1. Palladium

Palladium is by far the most versatile and widely used metal among transition metals employed in catalysis. In all cases, for this kind of catalysts the catalytically active species have proven to be Pd nanoparticles (NPs) supported on various insoluble matrices. Generally, the catalysts kept their activity and selectivity over several subsequent runs and the reported studies differ from each other for the employed reductant and/or the dimension distribution of the metal NPs.

As recently highlighted by Sukhorukov ^[1], the RA of carbonyl derivatives with nitro compounds can viewed as an old reaction because more than 80 years ago Major ^[2] and Emerson et al. ^[3][4] reported on the coupling of nitroarenes with aldehydes under catalytic hydrogenation over platinum oxide (PtO

₂: Adams’ catalyst ^[5]) and Raney Nickel catalyst, respectively. The proposed protocols were generally applicable to both aromatic and aliphatic aldehydes but in most cases low or moderate yields in secondary amines were achieved.

The modern revaluation for the employment of heterogeneous catalysis for carrying out RA of aldehydes with nitroarenes started only in the 2000 s with the use of commercial source of palladium catalyst (Pd/C). In fact, Yoon and co-workers reported that Pd/C promoted the conversion of nitroaromatics and aldehydes into 

N

₁₀

₁₄

Scheme 1) ^[6].

Scheme 14.

 Stepwise RA catalyzed by Pd/C in the presence of decaborane.

A simple and efficient stepwise RA was achieved throughout reduction of nitroarenes followed by reductive amination. Although the proposed protocol resulted chemoselective and could also be extended to ketones, neither investigations of the scope of reaction nor data on recyclability of catalyst were reported. However, in a follow-up paper ^[7], the same group was able to extend their protocol under excess of formaldehyde for the synthesis of tertiary amines in high yields.

In 2007, Rhee and co-workers proposed another protocol for DRA accelerated by Pd/C ^[8]. Twenty-two mono-

N

₄

Scheme 2). Moreover, it was demonstrated that Pd/C catalyst could be reused for 10 cycles. The proposed protocol, although facile and environmentally benign, is unfortunately not applicable to aromatic aldehydes.

Scheme 25.

 DRA catalyzed by Pd/C in the presence of ammonium formate.

Scheme 3) ^[9].

Scheme 36.

 RA catalyzed by Pd/C under H

₂

.

However, when formaldehyde was used, formation of substantial amounts of the corresponding tertiary amine was observed, but in this case the authors found out that a stepwise RA could be applied with satisfactory yield. No data on the recyclability of the catalyst were given.

Sydnes and co-workers, in a follow-up paper ^[10], extended the scope of their stepwise RA to aromatic aldehydes (

Scheme 4). Isopropanol was used as solvent in place of ethanol. However, for the substrates giving a particularly slow imine-forming step, benzene (or benzene/ethanol) under refluxing conditions was employed as solvent for improving the total yields. In these cases, Pd/C was replaced with Pd/Al

₂

₃ due to the greater stability of the latter catalyst at high temperatures with respect to Pd/C ^[11]. Sometimes, it was found beneficial to add 0.5 equiv (with respect to nitroarene) of triethylamine before the final imine reduction. Twelve benzylated anilines in yields ranging from 41% to 99% were obtained and some case of low yield was attributed to the substitution patterns associated with the aromatic aldehydes. Once again, no investigations on the recyclability of the catalyst were made.

Scheme 47.

 Stepwise RA catalyzed by Pd/C or Pd/Al

₂

O

₃

 under H

₂

.

₂

₄

Scheme 5) ^[12]. The yields were higher when the substituent in the benzaldehyde ring was electron withdrawing. The role of water as hydrogen donor was verified by using D

₂

Scheme 58.

 DRA catalyzed by Pd/C with B

₂

(OH)

₄

 and H

₂

O.

Another important kind of palladium-based heterogeneous catalysts effective for RA is constituted by Pd NPs supported onto organic naturally derived matrices. Pd NPs supported on Gum-Acacia colloids (GA-Pd) have been reported by Sreedhar and co-workers for successful Pd-catalysed DRA applied to both aromatic and aliphatic aldehydes ^[13]. The supported Pd NPs with a narrow size distribution (ranging from 6 to 12 nm) resulted active and selective towards the formation of secondary anilines for at least five subsequent cycles at room temperature, in methanol solvent, using 1 atm dihydrogen as the reductant (

Scheme 6). The yields were quite high (76–96%).

Scheme 69.

 DRA catalyzed by Gum-Acacia supported Pd NPs.

₂ ^[14]. The catalytic system was active, selective, and recyclable for up to four subsequent runs (

Scheme 7).

Scheme 710.

 DRA catalyzed by Pd NPs supported onto Sour Cherry tree gum.

N-substituted anilines under 3 bar dihydrogen in glycerol at 100 °C ^[15]. The yields of secondary anilines ranged from 62 to 89%. No recyclability experiments have been carried out on the RA with this catalytic system.

Dell’Anna and co-workers reported the catalytic activity and recyclability of polymer supported Pd nanoparticles (Pd-pol) obtained by copolymerization of Pd(AAEMA)

₂

⁻ = deprotonated form of 2-(acetoacetoxy) ethyl methacrylate] with methacrylic comonomers, followed by reduction under reaction conditions ^[16]. Pd-pol also proved to accelerate other kinds of chemical reactions such as reductions, oxidations and esterification. ^{[17][18][19][20][21][22]} However, the Pd-pol catalysed reductive amination was successful in one step by using aliphatic aldehydes only. In fact, when benzaldehydes were employed, the one-pot reaction was carried out in three steps to avoid benzyl alcohol formation (

Scheme 8). The catalytically active species were in situ formed Pd NPs with a narrow size distribution centred at 5 nm in diameter, whose morphology remained almost unchanged during reaction. The catalyst resulted recyclable for at least eight subsequent runs without loss of activity and selectivity. The catalytic reactions were performed under mild conditions (1 atm H

₂

Scheme 811.

 RA catalyzed by Pd-pol.

₂

₂

Scheme 9) ^[23]. The catalytic system gave poor yield (23%) in the desired product, when the benzaldehyde had a substituent in 

ortho

Scheme 912.

 DRA catalyzed by Pd/SiO

₂

.

₄

Scheme 10) ^[24]. Transmission Electron Microscopy (TEM) images showed the formation of an ordered mesostructure in H-hierarchical ZSM-5, supporting Pd NPs with an average diameter of 3–6 nm dispersed in the matrix. The activity of the catalyst was quite high, reaching excellent yields (92%–98%) in short time (10–35 min). Recyclability tests demonstrated that after 6 runs with the same catalyst, the yield into the secondary amine passed from 98% (1

^st

^th

₄

₄

Scheme 103.

 DRA catalyzed by Pd/H- hierarchical ZSM-5.

