6061 (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. It has good mechanical properties, exhibits good weldability, and is very commonly extruded (second in popularity only to 6063). It is one of the most common alloys of aluminum for general-purpose use. It is commonly available in pre-tempered grades such as 6061-O (annealed), tempered grades such as 6061-T6 (solutionized and artificially aged) and 6061-T651 (solutionized, stress-relieved stretched and artificially aged).

  • weldability
  • a96061
  • silicon

1. Chemical Composition

6061 Aluminum Alloy Composition by Mass %[1]
Al Mg Si Fe Cu Cr Zn Ti Mn Remainder
95.85 - 98.56 0.8 - 1.2 0.40 - 0.8 0.0 - 0.7 0.15 - 0.40 0.04 - 0.35 0.0 - 0.25 0.0 - 0.15 0.0 - 0.15 0.05 each, 0.15 total

2. Properties

The mechanical properties of 6061 depend greatly on the temper, or heat treatment, of the material.[2] Young's Modulus is 69 GPa (10,000 ksi) regardless of temper.[3]

2.1. 6061-O

Annealed 6061 (6061-O temper) has maximum ultimate tensile strength no more than 150 MPa (22 ksi),[4][5] and maximum yield strength no more than 83 MPa (12 ksi)[4] or 110 MPa (16 ksi).[5] The material has elongation (stretch before ultimate failure) of 10–18%. To obtain the annealed condition, the alloy is typically heated at 415 °C for 2-3 hours.[6]

2.2. 6061-T4

T4 temper 6061 has an ultimate tensile strength of at least 180 MPa (26 ksi)[5] or 210 MPa (30 ksi)[4] and yield strength of at least 110 MPa (16 ksi). It has elongation of 10-16%.

2.3. 6061-T6

 
6061-T6 Aluminum Standard Heat Treating Process. https://handwiki.org/wiki/index.php?curid=2068390

T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminum alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively.[7] This can exceed the yield strength of certain types of stainless steel.[8] In thicknesses of 6.35 mm (0.250 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties. The typical value for thermal conductivity for 6061-T6 at 25 °C (77 °F) is around 152 W/m K. A material data sheet [9] defines the fatigue limit under cyclic load as 97 MPa (14 ksi) for 500,000,000 completely reversed cycles using a standard RR Moore test machine and specimen. Note that aluminum does not exhibit a well defined "knee" on its S-n graph, so there is some debate as to how many cycles equates to "infinite life". Also note the actual value of fatigue limit for an application can be dramatically affected by the conventional de-rating factors of loading, gradient, and surface finish.

3. Microstructure

Different aluminum heat treatments control the size and dispersion of Mg2Si precipitates in the material. Grain boundary sizes also change, but do not have as important of an impact on strength as the precipitates. Grain sizes can change orders of magnitude based upon stress and can have grains as small as a few hundred nanometers, but are typically a few micrometers to hundreds of micrometers in diameter. Iron, manganese, and chromium secondary phases (Fe2Si2Al9, (Fe, Mn, Cr)3SiAl12) often form as inclusions in the material.[10]

Grain boundaries in extruded plate 6061 aluminum alloy. https://handwiki.org/wiki/index.php?curid=1774629

Grain sizes in aluminum alloys are heavily dependent upon the processing techniques and heat treatment. Different cross-sections of material which has been stressed can cause order of magnitude differences in grain size.[11] Some specially processed aluminum alloys have grain diameters which are hundreds of nanometers,[12] but most range from a few micrometers to hundreds of micrometers.[13]

4. Uses

6061 is commonly used for the following:

  • construction of aircraft structures, such as wings and fuselages, more commonly in homebuilt aircraft than commercial or military aircraft.[14] 2024 alloy is somewhat stronger, but 6061 is more easily worked and remains resistant to corrosion even when the surface is abraded, which is not the case for 2024, which is usually used with a thin Alclad coating for corrosion resistance.[15]
  • yacht construction, including small utility boats.[16]
  • automotive parts, such as the chassis of the Audi A8 and the Plymouth Prowler.
  • flashlights
  • aluminum cans for the packaging of food and beverages.
  • Scuba tanks and other high pressure gas storage cylinders (post 1995)

