas, P.; Habibovic, P.; van Rijt, S. Guiding mesenchymal stem cell differentiation using mesoporous silica nanoparticle-based films. Acta Biomater. 2019, 96, 557–567.
  127. Baht, G.S.; Vi, L.; Alman, B.A. The Role of the Immune Cells in Fracture Healing. Curr. Osteoporos. Rep. 2018, 16, 138–145.
  128. Xiang, G.; Huang, X.; Wang, T.; Wang, J.; Zhao, G.; Wang, H.; Feng, Y.; Lei, W.; Hu, X. The impact of sitagliptin on macrophage polarity and angiogenesis in the osteointegration of titanium implants in type 2 diabetes. Biomed. Pharmacother. 2020, 126.
  129. Zhang, J.; Shi, H.; Zhang, N.; Hu, L.; Jing, W.; Pan, J. Interleukin-4-loaded hydrogel scaffold regulates macrophages polarization to promote bone mesenchymal stem cells osteogenic differentiation via TGF-β1/Smad pathway for repair of bone defect. Cell Prolif. 2020, 53.
  130. Castaño, I.M.; Raftery, R.M.; Chen, G.; Cavanagh, B.; Quinn, B.; Duffy, G.P.; O’Brien, F.J.; Curtin, C.M. Rapid bone repair with the recruitment of CD206. Acta Biomater. 2020, 109, 267–279.
  131. Zhu, Y.; Liang, H.; Liu, X.; Wu, J.; Yang, C.; Wong, T.M.; Kwan, K.Y.H.; Cheung, K.M.C.; Wu, S.; Yeung, K.W.K. Regulation of macrophage polarization through surface topography design to facilitate implant-to-bone osteointegration. Sci. Adv. 2021, 7.
  132. Zheng, Z.W.; Chen, Y.H.; Wu, D.Y.; Wang, J.B.; Lv, M.M.; Wang, X.S.; Sun, J.; Zhang, Z.Y. Development of an Accurate and Proactive Immunomodulatory Strategy to Improve Bone Substitute Material-Mediated Osteogenesis and Angiogenesis. Theranostics 2018, 8, 5482–5500.
  133. Gong, L.; Li, J.; Zhang, J.; Pan, Z.; Liu, Y.; Zhou, F.; Hong, Y.; Hu, Y.; Gu, Y.; Ouyang, H.; et al. An interleukin-4-loaded bi-layer 3D printed scaffold promotes osteochondral regeneration. Acta Biomater. 2020, 117, 246–260.
  134. Lian, J.B.; Stein, G.S.; van Wijnen, A.J.; Stein, J.L.; Hassan, M.Q.; Gaur, T.; Zhang, Y. MicroRNA control of bone formation and homeostasis. Nat. Rev. Endocrinol. 2012, 8, 212–227.
  135. Seeliger, C.; Karpinski, K.; Haug, A.T.; Vester, H.; Schmitt, A.; Bauer, J.S.; van Griensven, M. Five freely circulating miRNAs and bone tissue miRNAs are associated with osteoporotic fractures. J. Bone Miner. Res. 2014, 29, 1718–1728.
  136. Lin, J.; Mohamed, I.; Lin, P.H.; Shirahama, H.; Milbreta, U.; Sieow, J.L.; Peng, Y.; Bugiani, M.; Wong, S.C.; Levinson, H.; et al. Modulating Macrophage Phenotype by Sustained MicroRNA Delivery Improves Host-Implant Integration. Adv. Healthc. Mater. 2020, 9.
  137. Mencía Castaño, I.; Curtin, C.M.; Duffy, G.P.; O’Brien, F.J. Next generation bone tissue engineering: Non-viral miR-133a inhibition using collagen-nanohydroxyapatite scaffolds rapidly enhances osteogenesis. Sci. Rep. 2016, 6.
  138. Garg, K.; Pullen, N.A.; Oskeritzian, C.A.; Ryan, J.J.; Bowlin, G.L. Macrophage functional polarization (M1/M2) in response to varying fiber and pore dimensions of electrospun scaffolds. Biomaterials 2013, 34, 4439–4451.
  139. Mahon, O.R.; Browe, D.C.; Gonzalez-Fernandez, T.; Pitacco, P.; Whelan, I.T.; Von Euw, S.; Hobbs, C.; Nicolosi, V.; Cunningham, K.T.; Mills, K.H.G.; et al. Nano-particle mediated M2 macrophage polarization enhances bone formation and MSC osteogenesis in an IL-10 dependent manner. Biomaterials 2020, 239.
  140. Chen, Z.; Bachhuka, A.; Han, S.; Wei, F.; Lu, S.; Visalakshan, R.M.; Vasilev, K.; Xiao, Y. Tuning Chemistry and Topography of Nanoengineered Surfaces to Manipulate Immune Response for Bone Regeneration Applications. ACS Nano 2017, 11, 4494–4506.
More
© Text is available under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/)