₃

₄

₂

₃

₄ nanocomposites constituted by Pd NPs of 3 nm ca. in size dispersed onto magnetite NPs with an average size of 20 nm ^[25]. These interesting nano-catalysts were able to catalyze the DRA between benzaldehyde and various nitrobenzenes under hydrogen (1 atm) at room temperature (

Scheme 11). Ethanol and methanol were both good solvents, but EtOH was preferred to MeOH from the environmental point of view. The catalyst was easily removed from the reaction mixture thanks to its magnetic features, and then recycled for up eight times without loss of activity and selectivity.

Scheme 114.

 DRA catalyzed by Pd/Fe

₃

O

₄

.

₃

₄

₂

₃

₄

₂) ^[26]. These nano-catalysts resulted active and selective in the DRA at room temperature in ethanol under 1 atm H

₂

Scheme 12). The catalyst was easily recovered at the end of the reaction for further re-uses. The authors noticed that the presence of an electron withdrawing group in 

para-

Scheme 3

Scheme 125.

 DRA catalyzed by XL-Pd(0)–Fe

₃

O

₄

@SiO

₂

.

₃

₄

₃

₄) ^[27]. The Pd NPs with a mean diameter of 7–8 nm resulted homogeneously dispersed onto the surface of the magnetite coated hollow silica sphere. The catalyst could be easily recovered at the end of the reaction, due to its magnetic features, and was reused for six times, without loss of activity. The catalytic tests were carried out in ethanol under dihydrogen atmosphere at room temperature (

Scheme 13) and the obtained yields were quite high (60%–99%).

Scheme 136.

 DRA catalyzed by Pd/HMMS-Fe

₃

O

₄

.

₃

₄

₃

₄@C) ^[28]. These nano materials represent a rare example of catalysts active for DRA performed in water. Since it was proven the existence of carboxyl groups in the outer carbon layer of these nanocomposites, in our opinion, this occurrence was beneficial for the imine formation step, being the latter favored by acid environment ^[29], thus allowing the use of water as the solvent. The catalytic experiments were carried out in water at room temperature or at 60 °C under 1 atm dihydrogen. The catalyst could be recycled for up to six subsequent runs (

Scheme 14).

Scheme 147.

 DRA catalyzed by Pd/Fe

₃

O

₄

@C.

Scheme 158.

 DRA catalyzed by Fe

₃

O

₄

@SiO

₂

/EDAC–Pd(0).

Scheme 169.

 DRA catalyzed by Pd@Fe

₃

O

₄

-NH

₂

/Starch.

Scheme 20.

 DRA catalyzed by Pd/Fe

₃

O

₄

/

Euphorbia stracheyi Boiss

 root extract.

Scheme 21.

 Stepwise RA catalyzed by np-Pd.

2. Platinum

Few examples have been reported in recent years in the field of RA catalyzed by platinum-based catalysts. Among them, Lu and Gu and co-workers ^[34][70] proposed the use of ultrathin Pt nanowires (Pt NWs) as catalyst for DRA starting from various nitroarenes with different benzaldehydes under 1 atm H₂, in toluene, at T = 100 °C. The yields in the desired products were quite high, reaching the value of 95% in some cases (Scheme 22). Recyclability tests demonstrated that the catalyst could be recycled for 6 runs, without losing activity and selectivity. TEM analyses showed that Pt NWs were several hundred nm long and had an average diameter of 2 nm. On the base of GC analyses and DFT calculations, the authors proposed an unusual mechanism pathway for the DRA with their catalytic system. Since Pt catalysts (like Pd catalysts) reduce nitroarenes following the direct route reported in Scheme 2, the authors claimed that, in the presence of Pt NWs under H₂, the hydroxylamine intermediate (see Scheme 2) directly reacts with the carbonyl group of the aldehyde before converting into aniline. In this way, the N-substituted secondary aniline would be obtained without passing throughout the formation of imine.

Scheme 22.

 DRA catalyzed by Pt NWs.

Shreedar and coworker ^[35][71], following their study on precious metal catalyzed RA, employed PtO₂ as pre-catalyst for the stepwise RA starting from various nitrobenzenes, that were first converted into anilines and then condensed with benzaldehydes to give imines. At the end, the imines were hydrogenated to obtain the target product in one-pot three-step way. The overall reaction occurred in methanol at room temperature, by putting the system under 1 atm of H₂ only in the first and in the third step. The catalytically active species were Pt particles suspended in the reaction medium, obtained by preliminary H₂ reduction of PtO₂ suspended in methanol.

No recyclability tests have been reported. Yields ranged from 82 to 99%, being lower (52%) only by using tiophene-2-carboxaldehyde in the RA with nitrobenzene, because sulfur derivatives are known to poison noble metal catalysts (Scheme 23).

Scheme 23.

 Stepwise RA in the presence of PtO

₂

 as pre-catalyst.

In 2020 Zhang and coworkers described the synthesis of Pt nanoparticles with average size of 2.9 ± 0.6 nm loaded onto commercial carbon black to obtain Pt/C with 0.5%_w of Pt, able to catalyze DRA ^[36][72]. The reaction conditions used for catalyzing DRA were quite harsh for a noble metal-based system: T = 70–90 °C, under 1 MPa of H₂ in isopropanol as the solvent, t = 8 h. Conversely, the metal loading was very low (0.026 mol% of Pt) (Scheme 24). Yields were excellent (85%–98%). Recyclability studies revealed a slight decrease of activity after five subsequent runs with the same catalyst.

Scheme 24.

 DRA catalyzed by Pt/C.

3. Iridium

An Ir-based catalyst employed in DRA has been reported by Corma’s group ^[37][73]. The catalyst was a multisite metal organic framework (MOF) material, prepared starting from amine-functionalized Zr-based MOFs, loaded with an Ir complex. This new Zr/Ir-MOF nano-compound acted as a hybrid catalyst that combined the properties of soluble organometallic complexes with those of the MOF heterogeneous support. In fact, it resulted active, selective, and recyclable for at least four runs in the DRA of benzaldehyde with nitrobenzene under 6 bar H₂ at 100 °C in 24 h (Scheme 25). Hot filtration tests demonstrated that the catalytic cycle occurred in the heterogeneous phase, while TEM analyses revealed that no metal nanoparticles formed during the reaction.

Scheme 25.

 DRA catalysed by Ir/Zr-MOF.

In 2017, Huang and co-workers prepared an Ir catalyst (Ir@NC600-2h) by pyrolysis under nitrogen at 600 °C for 2 h of the iridium pre-catalyst, obtained by reaction of the ionic liquid 1-methyl-3-cyanomethylimidazolium chloride with IrCl₃ in the presence of activate carbon powder, to form Ir NPs of 3–5 nm in size, dispersed in the resulting N-doped carbon material ^[38][74]. The catalyst was employed in the DRA of aldehydes with nitroaromatics in toluene at 80 °C under 20 bar H₂. The obtained yields were excellent (93%–99%) (Scheme 26). Recyclability tests were performed starting from benzaldehyde and aniline (instead of nitrobenzene) and the recovered catalyst was reused for five subsequent runs with a slight decrease in its activity.