6061-T6 is used for:

  • bicycle frames and components.
  • many fly fishing reels.
  • the Pioneer plaque
  • the secondary chambers and baffle systems in firearm sound suppressors (primarily pistol suppressors for reduced weight and improved mechanical functionality), while the primary expansion chambers usually require 17-4PH or 303 stainless steel or titanium.[17][18]
  • The upper and lower receivers of many non mil-spec AR-15 rifle variants.
  • Many aluminum docks and gangways, welded into place.
  • Material used in some ultra-high vacuum (UHV) chambers
  • Many parts for remote controlled model aircraft, notably helicopter rotor components.
  • Large amateur radio antennas.
  • Fire department rescue ladders

4.1. Welding

6061 is highly weldable, for example using tungsten inert gas welding (TIG) or metal inert gas welding (MIG). Typically, after welding, the properties near the weld are those of 6061-T4, a loss of strength of around 40%. The material can be re-heat-treated to restore near -T6 temper for the whole piece. After welding, the material can naturally age and restore some of its strength as well. Most strength is recovered in the first few days to a few weeks. Nevertheless, the Aluminum Design Manual (Aluminum Association) recommends the design strength of the material adjacent to the weld to be taken as 165 MPa/24000 PSI without proper heat treatment after the welding. Typical filler material is 4043 or 5356.

4.2. Extrusions

6061 is an alloy used in the production of extrusions—long constant–cross-section structural shapes produced by pushing metal through a shaped die.

4.3. Forgings

6061 is an alloy that is suitable for hot forging. The billet is heated through an induction furnace and forged using a closed die process. This particular alloy is suitable for open die forgings. Automotive parts, ATV parts, and industrial parts are just some of the uses as a forging. Aluminum 6061 can be forged into flat or round bars, rings, blocks, discs and blanks, hollows, and spindles. 6061 can be forged into special and custom shapes.[19]

4.4. Castings

6061 is not an alloy that is traditionally cast due to its low silicon content affecting the fluidity in casting. It can be suitably cast using a specialized centrifugal casting method. Centrifugally cast 6061 is ideal for larger rings and sleeve applications that exceed limitations of most wrought offerings. [20]

5. Equivalent Materials

6061 Aluminum Equivalent Table[21]

US European Union ISO Japan China
Standard Grade (UNS) SAE AMS Standard Grade Standard Numerical (Chemical Symbols) Standard Grade Standard Grade Standard Grade
AA;

ASTM B209;

ASTM B211;

ASTM B221;

ASTM B210;

ASTM B308/B308M;

ASTM B241/B241M

6061 (UNS A96061) SAE AMS 4025;

SAE AMS 4026;

SAE AMS 4027;

SAE AMS 4117

6061 EN 573-3 EN AW-6061

(EN AW-AlMg1SiCu)

ISO 209 AW-6061 JIS H4000;

JIS H4040

6061 GB/T 3880.2

GB/T 3190

6061

6. Standards

Different forms and tempers of 6061 aluminum alloy are discussed in the following standards:[22]

  • ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
  • ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes
  • ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
  • ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes
  • ASTM B308/308M: Standard Specification for Aluminum-Alloy 6061-T6 Standard Structural Profiles
  • ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
  • ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
  • ISO 6361: Wrought Aluminum and Aluminum Alloy Sheets, Strips and Plates

The content is sourced from: https://handwiki.org/wiki/Chemistry:6061_aluminium_alloy

