Illustration of the antibacterial mechanisms of GO, which consist of (1) penetration and disruption of the bacterial cell membrane, (2) leakage of the intracellular content following penetration and disruption of the cell membrane, (3) oxidative stress by the generation of reactive oxygen species (ROS0 and depletion of the antioxidant in the bacteria) and (4) bacteria entrapping (wrapping effect) by GO.
A study has demonstrated the antibacterial activity of GO nanowalls against
S. aureus and
E. coli, which was attributed to the direct contact of the very sharp edges (nano-knives) on the nanowalls and the bacteria. In this
res
tudyearch, SEM showed that the nanowalls that were almost perpendicular to the substrate that it was deposited on provided extremely sharp edges, allowing efficient interaction with the bacteria. The leakage of intracellular components also confirmed the cell membrane damage by the sharp edges of the GO nanowalls, which was more effective on
S. aureus than
E. coli. It was mentioned to be due to the lack of an outer membrane on
S. aureus [25]. Interestingly, another study also showed that controlled vertically aligned GO nanosheets penetrated and disrupted the membrane of
E. coli. In this
res
tudyearch, GO nanoflakes suspension was used
[29]. Thus, it is suggested that it could be due to the availability of more sharp edges in the suspension than that of being coated as GO is more freely mobile. This was supported by two other studies, which demonstrated that GO vertically oriented to the cell membrane is more ready for penetration due to it being able to overcome the energy barrier
[30,31][30][31]. Moreover, studies with simulations have also reported that the GO nanosheets would enter a fluctuation or swinging mode so that they will find a diving force to overcome the energy barrier before piercing through the cell membrane
[32,33][32][33]. In addition, another study also mentioned that vertical GO from approximately 3.5–4.7 nm of the bacteria membrane surface would always spontaneously penetrate through the cell membrane. Furthermore, after penetrating into the membrane, simulation experiments described the mechanism of GO disrupting the membrane by phospholipid extraction. This was said to be due to the hydrophobic interactions of the phospholipids and the hydrophobic “sp
2” regions on the GO. It was also claimed that a larger GO (500 nm) demonstrated stronger antibacterial effects due to stronger cutting effects. Moreover, a larger GO also gives a larger hydrophobic region, which enhances the phospholipid extraction activity
[33]. Another study also mentioned the importance of “sp
2” regions in interactions with the phospholipid membrane
[24]. Interestingly, SEM images from one study showed that a smaller GO (1295 nm) exhibits enhanced cutting effects on
S. mutans. This is suggested to be attributed to a smaller area with more sharp edges exposed
[16]. Nevertheless, 500 nm
[33] is smaller than 1295 nm
[16]. Another study also reported that smaller GO nanosheets enable the blade effect of sharp edges as its predominant antibacterial mechanism
[34]. As mentioned above, these claims are due to researchers synthesising GO in different range of sizes. A study demonstrated that the presence of electrolytes in the GO suspension would prevent the activity of sharp edges due to reacting with the ions, forming aggregates
[35]. It was said that the aggregation of GO increases the surfaces energy, thereby preventing the cutting action of the sharp edges. This
res
tudyearch also demonstrated that the optimum concentration for the action of sharp edges is below 6 µg/mL when GO is suspended in any solution. However, as the concentration increases, antibacterial activity is only observed in GO dispersed in water. This was further confirmed by the observation of cellular debris and change in the morphology of bacteria on the AFM
[34]. In addition to this, quantum mechanics calculations also indicated that further oxidation on the previous oxidised sites could significantly decrease the energy barrier
[33]. In addition, another simulation study also reported that the degree of oxidation of GO affects its position within the phospholipid bilayer
[31]. One other study mentioned than larger GO nanosheets with a higher degree of oxidation could cause larger and more irregular membrane perturbation
[32]. In addition, another study also suggested that electron transfer from the membrane of
E. coli to the oxygen functional groups of GO coated on metals leads to a loss of membrane integrity
[36]. Moreover, another study also reported the availability of peaks or sharp edges promotes a charge transfer, thereby leading to destruction of the cell membrane. This was made evident by the increase in uptake of PI, a membrane impermeable dye, by the bacteria
[18]. Therefore, it is important to consider these factors in the design and synthesis of GO.