Scheme 26.

 DRA catalysed by Ir@NC600-2h.

4. Ruthenium

There is just one recent example of Ru catalyst employed for RA, reported in 2012 by Sánchez and co-workers, that synthesized and immobilized on MCM-41 a Ru(II) hydride complex containing a pincer-type pyridine-functionalized N-heterocyclic carbene ligand. This catalyst was used to selectively catalyse the formation of N-substituted amines from nitroaromatics and carbonyl compounds ^[39][75]. The reactions were carried out in isopropanol in this way: first the nitroarene/carbonyl compound mixture was kept at 40 °C under 1.5 bar H₂ for 4 h, causing nitroarene reduction and subsequent imine formation, and then the system was heated to 80 °C under 5 bar H₂ for 12 h for obtaining good yields in the target molecule (Scheme 27). Ethanol could not be used as it resulted in the formation of N-ethyl anilines. The acidity of the MCM-41 matrix promoted the formation of the imine intermediate and, for this reason, the supported Ru catalyst resulted more active than its soluble analogue. Recyclability tests showed that the activity of the recovered heterogeneous catalyst did not decrease after 4 cycles.

Scheme 27.

 DRA catalysed by Ru/MCM-41.

5. Rhodium

There is just one example of Rh-based heterogeneous catalysts for RA in recent years. In 2015 Huang and co-workers reported on the synthesis of a Rh pre-catalyst by reaction between RhCl₃ and 1,10-phenantroline in the presence of activate carbon, following a procedure introduced by Beller’s group for the synthesis of cobalt ^[40][76] and iron catalysts ^[41][77]. The obtained black solid was calcined at 800 °C for 2 h under N₂ to get the final catalyst Rh@CN as black powders formed by N-doped carbon supporting Rh nanoparticles of 6 nm in size ^[42][78]. Rh@CN was able to catalyze the DRA of differently substituted benzaldehydes with various nitrobenzenes under 3 MPa of H₂, at 80 °C, in ethanol for 6–15 h (Scheme 28). The catalyst was re-used for four subsequent runs without loss of activity. TEM analyses showed that Rh NPs slightly increased in size (8 nm) after recycles.

Scheme 28.

 DRA catalysed by Rh@CN.

6. Gold

Between 2007 and 2009, Corma’s group was the first to understand the potential of gold nanoparticles for promoting several cascade-type reactions for the synthesis of different nitrogen-based compounds ^[43][44][79,80] but they reported only one case of DRA starting from nitroarenes and aldehydes catalyzed by TiO₂ supported Au NPs. In this framework, in 2009 Tokunaga and co-workers ^[45][81] employed Au NPs (2−3 nm in diameter) supported on Fe₂O₃ (Au/Fe₂O₃) under low hydrogen pressure for one-pot synthesis of aniline derivatives from nitroarenes and aliphatic or aromatic aldehydes in yields from 58 to 96% (Scheme 29). Aliphatic aldehydes gave lower yields while nitroarenes with electron-withdrawing substituents needed longer reaction times. No attempts of recyclability were carried out with the catalyst because Au/Fe₂O₃ after the catalytic reaction showed a slightly increase of gold particle size as revealed by TEM investigations.

Scheme 29.

 DRA catalysed by Au/Fe

₂

O

₃

.

In 2015, Nuzhdin and co-workers ^[46][82] published their first paper reporting on one-pot reductive amination of aromatic and aliphatic aldehydes with nitroarenes, promoted by Au/Al₂O₃ catalyst with a mean Au particle diameter of 3.4 nm in a continuous flow packed bed reactor using high pressure of molecular hydrogen as a reducing agent (Scheme 30). Nine secondary aromatic amines were achieved in good to excellent yields and the catalyst showed remarkably high chemoselectivity towards the synthesis of N-heptyl-3-vinylaniline starting from 3-nitrostyrene and n-heptaldehyde. In the case of N-heptylaniline, the catalyst was regenerated three times by washing every 135 min the catalyst cartridge with a flow of pure methanol (1 mL/min) for 30 min. Between any cycle (reaction and regeneration) only a slight decay in the yield of N-heptylaniline was observed without leaching of Au from the Au/Al₂O₃ or increasing in gold particle size, but carbon deposition occurred at some extent, as ascertained by differential thermal analysis.

Scheme 30.

 DRA catalysed by Au/Al

₂

O

₃

 in flow reactor.

The high chemoselectivity shown by Au/Al₂O₃ paved the way to a follow-up article ^[47][83] in which the same group reported that Au/Al₂O₃ could also catalyze in a continuous-flow the DRA of aliphatic unsaturated aldehydes with nitroarenes (Scheme 31) obtaining unsaturated secondary amines in moderate to excellent yields (46−99%). Also in this case, the authors were able to regenerate the catalyst by washing it every 150 min with a flow of pure toluene (0.5 mL/min) for 30 min and again it was ascertained by thermal analysis that the formation of carbon-based deposits was the main reason for the slight catalyst deactivation.

Scheme 31.

 DRA catalyzed by Au/Al

₂

O

₃

 in flow reactor using unsaturated aliphatic aldehydes.

Cao and co-workers showed that Au/TiO₂-R, constituted by Au NPs with an average particle size of 2.2 nm supported on titania in the form of rutile (TiO₂-R), catalyzed under very mild reaction conditions the chemoselective transfer hydrogenative DRA of aldehydes with nitroarenes in neat water as solvent employing formic acid (FA) as hydrogen donor (Scheme 32) ^[48][84]. A broad scope reaction was demonstrated with twenty-one secondary aromatic amines being obtained in good to excellent yields (83–98%) minimizing N-formyl derivatives and other unwanted by-products that usually form in appreciable levels with FA-based protocols. Moreover, raising the reaction time up to 20 h, a gram-scale reaction (up to 20 mmol scale-up) was accomplished for the synthesis of N-benzylaniline in 94% yield. Au/TiO₂-R was reused five times without loss of activity and metal leaching. In addition, investigations by TEM, X-ray Photoelectron Spectroscopy (XPS) and X-Ray Diffraction (XRD) revealed almost no change in the dispersion of the Au NPs or metallic state of Au before and after each reuse.

Scheme 32.

 DRA catalyzed by Au/TiO2-R.

In 2020, Rossi and co-workers immobilized pre-synthesized Au NPs by sol-immobilization method on Stöber silica (microspheres of ca 400 nm) obtaining the Au/SiO₂-NH₂ catalyst ^[49][85], which was employed for both reductions and reductive aminations using formic acid as hydrogen source (Scheme 33). The active species were supported Au NPs with an average particle size of 2.2 nm that catalyzed the formation of fourteen secondary amines in moderate to very good yield (41%–92%). To achieve high reaction rates, it was necessary to employ an appropriate Brønsted base (triethylamine), which acted cooperatively with the gold surface for the activation of formic acid as reducing agent. Although the Au/SiO₂-NH₂ catalyst could be reused up to five times without any significant loss of activity and almost no agglomeration of the Au NPs in selective hydrogenation of alkynes, no details on the catalyst recyclability was furnished.