References

  1. B07 Committee (in en). Specification for Aluminum and Aluminum-Alloy Sheet and Plate (Metric). doi:10.1520/b0209m-14. http://www.astm.org/cgi-bin/resolver.cgi?B209M-14. 
  2. Alcoa 6061 data sheet (pdf), accessed October 13, 2006 http://www.alcoa.com/adip/catalog/pdf/Extruded_Alloy_6061.pdf
  3. Aluminum Standards and Data 2006 Metric SI, by the Aluminum Association Inc.
  4. ASTM B209
  5. ASTM B221
  6. ASM Handbook Committee (1991). "Heat Treating of Aluminum Alloys". Volume 4: Heat Treating. ASM. pp. 871. doi:10.1361/asmhba0001205.  https://dx.doi.org/10.1361%2Fasmhba0001205
  7. Material Properties Data: 6061-T6 Aluminum http://www.makeitfrom.com/material-properties/6061-T6-Aluminum/
  8. "Archived copy". http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=MQ304A. 
  9. "ASM Material Data Sheet". http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=MA6061T6. 
  10. Hatch, John (1984). "Microstructure of Alloys". Aluminum: Properties and Physical Metallurgy. ASM International. pp. 54–104. ISBN 9780871701763. 
  11. Nakai, Manabu; Itoh, Goroh (2014). "The Effect of Microstructure on Mechanical Properties of Forged 6061 Aluminum Alloy". Materials Transactions 55 (1): 114–119. doi:10.2320/matertrans.ma201324. ISSN 1345-9678.  https://dx.doi.org/10.2320%2Fmatertrans.ma201324
  12. Lee, S. H; Saito, Y; Sakai, T; Utsunomiya, H (2002-02-28). "Microstructures and mechanical properties of 6061 aluminum alloy processed by accumulative roll-bonding". Materials Science and Engineering: A 325 (1): 228–235. doi:10.1016/S0921-5093(01)01416-2. ISSN 0921-5093.  https://dx.doi.org/10.1016%2FS0921-5093%2801%2901416-2
  13. Easton, M.A.; StJohn, D.H. (2008). "Improved prediction of the grain size of aluminum alloys that includes the effect of cooling rate" (in en). Materials Science and Engineering: A 486 (1–2): 8–13. doi:10.1016/j.msea.2007.11.009.  https://dx.doi.org/10.1016%2Fj.msea.2007.11.009
  14. Aluminum Information at aircraftspruce.com, accessed October 13, 2006 https://www.aircraftspruce.com/catalog/mepages/aluminfo.php
  15. 6061 vs 2024 . Homebuiltairplanes.com. Retrieved on 2012-04-04. http://www.homebuiltairplanes.com/forums/aircraft-design-aerodynamics-new-technology/5003-6061-vs-2024-a.html
  16. Boatbuilding with Aluminum, Stephen F. Pollard, 1993, ISBN:0-07-050426-1
  17. EVOLUTION 9mm, 1/2-28 TPI . Advanced Armament. Retrieved on 2012-04-04. http://www.advanced-armament.com/product.aspx?pid=199
  18. Amphibian S .22LR : Suppressor : AWC Systems Technology. Awcsystech.com. Retrieved on 2012-04-04. http://www.awcsystech.com/products/suppressors/amphibian-s/
  19. "6061 Aluminum Alloy Forging | Anderson Shumaker". http://www.andersonshumaker.com/materials/aluminum/6061-aluminum.html. 
  20. "Aluminum Alloys | Johnson Centrifugal". 27 August 2019. http://johnsoncentrifugal.com/aluminum-alloys/. 
  21. Cole, Andrew (2020-05-24). "AL 6061-T6 Aluminium Alloy Properties, Tensile & Yield Strength, Thermal Conductivity, Modulus of Elasticity, Equivalent Material". https://www.theworldmaterial.com/al-6061-t6-aluminum-alloy/. 
  22. 6061 (3.3214, H20, A96061) Aluminum. Retrieved on 2014-11-14. http://www.makeitfrom.com/material-properties/6061-3.3214-H20-A96061-Aluminum/
More
This entry is offline, you can click here to edit this entry!
Video Production Service