3.2. Bacteria Entrapping (Wrapping) Effect
A recent study has reported that larger-sized GO have a stronger entrapping ability
[16]. In this
res
tudyearch, SEM revealed GO with larger sizes ranging from 2015 to 4544 nm exhibited an entrapping effect on
S. mutans. Furthermore, an SEM observation in a previous study has shown the entrapping effect of GO (0.31 ± 0.2 µm) on
E. coli [41][37]. In addition to this, it was also reported in another study that larger-sized GO (0.65 µm
2) possessed a stronger entrapping effect on
E. coli. However, this effect was only bacteriostatic
[38]. These findings were also observed in previous studies. After sonication to release the bacteria from the nanoparticles, the bacteria were able to proliferate once again
[46,47,48][39][40][41]. Interestingly, another study showed the entrapping ability of GO nanoflakes (450–870 nm) on Mycobacterium smegmatis to be bacteriostatic
[49][42]. One other study also mentioned that larger GO (>0.4 µm
2) exhibited stronger antibacterial effects on
E. coli, as they have a better bacterial entrapping ability, which is observed by AFM. This
res
tudyearch described the inhibition of nutrient uptake due to bacteria being trapped within the GO, leading to cell death
[24]. A handful of studies have claimed that larger GO exhibited a stronger entrapping effect. However, the effects of the GO sizes on this mechanism are not conclusive. This could be due to several reasons, as suggested below:
-
The method of size measurement used is different (area and diameter).
-
The difference in ranges of the GO sizes. For example, one study may synthesise nanosize GO, while, in another study, microsized GO is used.
-
The different types of bacteria with different sizes and concentrations used.
One study has described the role of GO nanosheets with peaks and terrains in the bacteria-entrapping activity. It was mentioned that the entrapping effect was enhanced when the size of the bacteria matches the deep terrains of GO, which led to the degradation of the membrane integrity and intracellular leakage, as observed on the SEM
[18]. Another study demonstrated the wrapping effect of GO on
S. aureus but not
P. aeruginosa on AFM
[14]. It was speculated to be attributed to the interaction with the thick peptidoglycan of
S. aureus [50][43]. Once again, another study also showed the stronger entrapping ability of GO on
S. aureus than
E. coli. It was suggested that the smaller and spherical
S. aureus was easier to entrap
[17]. Moreover, another study proposed the bacteria-entrapping effect as the antibacterial mechanism against various multidrug-resistant bacteria. It was suggested to be due to the similar or slightly larger size of GO, which allowed bacteria entrapment
[16]. One other study also mentioned that GO nanosheets larger than the bacteria have enhanced entrapping activity. AFM observation showed no change in the morphology, which confirmed the bacteria entrapment
[34]. Thus, it can be seen that the size and shape of bacteria play a role in the bacteria-entrapping mechanism.
3.3. Oxidative Stress
Oxidative stress caused by GO can be via the production of ROS of the depletion of antioxidants present in the bacterial cell
[54][44]. One recent study has reported that the size of GO does not affect the oxidative stress activity ability on
S. mutans [16]. Interestingly, a previous study demonstrated that smaller GO nanosheets coated on a nitrocellulose filter surface are better at inducing oxidative stress on
E. coli [38]. This was also observed in another study
[55][45]. This was speculated to be due to the higher defect densities on the carbon structure, which allowed more oxygen adsorption onto the GO nanosheets.