Scheme 33.

 DRA catalyzed by Au/SiO

₂

-NH

₂

.

7. Silver

The only example of a silver-based catalyst reported in recent years for catalysing RA is the one reported in 2017 by Nuzhdin and co-workers, that used Ag/γ−Al₂O₃ catalyst for one-pot reductive amination of aliphatic and aromatic aldehydes with nitroarenes under continuous-flow conditions ^[50][86]. This catalytic system was similar to the above reported Au/Al₂O₃ catalyst ^[46][47][82,83]. The catalyst used to fill the cartridge of the flow reactor was prepared by wet impregnation of γ-Al₂O₃ with silver nitrate, followed by calcination in air at 500 °C for 3 h. The as-prepared catalyst was formed by Ag NPs with a mean size of 5 nm dispersed onto the alumina matrix. However, before use, the catalyst was treated with H₂ (3 MPa) at 110 °C for 1 h to be further reduced. Its catalytic activity was evaluated in the DRA under continuous flow conditions of nitroarenes and various aliphatic and aromatic aldehydes at 100 °C in toluene under H₂ (3 MPa) to get fourteen N-substituted anilines containing alkyl, OH, OCH₃, and even Cl, Br and C=C groups in good to excellent yields (Scheme 34). The accumulation of carbonaceous deposits on the catalyst was the main cause of catalyst deactivation. However, the activity of the spent catalyst could be restored completely through an oxidative treatment in air. The regeneration was carried out only once, but the morphology of the regenerated catalyst remained unchanged and no Ag NPs agglomeration occurred.

Scheme 34.

 DRA catalyzed by 

Ag/γ-Al₂O₃

 under flow conditions.

8. Copper

Following their research studies on DRA promoted by metal catalysts under continuous flow conditions, in 2017, Nuzhdin et al. prepared CuO/γ-Al₂O₃ pre-catalyst for the chemoselective hydrogenation of nitroarenes and one-pot reductive amination of aliphatic and aromatic aldehydes with different nitroarenes ^[51][87]. Before reaction the catalyst was reduced at 120 °C under 50 bar H₂ for 60 min to get Cu/γ-Al₂O_3, the real catalytically active species. The catalytic experiments were carried out in a continuous flow reactor, by using molecular hydrogen as reducing agent with a 1.5 molar excess of aldehyde with respect to nitroarene (because part of the aldehyde was reduced into alcohol) (Scheme 35). Indeed, methanol as the solvent was avoided, since in CH₃OH the hydrogenation of the aldehyde was too fast, thus decreasing the yield into the desired secondary amine. Toluene resulted the best solvent. In the DRA of n-heptanal, introduction of electron-withdrawing substituents in para-position of the nitrobenzene ring decreased the reaction yields, while electron-donating substituents increased the final yields (opposite to what observed by Kalbasi and co-workers in their Pd system ^[24][61]). The observed effect of substituents suggested that the rate determining step of the overall reaction was the imine formation, because the electron properties of the substituents affected the nucleophilic features of the intermediate primary anilines. Various secondary amines were obtained in 10–97% yields (Scheme 35), and a comparison between Cu/γ-Al₂O₃ and the analogous Au/γ-Al₂O₃ ^[46][47][82,83] activities showed that the mass of the secondary amine (g) produced during 1 h per mass of metal (g), in Cu system was only 3.3–4.1 times lower than in Au one. Formation of carbonaceous deposits on the catalyst surface led to a slight deactivation of Cu/γ-Al₂O_3, which was regenerated once by oxidative treatment in air at 330 °C for 2 h. The influence of different supports, such as γ-Al₂O₃, SiO₂, and TiO₂–SiO₂ on the activity of Cu catalyst in DRA of n-heptanal with p-nitrotoluene under continuous flow conditions was deeply studied in a follow-up article ^[52][88], and it was demonstrated that Cu/γ-Al₂O_3, was the most active catalyst among those considered. In the same article the authors proposed a heterolytic cleavage of dihydrogen in the catalytic cycles of the hydrogenation steps.

Scheme 35.

 DRA catalyzed by Cu/γ-Al

₂

O

₃

 under flow conditions.

9. Iron

In recent years, Beller’s group has made many efforts in developing earth abundant metal based catalytic systems for DRA reaction. In 2014 they reported on the use of an iron oxide catalyst (Fe₂O₃/NG@C ) ^[41][77] for one-pot direct reductive amination of various benzaldehydes with different nitroarenes, using THF/H₂O as the solvent ^[53][89] in quite harsh reaction conditions: T = 170 °C, 70 bar of dihydrogen, reaction time = 30 h (Scheme 36). The catalyst was obtained by reaction of Fe(OAc)₂ and 1,10-phenanthroline, followed by addition of Vulcan XC72R as carbon support. The resulting suspension containing iron coated carbon powder was dried and pyrolyzed at 800 °C for 2 h under argon to get the final catalyst, namely Fe₂O₃/NG@C, which resulted core-shell structured with a core of Fe₂O₃ nanoparticles with size ranging from 2 to 100 nm (with some agglomeration) incorporated in a layer of N-doped graphene containing both pyridinic and pyrrolic nitrogen species. Doping a catalyst with nitrogen is a strategy largely used by Beller’s group and then followed also by other scientists, aiming at affecting the electronic features of the metals and at stabilizing the formed metal-based nanoparticles. Fe₂O₃/NG@C was recovered at the end of reaction and re-used for five cycles with a slight loss of activity.

Scheme 36.

 DRA catalyzed by Fe

₂

O

₃

/NG@C.

In a follow-up article ^[54][90], Beller detailed the above reported protocol for both the synthesis of Fe₂O₃/NG@C and catalytic tests, isolating for all RA trials the products by flash chromatography (Scheme 37), obtaining for some examples yields slightly different from the ones reported in Scheme 36 for the same substrates.

Scheme 37.

 DRA catalyzed by Fe

₂

O

₃

/NGr@C.

10. Cobalt

In 2013 Beller’s group synthesized the cobalt-based catalyst Co₃O₄/NGr@C (analogous to Fe₂O₃/NGr@C) by loading Vulcan XC72R carbon powder with a cobalt (II)-phenanthroline-chelate complex, and then pyrolyzing the obtained material at 800 °C for 2 h under Ar ^[40][76]. Co₃O₄/NGr@C was a core-shell nanocomposite constituted by a core of Co NPs and a shell of Co₃O₄ NPs with size in the range of 2–20 nm, forming agglomerates sizing 20–200 nm, coated in turn by a N-doped graphene layer. The so obtained heterogeneous catalyst was employed for DRA in THF/H₂O under quite severe conditions: 110–125 °C, 50 bar of H₂, reaction time = 24 h (Scheme 38) ^[55][91]. However, the designed catalytic system had the great advantage to tolerate the presence of other reducible groups, such as C=O, or halogen substituents (resisting to dehydrohalogenation) in the starting nitroarene ring or/and in the used benzaldehyde. This valuable peculiarity is a characteristic common to all Co-based catalytic systems for DRA proposed by Beller in subsequent works. Recyclability tests demonstrated that on passing from the first to the second run with the same catalyst, the yield dropped from 95% to 70% ca., then remaining constant at around 60% until the sixth cycle.

