1. Structural Support to Improve Structure Sustainability
In semiconductor photocatalysis, different carbon compounds such as CNTs, CDs, graphene, GO, and activated carbon (AC) serve as structural support [
62,
63,
64,
65,
66]. Carbon nanomaterials offer a larger surface site for the dissemination and immobilization of nanoparticles (NPs). These inert and thermally stable CNMs maintain their structure and properties when coupled with NPs. Numerous defect and active sites (oxygen-based functional groups) present in carbon materials can be exploited to initiate the development and anchoring of homogenous nanoparticles. The carbon materials’ light weight is essential for their use as structural support. It is now also possible to produce activated carbon, carbon fibers, CNTs, and graphene on a considerable scale and inexpensively due to the copious amount of carbon in the earth’s crust. The presence of these carbon components can change nucleation and growth rates, slowing down semiconductor nanoparticle aggregation and strengthening their architectures [
67,
68,
69]. This section discusses how carbon-based materials stabilize nanostructures. Thus, structural stability applies to component geometries and morphologies. Extremely small nanoparticles, clusters, or other nanostructures that are dispersed and stabilized can substantially increase structural strength. As a result, semiconductor nanoparticles possess a large surface area, numerous surface defects, and a superior contact interface with carbon materials for increased charge transfer. Therefore, carbon-based hybrid semiconductor photocatalysts are more effective at producing H
2 than pure semiconductor photocatalysts. The surface chemistry of carbon materials is greatly impacted by interactions between semiconductor nanoparticles and carbon material. Wang et al. [
64] proposed that hydroxyl, carboxyl, carbonyl, and epoxy groups increased the hydrophilic property of the CNTs surface by first treating them with HCl and HNO
3. The Zn
xCd
1−xS nanoparticles were then supported by the functionalized CNTs using a solvothermal technique with the help of the raw ingredients including zinc acetate, cadmium chloride, and thiourea. The well-organized Zn
0.83Cd
0.17S nanoparticles on the CNTs surface have a diameter of about 100 nm. If CNTs were not there, these nanoparticles would stick together. The excellent dispersion improves the interfacial surface of the Zn
0.83Cd
0.17S/CNT photocatalyst. Since the conduction band of the photocatalytic material is more populated than the Fermi level of CNTs, photoexcited electrons will move to the surface of the nanotubes. Thus, the aforesaid phenomenon can efficiently separate photoinduced charge carriers at the photocatalyst’s interface. In addition, CNT-incorporated Zn
0.83Cd
0.17S nanocomposite has a lower band gap value than pure Zn
0.83Cd
0.17S. Under 300 to 800 nm illumination, Zn
0.83Cd
0.17S/CNT nanocomposite generates 6.03 mmol·h
−1g
−1 of H
2, which is 1.5 times more than the pristine Zn
0.83Cd
0.17S.
Li et al. [
70] prepared CdS-coupled graphene nanosheets via a hydrothermal approach using GO as supporting material, Cadmium acetate for Cd
2+ precursor, and DMSO as the solvent as well as source of S
2−. Solvothermal heating turned GO into graphene with CdS clusters on its surface. The interactions between nanoparticles and graphene can be strengthened by physical adsorption, the electrostatic force of attractions, and charge transference. The homogenous CdS cluster distribution on graphene, the CdS/graphene photocatalyst, has a greater specific surface area. Uniform CdS cluster distribution is attributed to the more effective transport of photoexcited charges to graphene. At 1.0 wt% graphene, 1.12 mmol·h
−1 of hydrogen is generated, which is 4.87 times than the neat CdS. Shen et al. [
71] also used rGO additive to stabilize the very thin nanorods of Zn
0.5Cd
0.5S with a corresponding upsurge in photocatalytic H
2 evolution.