[56][46]. This was indicated by the higher D band-to-G band ratio of Raman spectroscopy. Interesting, this ratio has a strong correlation with glutathione oxidation (R
2 = 0.96). It was also mentioned that the oxidation capacity of GO nanosheets does not associate with the amount of oxygen-containing functional groups
[38]. One other study also mentioned that the adsorption of oxygen on the defect sites leads to the production of ROS, eventually oxidising glutathione
[57][47]. In addition to this, another study also reported the presence of defects leading to the formation of hydroxyl radicals. Defects were observed by the increase in the D band in the Raman analysis. It was said that the hydroxyl radicals will attack the carbonyl groups in the peptide linkages on the bacterial membrane
[22]. It was mentioned that a tighter bacteria entrapping effect and presence of defects improves the interaction between the GO and bacteria, leading to a better charge transfer, increasing oxidative stress
[18].
Furthermore, another study also suggested the oxidative stress-inducing activity as an antibacterial mechanism for immobilised flat GO on the PET substrate. The immobilised GO renders it unable to penetrate or entrap the
E. coli. Thus, this
res
tudyearch suggested that the oxidative stress was caused by electron transfer via the direct contact of the bacterial with the GO surface
[58][48]. Moreover, another study demonstrated that the availability of the GO basal plane is essential for its antibacterial activity
[59][49]. Nonetheless, a simulation study reported that further oxidation in the oxygen-containing functional groups could improve the oxidation reaction pathways
[31]. Moreover, another study reported that GO coated on a metal surface is able to induce oxidative stress via ROS production against
E. coli. This was said to be attributed to the electron transfer from the bacteria membrane to the oxygen functional groups, generating ROS
[36]. On the other hand, it was reported in a study that physical interactions do not play a major role in the antibacterial activity of surface-coated GO. AFM has shown repulsive forces between GO and
E. coli. In addition, the bridging of lipopolysaccharides on the cell surface also creates a protective barrier. In this
res
tudyearch, GO demonstrated its antibacterial activity by the oxidation of glutathione
[48][41]. Therefore, it can be seen that, generally, GO coated on surfaces induces oxidative stress as its main antibacterial mechanism. In contrast, several studies have also shown that ROS produced in bacterial cells exposed to GO is higher than other graphene derivatives. This was suggested to be due to the stability of GO in suspensions
[28,60,61][28][50][51]. It was also reported that GO could easily react with water to form hydroxyl radicals, leading to a higher production of ROS
[22]. In addition to this, it was also observed that oxidative stress is more effectively induced in Gram-negative bacteria. A few studies have claimed that it was due to the difference in structures of the cell membranes. For example, a study mentioned that Gram-positive bacteria are more susceptible to GO due to the lack of an outer membrane
[22]. Several other studies claimed that GO is more effective on Gram-negative bacteria due to the thinner peptidoglycan layer
[15,17,20][15][17][20]. Interestingly, another study reported that the peptidoglycan layer does not affect the antibacterial activity of GO
[24]. Nevertheless, the antibacterial activity of GO does not depend on the structure of the cell membrane alone. There are other factors that contribute to the antibacterial effect, such as enzymatic activity
[62][52].
4. Photoactivation of GO
The antibacterial activity of GO has also been reported to be induced by photoactivation. For example, one study demonstrated that GO reduced to rGO via light induction produces ROS via the singlet oxygen–superoxide anion radical pathway, which was shown to have antibacterial activity against
Enterobacter sp.
[63][53]. Another study mentioned that
E. coli was able to kill itself as it reduces GO into rGO in anaerobic conditions
[64][54]. In addition, reduced GO/ZnO nanowires were also reported to have a photo-induced antibacterial effect against
E. coli. In this
res
tudyearch, XPD data showed that GO underwent a photocatalytic reduction due to the charge transfer between GO and ZnO, although the material coated onto ZnO was just GO. Interestingly, the photoinactivation of
E. coli by reduced GO/ZnO nanowires, which was 99.5%, was signficantly higher than ZnO alone, which was 58%
[65][55]. These studies showed that the reduction of GO can be considered an intermediate pathway in its antibacterial mechanism. It was also noticed that these studies gave GO treatment at the initial stage. This could be due to the lack of dispersibility of rGO in water due to the reduction of hydrophilic functional groups.