Scheme 38.

 DRA catalyzed by Co

₃

O

₄

/NGr@C.

In 2018 Jagadeesh and co-workers employed the same Co₃O₄/NGr@C material as catalyst for DRA, using in this case the mixture formic acid/Et₃N (in 5/2 molar ratio), instead of H₂, as the hydrogen donor (Scheme 39) ^[56][92]. The good yields obtained in the catalytic tests remained mainly constant also performing gram-scale reactions. The catalyst could be recycled up to five times demonstrating stability and reusability. This catalytic system was highly chemoselective, tolerating the presence of many reducible groups.

Scheme 39.

 DRA catalyzed by Co

₃

O

₄

/NGr@C with HCOOH/Et

₃

N.

In 2017 Beller and co-workers synthesized MOF-derived cobalt nanoparticles catalytically active in direct RA reactions ^[57][93]. The catalyst was obtained by preparing a Co-diamine-dicarboxylic acid MOF precursor (namely Co-DABCO-TPA MOF, DABCO = 1,4-diazabicyclo [2.2.2]octane and TPA = terephthalic acid), which was in turn pyrolyzed on Vulcan XC72R carbon at 800 °C for 2 h under Ar, to get the final active nanomaterial (Co-DABCO-TPA@C-800), constituted by Co nanoparticles with diameters ranging from <5 to 30 nm, encapsulated in N-doped graphitic shells, supporting also single Co atoms. As in the previously reported work ^[55][91], some core-shell particles with cobalt oxide Co₃O₄ shells at metallic Co cores were also present. The new nanomaterial was tested as catalyst in the synthesis of a wide range of amines in good to excellent yields (Scheme 40) through DRA starting from different aldehydes with nitro compounds under 40 bar of molecular hydrogen at 120 °C in tert-BuOH in the presence of amberlite IR-120 for 24 h. The recyclability of the catalyst was tested in the synthesis of amphetamine, i.e. in the reaction between acetophenone and ammonia: the catalyst resulted recyclable for at least six runs without loss of activity and selectivity.

Scheme 40.

 DRA catalyzed by Co-DABCO-TPA@C-800.

Following the above mentioned strategy of using N-doped carbon support for synthetizing Co-based catalysts, in 2017 Cui and co-workers have described the preparation of a new nanomaterial (Co/mCN-900) by pyrolysis under N₂ at 900 °C for 1 h of a mixture of melamine, polyacrylonitrile, and Co(NO₃)₂⋅6H₂O ^[58][94]. In this way, a fluffy mesoporous carbon structure with high surface area and high nitrogen content was obtained. This N-doped carbon material supported dispersed accessible Co nanoparticle active sites (average size of 6 nm) and resulted an efficient catalyst in the N-alkylation of different nitrobenzenes with substituted benzaldehydes, allowing the synthesis of a wide range of aromatic amines with good yields under 1 MPa of H₂, at 150 °C in ethanol (Scheme 41). The recyclability test was performed for the hydrogenation of nitrobenzene only (first step of the RDA) for six runs with the same catalyst. The catalytic system tolerated the presence of other reducible groups.

Scheme 41.

 DRA catalyzed by Co/mCN-900.

In 2017, Zhang and co-worker investigated the catalytic activity in DRA of a cobalt-based material, namely Co-Nx/C-800-AT ^[59][95], generated from the pyrolysis of cobalt phthalocyanine/silica composite at 800 °C under N₂ and subsequent etching by HF to remove Co nanoparticles and silica template, affording a mesoporous polymer with mean pore size of 3.6 nm, containing Co-N_x catalytically active sites ^[60][96]. This strategy of synthesis, differently from the above reported ones, aims to remove all metal (or eventually metal oxide) nanoparticles, leaving a carbon-based support retaining just Co-N_x fragments, considered responsible for catalytic activity. As shown in Scheme 42, DRA was carried out at 150 °C in ethyl acetate using formic acid as hydrogen donor and a combination of different aldehydes and nitro compounds was well tolerated under reaction conditions. Moreover, the catalyst was active and stable during six runs without leaching of Co from the system. The catalytic system was highly chemoselective tolerating the presence of C=O, CN, and halogen atoms in the nitroarene ring.

Scheme 42.

 DRA catalyzed by Co-Nx/C-800-AT.

In addition, the catalyst Co-N_x/C-800-AT has been tested in the RDA reaction using H₂ (10 bar), as the reductant, in methanol at 110 °C for 10 h ^[61][97]. Kinetic studies pointed out that, for the Co-N_x/C-800-AT catalytic system, the rate-determining step of the overall reaction was the hydrogenation of the imine intermediate. For this reason, the steric hindrance of the substituents located in ortho-position in nitroarene and benzaldehyde substrates dramatically decreased the final yields towards the target molecule. Scheme 43 summarizes the wide scope of substrates explored. The catalyst was successfully recycled for six runs

Scheme 43.

 DRA catalyzed by Co-N

_x

/C-800-AT under 10 bar H

₂

.

On the basis of the above reported results, in the second part of 2017, Zhang’s group synthesized another catalyst by pyrolysis at 600 °C for 3 h under N₂ of cobalt supporting zeolitic imidazolate-frameworks (ZIF-67)/graphene oxide (GO) composite (ZIF-67/GO), followed by acid-etching with H₂SO₄, aiming to remove Co NPs formed under calcination ^[62][98]. Differently from the Co-N_x/C-800-AT material, in this case the acid washing was able to remove just the surficial metal nanoparticles of the new material and the resulting catalyst (Co@CN-600-AT) still contained Co NPs with an average diameter of 8.2 nm, embedded into the reduced graphene oxide phase (graphene oxide became reduced graphene oxide during calcination). Co@CN-600-AT was active, stable, and selective in the direct RA using formic acid as hydrogen source, in THF at 190 °C for 15 h (Scheme 44). The catalyst could be recycled for six times without losing its activity.

Scheme 44.

 DRA catalyzed by Co@CN-600-AT.

Following their studies on the synthesis of N-doped cobalt-based material, in 2017 Zhang’s group prepared another cobalt containing precursor, similar to the above reported ZiF-67/GO, but with silica in place of graphene oxide (ZIF-67/SiO₂ composite). This cobalt containing material was pyrolyzed at 800 °C for 8 h under N₂, and subsequently treated with hydrofluoric acidto remove surficial Co nanoparticles and silica template, yielding nitrogen-doped carbon-embedded Co nanoparticles with an average size of 6.3 nm (Co@CN-800) ^[63][99].