2. Cocatalyst
Cocatalysts in a photocatalytic system enhance H
2 evaluation efficacy. Metals such as Pt, Au, or Pd have a more significant work function than semiconductors, making them excellent cocatalysts. Cocatalysts improve charge separation, provide catalytic sites, reduce over-potential, and minimize H
2 activation energy [
72,
73]. Noble metals are expensive and rare. Thus, economical cocatalysts are needed for economic photocatalytic systems. Carbon compounds are effective cocatalysts for photocatalytic H
2 evaluation [
74,
75]. The Fermi level of carbonaceous compounds is lesser than CB but RP is greater than H
+/H
2. Carbon compounds have advantages similar to noble metal cocatalysts, with increased active sites and a localized photothermal effect owing to increased surface area and extended light absorption intensity [
76,
77]. Khan et al. [
74] fabricated a CNTs/CdS/TiO
2/Pt photocatalyst via the hydrothermal method. Pt was designed onto TiO
2 via photodeposition whilst CdS via hydrolysis. This photocatalyst generates H
2 at a greater rate under visible radiations, using sodium sulfide and sulfate sacrificial agents. In the first step, the electrons and holes are separated between the TiO
2 and CdS interface. The photoelectron moves from the TiO
2 to the CNT surface and then Pt catalyst. The Pt nanoparticles work as cocatalysts due to their lower Fermi level of CNTs as compared to TiO
2. Both Pt and CNTs are promising photocatalysts and can improve the photo-catalytic H
2 evaluation of CdS/TiO
2. Preferably, using 0.4 and 4 wt.% of Pt and CNTs, respectively, enhances the photocatalytic performance by 50%. A graphene/MoS
2/TiO
2(GMST) photocomposite was prepared hydrothermally using Na
2MoO
4, H
2NCSNH
2, and graphene oxide precursors at 210 °C and utilized as an efficient material for photocatalytic H
2 production [
78]. It was exposed by using ethanol as a sacrificial agent and TiO
2 as the photocatalyst while graphene and MoS
2 functioned as cocatalysts. The GMST photocatalyst exhibited a high rate (~165.3 mol·h
−1) of H
2generation at 5.0 and 0.5 wt.% of graphene and MoS
2, respectively, having 9.7% quantum efficiency (QE) at 365 nm [
78]. A hybrid rGO/Zn
xCd
1−xS photocatalyst prepared first via coprecipitation and then a hydrothermal reduction approach elevates the cocatalytic performance for H
2 production [
79]. A high rate of H
2 evaluation (~1824 mol·h
−1g
−1) was observed for this optimized photocatalyst using 0.25 wt.% of rGO, which has 23.4% apparent QE at 420 nm under solar irradiation. Liu et al. integrated NH
3-treated CDs into g-C
3N
4 by heating CDs and urea for 3 h at 550 °C, where the carbon dots were first synthesized electrochemically and then hydrothermally treated with ammonia. This g-C
3N
4/CDs hybrid photocatalyst was found to be efficient in WS under solar light for the evolution of H
2 and O
2. A maximum QE of 16% was achieved using a g-C
3N
4/CD catalyst at 420 ± 20 nm. Actually, the photocatalytic action of g-C
3N
4 at the first stage caused water to be split into H
2O
2 and H
2, then, at the subsequent stage, the carbon dot-catalyzed breakdown of H
2O
2 into H
2O and O
2.
3. Photosensitization
Carbon compounds with semiconducting or dye-like characteristics can function as a photosensitizer in some cases, enhancing the photoresponse of a broad bandgap of the semiconductor photocatalyst by inducing additional photogenerated electrons [
80,
81,
82]. The emission of photoelectrons from the material can overlap with semiconductor absorption and are responsible for the transfer of the resonance energy from the carbon material to the coupled semiconductor. As the result, the LUMO of the carbon material becomes more negative in comparison to the coupled semiconductor’s CB. Wang et al. [
83] prepared a graphene/ZnS (G-ZS) photocatalyst via the hydrothermal method for photocatalytic H
2 evolution under visible light. A graphene-supported ZnS photocatalyst evaluated 7.42 mol·h
−1g
−1 hydrogen at 0.1 wt.% graphene, which was found to be 8 times that of the pristine ZnS. Since visible light cannot excite ZnS, the photoelectron most likely originates from graphene and migrates to the CB of ZnS [
80]. The rGO/Pt/TiO
2 photocatalyst is an excellent photosensitizer and evaluates H
2 at a rate of 11.24 mmol·h
−1g
−1. Carbon dots are excellent candidates for use as photosensitizers in photocatalytic reactions due to their high photo-absorption and photoluminescence properties. For instance, Martindale et al. [
84] fabricated a carbon dot (photosensitizer)-based Ni-bis- (diphosphine) (NiP) photocatalyst for H
2 generation under visible light. To produce this photocatalyst, 30 nmol of NiP and 2.2 nmol of CD are used in 0.1M EDTA solution with pH 6; a photocatalyst g-CQDs/NiP produces H
2 at 398 mol·h
−1g
−1. The apparent QE at 360 ± 10 nm was observed ∼1.4%. Carbon dots can convert near-infrared photons for semiconductor photocatalysis due to their photoluminescence up-conversion property [
82,
85]. Hydrogenated TiO
2(H-TiO
2)-based photocatalysts were prepared with carbon quantum dots (CQDs) under bath reflux. This photocatalyst is UV-visible-NIR compatible and showed remarkable photocatalytic H
2 production capability under the illumination of a 300 W Xe arc lamp. For this photocatalytic system, Pt was used as the cocatalyst and methanol as the sacrificial agent across a wide spectral range. The higher H
2 generation rate of 7.42 mmol·h
−1g
−1 was observed in comparison to H-TiO
2 nanobelts (6.01 mmol·h
−1g
−1) [
85].