As shown in Scheme 45, Co@CN-800 catalyst was active and recyclable (for at least eight runs) in the direct reductive amination of various substrates using formic acid, as hydrogen donor, at 170–190 °C in THF.

Scheme 45.

 DRA catalyzed by Co@CN-800.

Pyrolysis of ZIF-67 under N₂ at 600 °C, followed by HF etching to remove Co NPs from the surface gave a new material (called Co/N-C-600) that was employed as catalyst for DRA. ZIF-67, as previously reported, consists of cobalt supported zeolitic imidazolate-frameworks, made up of cobalt cation and 2-methylimidazole ligand, obtained by simply mixing Co(NO₃)₂·6H₂O with 2-methylimidazole in water. Co/N-C-600 contained Co-nanoparticles (with average diameter of 14 nm) embedded in N-doped carbon support and was active in the direct RA using, for the first time in this reaction, CO/H₂O as hydrogen source ^[64][100]. The proposed catalytic cycle envisaged the formation of formate ion and the resulting transfer hydrogenation mechanism resembled the pathway observed with the use of acid formic as hydrogen donor. The presence of nitrogen in the N-doped material was of crucial importance because doping N served as base site to capture the H⁺ from water during the activation of CO/H₂O, to generate the active species (a proton and a metal hydride). Several aldehydes were tested in the reaction with nitro compounds under the conditions experienced without loss of activity. Noteworthy, the strong interaction between cobalt nanoparticles and nitrogen atoms warranted a high stability of the catalyst for 6 recycling runs (Scheme 46).

Scheme 46.

 DRA catalyzed by Co/N-C-600 with CO/H

₂

O.

In 2019, Guo’s group developed a N,S-dual-doped carbon material embedding Co nanoparticles with an average size of 2.01 nm, useful for catalyzing DRA with formic acid ^[65][101]. For the synthesis of the new catalyst, first the microwave assisted condensation of melamine and terephthalaldehyde was carried out in DMSO to give a Shiff base network (SNW-1, a porous organic polymer) incorporating sulfur impurities (due to the solvent used). Then, SNW-1 was impregnated with a cobalt salt and coated with glucose, and then pyrolyzed under inert atmosphere at 850 °C for 2 h. The resulting nanomaterial, Co@NSC-3 had a core-shell structure with cores of well-distributed cobalt NPs and N,S-doped carbon shells. Co@NSC-3 catalyzed the direct RA with formic acid as a hydrogen donor at 170 °C in THF/H₂O. The system worked without a base and showed interesting activity, selectivity, and stability for the synthesis of several kinds of secondary amines (Scheme 47). Recyclability tests demonstrated that the catalytic system could be re-used for at least five runs without loss of activity and selectivity.

Scheme 47.

 DRA catalyzed by Co@NSC-3.

11. Nickel

In 2015 Kalbasi and Mazaheri ^[66][102] reported the synthesis of nickel nanoparticles (average size of 5 nm), supported on acid hierarchical zeolite (Ni/H-mZSM-5) with a microporous/mesoporous structure, as an acid-metal bifunctional catalyst. The catalytic activity of Ni/H-mZSM-5 was tested in one-pot RA of aromatic aldehydes with nitroarenes at room temperature, by using sodium borohydride as reducing agent and water as the solvent (Scheme 48). The simultaneous presence of acid and metal in the catalytic structure promoted a high activity and reusability of the heterogeneous catalyst in water under mild conditions for at least five runs, with a slight reduction of activity (the yield dropped from 98% of the first run down to 73% of the fifth cycle). The efficiency of the Ni catalytic system prompted the same authors to replace Ni for Pd, preparing the analogous Pd/H-hierarcal ZSM-5 already discussed in ^[24][61].

Scheme 48.

 DRA catalyzed by Ni/H-mZSM-5.

On the basis of the above reported results, Kalbasi and coworker ^[67][103] developed a new heterogeneous catalyst constituted by ordered mesoporous carbon CMK-8 supporting both Ni nanoparticles (size ranging from 2 to 6 nm) and polystyrene sulfonic acid (PSSA) chains, thus having a dual (metal and acid) functionality. The new heterogeneous bi-functional catalyst, Ni-PSSA/CMK-8 was similar in the concept to the previously reported Ni/H-mZSM-5. The difference between the two catalysts was in the solid support: while hierarchical ZSM-5 is an inorganic solid acid with a relatively low surface area, PSSA/CMK-8 composite is an organic solid acid with a higher surface area, thus potentially more active. The new catalyst was tested in direct RA of aldehydes under mild reaction conditions and short reaction time in ethanol/water as solvent (Scheme 49). Recyclability tests demonstrated that the catalyst could be used for at least ten runs with slight metal leaching into solution and small decrease of yield (83% in the first run; 68% in the 10^th cycle). For DRA carried out with Ni-PSSA/CMK-8 the authors observed the same substituent electronic effects registered with Pd/H-hierarchical ZSM-5 catalytic system ^[24][61], that is: the reaction rate was improved by the presence of electron withdrawing and electron donating substituents in nitrobenzene and benzaldehyde rings, respectively. In addition, to get insights into the mechanism pathway, Kalbasi and coworker mixed aniline, benzaldehyde, and Ni-PSSA/CMK-8 in EtOH/H₂O in the absence of the reductant and observed 40% yield in imine (no secondary amine formation), but when they added to the mixture the appropriate amount of NaBH₄, they registered 83% yield in the target molecule (secondary amine), and not 40% as they thought to find. On the basis of this observation, the authors claimed for their catalytic system the presence of an additional mechanism for the imine formation, passing through the reaction between benzyl alcohol (eventually formed under reaction conditions, but not detected by the authors) and aniline, to give imine, subsequently reduced to secondary amine. However, this speculation is not convincing because the condensation between benzaldehyde and aniline is an equilibrium reaction ^[29][36], whose balance is shifted towards the imine product once the latter is subtracted from the system, due to its hydrogenation. Therefore, it was not surprising that the yield into secondary amine increased when the imine was removed from the equilibrium.

Scheme 49.

 DRA catalyzed by Ni- PSSA/CMK-8.

In 2019 Wang and Chen prepared a MOF-derived catalyst with nickel nanoparticles (6–7 nm in size) uniformly embedded in nitrogen doped carbon shells ^[68][104], following roughly the strategy already introduced by Beller and discussed in the above reported paragraphs. In details, the new catalyst was obtained by mixing 2-aminoterephthalic acid and polyvinylpyrrolidone with a nickel(II) salt in DMF/water, thus obtaining a green solid precipitate (Ni-MOF-NH₂), which was pyrolyzed at 600 °C for 1.5 h under Ar to get the final Ni@NC-600-1.5 catalyst. The new catalyst resulted active and selective for at least five runs in direct RA under H₂ (2 MPa) at 100 °C in THF/H₂O (Scheme 50). The catalyst possessed magnetic features which allowed its easy removal from the reaction mixture by an external magnet, and its subsequent recycling for five runs without loss of activity and recyclability. XRD analyses excluded the formation of NiO, while N-doping promoted the dispersion of Ni nanoparticles and enhanced their ability to activate H₂ through heterolytic cleavage, further facilitated by the presence of pyridinic N found in the carbon shells.

Scheme 50.

 DRA catalyzed by Ni@NC-600-1.5.

Another example of N-doped organic matrix supporting Ni NPs as efficient catalyst for RA reaction has been reported in 2019 by Dell’Anna and co-workers ^[69][105]. Indeed, on the basis of the good results obtained with the already discussed Pd-pol ^[16][53], the strategy of synthesis followed for Pd-pol was transferred for the synthesis of Ni-pol, wherein the noble metal Pd was replaced by the earth abundant nickel. The polymer has been prepared by co-polymerizing the metal containing monomer ^[70][106] Ni(AAEMA)₂ [AAEMA⁻ = deprotonated form of 2-(acetoacetoxy) ethyl methacrylate] with N,N-dimethylacrylamide and N,N’-methylenebisacrylamide ^[71][107] and submitting it to calcination at 300 °C under N₂, obtaining a N-containing organic polymer (Ni-pol) with a homogeneous distribution of cubic nanocrystals of Ni of average cross section value of 35 nm ^[72][108]. Ni-pol was tested in the stepwise RA of various benzaldehydes with different nitroarenes in methanol at room temperature, using NaBH₄ as the reductant (Scheme 51). The addition of few drops of formic acid was necessary in the condensation step to promote the formation of the imine intermediate. Twenty-two secondary amines have been synthetized with Ni-pol catalytic system, some of them containing halogen substituents (no hydro-dehalogenation occurred) or reducible group (-CN). Ni-pol was recovered at the end of reaction and used for five subsequent runs without loss of activity and selectivity.

Scheme 51.

 Stepwise RA catalyzed by Ni-pol.

In 2020, Hara and co-workers prepared Ni/NiO-300 by partial reduction of NiO at 300 °C with H₂ and employed it as heterogeneous catalyst for one-pot reductive amination of benzaldehydes with different nitroarenes under dihydrogen (1 MPa) in toluene for 20 h (Scheme 52) ^[73][109]. The catalyst could be reused for four cycles without catalytic losses. Scanning Electron Microscopy (SEM) and XPS analyses showed that Ni/NiO-300 was constituted by Ni particles with size of about 0.5–3 μm coated with a layer of NiO, which remained the same after catalytic cycles. The metal amount used is very high for a catalytic reaction.

Scheme 52.

 DRA catalyzed by Ni/NiO-300.

12. MoS₂ Catalyst

There is just one example reported in 2019 by Zhang et al. that used defective MoS₂ with sulfur vacancies for catalysing RDA to prepare secondary amines in excellent yields. MoS₂ was subjected to thermal treatment at 450 °C under nitrogen atmosphere (to get the so-called CAT-450) to improve its catalytic activity due to the sublimation of MoS₂ and sulfur ^[74][110]. Since sublimation of sulfur is faster than sublimation of MoS₂, large sulfur vacancies area on MoS₂ surface formed in CAT-450. These vacancies could effectively adsorb and activate dihydrogen, nitro compounds, and imines, for efficiently catalysing DRA of various nitroarenes and benzaldehydes in EtOH/H₂O, at 120–130 °C under 2 MPa H₂ for 5 h (Scheme 53). CAT-450 could be recycled without decrease of its catalytic performance after the fourth run.

Scheme 53.

 DRA catalyzed by CAT-450.

13. Heterobimetallic Catalysts

Recently, many efforts have been devoted to designing heterobimetallic catalytic systems active for RA, aiming at conjugating the properties of two different metals, hoping in a synergic action. In fact, using simultaneously two metals active in two different steps of the RA process could in principle improve the final yield towards the target product. In addition, a metal of a heterobimetallic catalyst could lower the extent of side reactions (such as reduction of aldehyde, C-N bond hydrogenolysis, etc.) deriving from the use of the other metal alone. Moreover, as for monometallic catalysts, the goodness of a heterobimetallic catalytic system could be enhanced by choosing a proper insoluble support with acidic, basic, or magnetic features.

13.1. PdAg

The first application of heterobimetallic nanoparticles for DRA from nitroarenes and aldehydes was reported in 2013 by He, Li and co-workers ^[75][111]. By co-reduction of Pd(acac)₂ and AgOOCCF₃ using a solution of borane-tert-butylamine adduct in oleylamine, they were able to synthesize a series of Pd_1−xAg_x (x = 0–1) nanoparticles, among which Pd₁Ag₃ NPs, with mean particle size of ca. 3 nm was found as optimal catalyst for DRA in terms of activity and selectivity under mild conditions (1 atm H₂ and RT). The exact Pd/Ag ratio was determined by inductively coupled plasma atomic emission spectroscopy (ICP-AES) analysis, and the catalyst was renamed as Pd₁Ag_1.7. Ten secondary amines were obtained in good to excellent yields (83–94%) with a good functional group compatibility (Scheme 54). The catalyst could be easily recovered by centrifugation and reused at least five times without loss of activity. Investigations by TEM revealed no observable structural change in the dispersion of the spent catalyst with respect to the fresh one.

Scheme 54.

 DRA catalyzed by Pd

₁

Ag

_1.7

.

Another heterobimetallic catalyst based on silver and palladium for RA from nitroarenes and aldehydes was proposed in 2018 by Metin and co-workers ^[76][112]. Taking advantage of their previous experience in the synthesis of AgPd alloy NPs by one-pot co-reduction of silver(I) acetate and palladium(II) acetylacetonate in the presence of oleylamine and oleic acid as surfactants in hot 1-octadecene ^[77][113], the authors were able to support, via. a liquid phase self-assembly method, these NPs (2.5 ± 0.5 nm) on high-surface area and commercially available mesoporous graphitic carbon nitride (mpg-C₃N₄) obtaining the mpg-C₃N₄/Ag₄₀Pd₆₀ catalyst. A protocol in harmony with the green chemistry rules was developed with this catalyst. In fact, it promoted a stepwise RA of arylaldehydes with nitroaromatics utilizing formic acid as hydrogen source and water as solvent (Scheme 55) furnishing eleven N-benzylanilines in moderate to excellent yields (65–99%). The proposed catalytic system could be reused at least 4 times without loss of activity, and investigations by TEM and powder XRD on recycled catalyst revealed that there was almost no change with respect to the initial morphology and crystal structure of fresh mpg-C₃N₄/Ag₄₀Pd₆₀ catalyst.

Scheme 55.

 DRA catalyzed by mpg-C

₃

N

₄

/Ag

₄₀

Pd

₆₀

.