4. Photocatalyst
Carbon-based nanomaterials are effective photocatalysts for H
2generation, according to theory and experiment [
86,
87,
88], owing to the semiconducting properties of CDs, CNTs, graphene, GO, rGO, and C
60. Such a nanocarbon of the semiconductor sort can have a greater number of negatively charged LUMO sites than H
+/H
2 RP. Reduced graphene oxide rGO is a commonly used photocatalyst [
89,
90], as its CB minimum consists of anti-bonding π* orbital; at pH = 0, it has a potential of −0.52 eV [
40]. Density functional theory (DFT) studies explain the electronic structure of graphene oxide by alternating the relative ratio of -OH and epoxy groups present on the surface. The resulting electronic structure shows the photocatalytic hydrogen, and oxygen evaluation reaction occurs [
91]. Teng’s group reported that GO synthesized by a modified Hummers’ method had an apparent direct E
g value of 3.3–4.3 eV and an indirect E
g of 2.4–3.0 eV. Graphene oxide (GO) is comprised of graphene molecules of different oxidation stats and can produce H
2 under UV/Visible illuminations. In a 20% methanol aqueous solution with 0.5g GO and no cocatalyst, mercury lamp irradiation yielded 17,000 mmol·h
−1 H
2 [
88]. Meng et al. [
90] prepared a p-MoS
2/n-rGO photocatalyst with p-type MoS
2 deposited on the surface of n-type rGO. Under solar irradiation and ethanol as sacrificial agents, this photocatalyst exhibited higher H
2 evaluation activity than bare MoS
2 and MoS
2/rGO. This is because, as shown by the photoelectrochemical experiment, the p-MoS
2/n-rGO junctions are very good at separating charges. Zhu’s team compared H
2 production activity for neat CDs and CD-based composite materials [
87,
92,
93]. An H
2 evaluation at a 423.7 mol·h
−1g
−1 was achieved using carbon dots in pure water without needing a cocatalyst. Carbon dots were created hydrothermally from MWCNTs oxide [
87]. In methanol sacrificial agent and Pt cocatalyst, a hybrid carbon nanodot/WO
3 photocatalyst produces H
2 at 1330 mol·h
−1g
−1 under xenon lamp irradiation [
92].
5. Band Gap Narrowing Effect
Chemical bonds can form when semiconductor photocatalysts and carbon compounds make strong contacts (e.g., metal O C bonds). Chemical bonding reduces photocatalyst band gaps, increasing H
2 production [
94,
95]. Ye et al. [
96] reported the hydrothermal fabrication of graphene/CdS (0.01:1) and CNTs/CdS (0.05:1) hybrid materials with the photocatalytic H
2 evaluation of and 52 mol·h
−1, respectively. The addition of graphene or CNTs into CdS resulted in the narrowing of the E
g values of these hybrid photocatalysts and consequently led to superior photocatalytic H
2 generation as compared to pristine CdS. This was in addition to the benefit of more effective charge separation. Bi
2WO
6 is often not used for water-splitting H
2 generation, due to its smaller RP and comparatively less negative CB. However, coupling Bi
2WO
6 nanosheets with graphene
, the CB of Bi
2WO
6 becomes more negative, and the feasibility of photocatalytic H
2 evaluation increases [
97]. In a typical experiment [
98], Bi
2WO
6 nanoparticles were produced via sonication onto the graphene’s sheets using GO, HNO
3, (NH
4)
10W
12O
41, and Bi(NO
3)
3·5H
2O, followed by calcination at 450°C for 3h in an inert environment. Raman and XPS research validated the chemistry between Bi
2WO
6 and graphene. After coupling with graphene, Mott–Schottky calculations showed that the RP of CB of Bi
2WO
6 increased from +0.09 V to −0.30 V as compared to the standard hydrogen electrode. As a result, 0.03 g of Bi
2WO
6/graphene photocatalyst was used to produce 159.2 mol·h
−1 of H
2at 420 nm in an aqueous solution of methanol.
In conclusion, in several aspects, carbon materials can significantly enhance the H2 reaction rate compared to semiconductor photocatalysts. The inclusion of various carbonaceous materials coupled with semiconductor photocatalysts can result in a variety of proficient effects including structural support for improved structure constancy, electron collection, the reduction of the recombination rate of photo-stimulated charge pairs, photocatalyst, Eg narrowing outcome cocatalyst, and photosensitization. It is essential to remember that certain carbon materials can potentially play many functions throughout the entire photocatalytic process. Moreover, due to some limitations imposed by its structure and properties, a particular type of carbon material might not be able to fulfill all the functions. The potential characteristics of various CNMs are summarized in Table 1.
Table 1. Role of carbon nanomaterials in photocatalysis.
Function Type |
Carbon Nanotubes |
Graphene |
Fullerenes |
Graphene Oxide |
Graphitic Carbon Nitride |
Carbon Quantum Dots |
Supporting material |
✔ |
✔ |
× |
✔ |
✔ |
✔ |
Photocatalyst |
✔ |
✔ |
✔ |
✔ |
× |
✔ |
Cocatalyst |
✔ |
✔ |
✔ |
✔ |
✔ |
✔ |
Photosensitizer |
× |
✔ |
✔ |
✔ |
✔ |
✔ |
Bandgap narrowing effect |
✔ |
✔ |
× |
✔ |
✔ |
✔ |
This entry is adapted from the peer-reviewed paper 10.3390/catal13010066