13.2. PdAu

In 2018 Kim and co-workers prepared an AuPd alloy supported on magnetic Fe₃O₄ nanoparticles with mean particle size of ca. 5 nm (AuPd–Fe₃O₄) from PdCl₂ and AuCl₃·3H₂O in presence of polyvinylpyrrolidone (PVP) and subsequent reduction with NaBH₄ ^[78][114]. Investigations through X-ray photoelectron spectroscopy (XPS) of the oxidation states and electronic properties on AuPd–Fe₃O₄ surface confirmed the formation of an alloy with Au and Pd metals that remained unchanged in these properties after a catalytic cycle. AuPd–Fe₃O₄ nanocatalyst promoted selective DRA from a variety of nitroarenes and aryl or alkyl aldehydes under 1 atm of H₂ at RT in methanol (Scheme 56). The selective syntheses of eighteen secondary amines in good to excellent yields were obtained and no N-debenzylation was remarkably observed in the case of reactions involving aryl aldehydes. Due to well-known magnetic property of the support, the separation of the AuPd–Fe₃O₄ catalyst could be rapidly realized by a small neodymium magnet and the catalyst could be recycled for further nineteen recycles without an appreciable loss of activity and significant metal leaching (only 7% loss of the initial content of gold and palladium). Under the optimized reaction conditions, the catalytic activity was maintained until the 13^th reaction cycle and a slight decrease of yield was observed from the 14^th to 16^th cycles. However, raising the reaction time from the 17^th to 20^th cycles the yields returned to the average values found in previous cycles. Thanks to the aid of accurate investigations by TEM and SEM, the authors were able to find that the modest metal leaching would not be the main reason for the reduced catalytic activity but that this was caused by a distinctive agglomeration of AuPd nanoalloy on Fe₃O₄ support after the 16^th and 20^th reaction cycle (see the Supporting Information of ^[78][114] for TEM and SEM images of the used catalyst).

Scheme 56.

 DRA catalyzed by AuPd–Fe

₃

O

₄

.

Liang and co-workers reported a series of catalysts for DRA, based on Au–Pd alloys well dispersed within amine functionalized metal-organic framework (MOF, UiO-66-NH₂) ^[79][115]. However, only Au–Pd alloy nanoparticles with low Pd content (Au-Pd_0.03@UiO-66-NH₂) exhibited high selectivity for DRA with benzaldehyde and nitrobenzene, and thus the sole synthesis of N-benzylaniline in 93% yield was obtained in cyclohexane as solvent at 50 °C under 1.0 MPa of H₂.

13.3. PdPt

In 2016 Kim group reported the synthesis of heterogenized bimetallic Pd−Pt−Fe₃O₄ nanoflakes via. the simultaneous reduction of PdCl₂ and K₂PtCl₄ in presence of PVP as a dispersant and ethylene glycol acting as both solvent and reductant, followed by deposition of the two metal NPs on commercially available Fe₃O₄ nanocrystals in a simple one-pot solution phase hydrothermal process ^[80][116]. Fe₃O₄ support was decorated with well-dispersed Pd–Pt NPs having diameters ranging from 5 to 8 nm. Pd−Pt−Fe₃O₄ proved to be a very active and magnetically recyclable catalyst for chemoselective reduction of several nitroarenes with the use of ammonia borane (NH₃BH₃) as a hydrogen source. These characteristics prompted Kim’s and Park’s groups to explore the use of Pd−Pt−Fe₃O₄ as magnetically catalyst for developing a very fast stepwise RA from nitroarenes and aldehydes at room temperature using NH₃BH₃ as reducing agent in a continuous flow system (Scheme 57) ^[81][117]. The peculiarity of the flow system developed by these authors is that the catalyst was directly fixed in a simple perfluoroalkoxy alkanes (PFA) tubing with the aid of commercially available permanent neodymium magnets without the use of a special cartridge or column. Obviously, the fixation of magnetic nanoflakes of Pd-Pt-Fe₃O₄ in tubes obtained in this way resulted reversible by removing the neodymium magnets. The selective syntheses of twenty-four secondary amines in moderate to excellent yields were obtained and, moreover, a long-term (24 h) effectiveness experiment using nitrobenzene and benzaldehyde, showed an average yield of 93% (12.2 g) in N-benzylaniline without Pd and Pt leaching.

Scheme 57.

 Stepwise RA catalyzed by Pd−Pt−Fe

₃

O

₄

 under continuous flow conditions.

13.4. CoRh

In 2015 the Chung group developed cobalt/rhodium heterobimetallic nanoparticles immobilized on charcoal Co₂Rh₂/C as catalyst for RA from aldehydes with nitroarenes under 5 atm pressure of carbon monoxide without an external hydrogen source, which is produced via a water gas-shift reaction thanks to water both added and generated in situ ^[82][118]. Co₂Rh₂ nanoparticles were obtained by reacting cobalt and rhodium carbonyl cluster Co₂Rh₂(CO)₁₂ in presence of oleic acid and trioctylphosphane oxide in hot ortho-dichlorobenzene and were eventually supported on flame-dried charcoal. The so-obtained Co₂Rh₂/C catalyst promoted the synthesis of fourteen N-benzylanilines in good to excellent yields in THF/H₂O mixture at high temperature (Scheme 58).

Scheme 58.

 DRA catalyzed by Co

₂

Rh

₂

/C.

Two years later ^[83][119], the same group reported that the heterogeneous Co₂Rh₂/C catalyst also showed excellent activity and good selectivity for one-pot DRA of aldehydes with nitroarenes in methanol under mild conditions (1 atm H₂ and 25 °C) without any additives (Scheme 59). A very wide scope of reaction was demonstrated by reporting the synthesis in moderate to excellent yields of thirty-one secondary amines with very broad functional group compatibility. The proposed procedure was also scaled up to the gram scale, and the Co₂Rh₂/C catalyst could be easily recovered by centrifugation and recycled at least six times without loss of activity. No investigations on spent catalyst morphology were reported.

Scheme 59.

 DRA catalyzed by Co

₂

Rh

₂

/C under H

₂

.

13.5. FeNi

In 2020 Chikate et al. immobilized non-noble Fe–Ni bimetallic nanoparticles (10%_w) on montmorillonite (MMT) generating a bifunctional nanocomposite 10% Fe–Ni/MNT, which was tested as catalyst for a stepwise RA of aldehydes with nitroarenes using NaBH₄ as hydrogen source (Scheme 60) ^[84][120]. Eleven secondary anilines were obtained in excellent yields and the catalytic system could be recycled at least five times without loss of activity. XPS studies carried out with fresh and recovered nanocomposite showed that surface properties of catalyst remained unaltered during reductive amination.

Scheme 60.

 Stepwise RA catalyzed by 10% Fe–Ni/MNT.

Finally, carbon-supported Fe–Ni alloy nanoparticles for DRA in a continuous fixed-bed reactor were already reported in 2015 by Esposito and co-workers. In this work the authors carried out DRA from nitrobenzene and benzaldehyde (3 equiv with respect to nitrobenzene) under very harsh conditions (125 °C and 10 bar of H₂) achieving N-benzylaniline in 83% yield ^[85][121].