Crack healing has been a key area of asphalt pavement research. Energy supply technologies (induction and microwave heating) have demonstrated significant efficacy in enhancing the crack healing capability of asphalt pavement, particularly in microcracks. Crack healing technologies can effectively prolong the service life of asphalt pavement, thereby further reducing the damage to the environment caused by road engineering, reducing energy consumption and CO2 emissions.

  • asphalt pavement
  • cracks
  • self-healing technologies

1. Hot Pouring

Hot pouring and fog sealing are the most traditional and universal methods to heal cracks in the current road maintenance. Hot pouring is usually applied for big and long structure cracks, while fog sealing is used for fatigue cracks and aged pavement surfaces [1]. The pavement heat pouring technology is mainly used to pour hot polymer materials with strong cohesion and elasticity into the cracks of the asphalt pavement. The polymer material is usually made of base asphalt, high molecular weight polymers, stabilizers, additives, and other materials. The method is used to repair large and long transverse cracks and horizontal cracks [1]. The road can be maintained in time to prevent the damage caused by the entry of rainwater and impurities and the appearance of potholes inside, thus extending its service life [2]. However, it can only be done completely manually, which is expensive and inefficient. And the cracks have extended to the last period when the materials can pot into the cracks. Hot pouring technology can not extend service life too much (Figure 1).
Figure 1. Hot pouring technology to heal the cracks.

2. Fog Sealing

A fog seal is an application of asphalt emulsion to an existing asphalt pavement surface that has aged and developed cracks or other distresses (Figure 2). After the asphalt emulsion is demulsified, the fog seal material can penetrate the aged asphalt concrete and also flow into the micro-cracks. It can rejuvenate aged asphalt concrete, close interconnected voids, heal cracks, and prevent moisture damage [3]. The technology could usually extend the surface performance of asphalt pavement for 2–3 years [4].
Figure 2. Fog seal technology with operation.
There are still certain disadvantages to the application process. After the asphalt emulsion breaks and cures, the cracks and voids are closed, and the skid resistance of the asphalt pavement surface will reduce significantly. Traditional fog seal materials face adhesion loss and spalling failure because of low mechanical strength and inadequate cracking resistance [5][6]. Islam’s research has shown that spraying fog seal reduces the coefficient of friction of pavements by 20% to 40% [6]. Low diffusion and uneven spraying combined with the decline of anti-skid resistance will not only affect the damage to the pavement structure but also seriously affect the safety of driving. Modified emulsified bitumen with polymer material (like styrene-butadiene-rubber (SBR) or styrene-butadiene-styrene (SBS)), which helps to increase the adhesion of the fog seal material [7]. Xu et al. found that waterborne additives (acrylates, cationic acrylates, and polyurethane) can improve the thermal cracking resistance of SBS-modified asphalt emulsions through the synergy effect [5]. Liu et al. used epoxy resin to modify fog seal materials and found it could shorten the surface dry time and increase the waterproofing and durability of asphalt pavement [8]. In order to increase the skid resistance performance of the pavement surface after fog sealing, a sand fog seal concept was proposed, which is composed of fog seal materials and fine sand. Ma et al. designed sand fog seal materials with different sand contents and optimised the 25% sand content to balance stability and fluidity well [9]. Zhang et al. also determined the best formulation of sand fog seal mortar and a method for predicting traffic open time based on image processing technology [10].

3. Heating Technologies

Bituminous material itself is a self-healing material capable of repairing cracks, but sufficient temperature and time are required. Mainly because the viscosity of bitumen is temperature-sensitive; the higher the temperature, the smaller the viscosity [11]. Heating the bitumen can reduce the viscosity of the asphalt, which not only reduces the surface energy of the crack but also makes the bitumen have better fluidity to flow into the crack and heal it [12]. And high temperatures help improve bitumen molecular diffusion to heal the cracks. Based on the theories, heating asphalt concrete technologies were proposed to heal the crack that occurred in the service process due to ageing, traffic loading, or fatigue. Induction heating and microwave heating are efficient and non-contact heating methods that are suitable for heating asphalt pavement [13]. They just take dozens of seconds to heat up to asphalt’s self-healing temperature.

3.1. Induction Heating

The basic principles of induction heating technology are electromagnetic induction and joule heating. During the test process, when the material is placed in the induced magnetic field, its interior will experience an electro-motive force according to Faraday’s law. Then the eddy currents are generated to heat the materials by Joule’s law. Besides, magnetic domain rotation will also produce hysteresis heating when applied to magnetic materials.Bituminous materials themselves cannot be heated directly by induction; some electrically conductive materials (like steel fibres, steel wool, steel slag, etc.) are considered to be added to asphalt mixtures [14][15]. After the conductive material heats up under an induction field, it can be conducted to the bitumen to heat up and heal the cracks [16]. The basic principle is shown in Figure 3. In Garcia et al.’s study, steel wool fibres were added to dense asphalt mixtures. The results show that a higher volume of steel wool fibres in the mixture may increase the air void content of asphalt concrete and affect its thermal conductivity [17]. When Liu et al. incorporated steel fibres, steel wool, and steel slag into porous asphalt concrete, it was found that the conductivity of samples with longer fibres with a smaller diameter was better than that of samples with shorter fibres with a larger diameter [18]. And the steel fibres and steel wool were more beneficial in increasing temperature than steel slag; they also improved the flexural strength of asphalt concrete [19]. 8% steel wool is considered the optimal content and increases the indirect tensile strength, resilient stiffness, and fatigue resistance of porous asphalt concrete [20]. An appropriate amount of steel fibres can increase the basic mechanical properties of asphalt concrete while also increasing its thermal properties.
Figure 3. Induction heating scheme.
Induction crack healing technology is mainly used to increase the temperature of asphalt concrete and reduce the viscosity of asphalt to promote crack healing. Temperature is the main index used to determine the crack healing rate [21]. Liu et al. believed that 85 °C was the optimal surface temperature for crack healing through a three-point bending test and that the optimal strength recovery rate could reach 78.8% [22]. Liu et al. designed the four-point blending test to investigate the fatigue life extension of asphalt concrete with steel fibres. Micro-strain amplitudes would affect the size of cracks between samples of the test. Higher micro-strain amplitudes and larger cracks were generated in the fatigue testing, which is hard to heal. Liu et al. found that the fatigue life extension ratio during different micro-strains and temperatures for hot mix asphalt and warm asphalt shows that induction heating technology can expand over 70% of the life by healing the crack [23][24]. Another advantage of induction heating technology is that the asphalt pavement can be heated multiple times during its service life. The strength recovery rate and fatigue life extension of asphalt concrete containing steel fibres are still unchanged after 5 cycles of induction heating [25][26]. Yang et al. also studied the induction heating crack healing level of asphalt concrete containing reclaimed asphalt pavement (RAP) and steel slag. The strength healing rate of RAP containing 40% can still reach 57.9%. At the same time, the crack healing rate will decrease by 10% after four cycles [27][28]. In December 2010 in the Netherlands, the first induction-heating asphalt pavement was paved [26], and it has been applied until now and remained well. In June 2014, this trial section received the first induction heating treatment, and it showed good healing ratios and ravelling resistance [29]. In 2018, in the Guangdong Province of China, a 400-metre induction healing pavement test section was also paved [30]. According to estimates, if all roads in the Netherlands were replaced with induction-heated pavements, it could save approximately 90 million euros every year, and the life span of roads would also extend by 50%. By the same calculation, China will save a maintenance expense of 1000 billion RMB if only 10% of the roads are replaced by induction healing pavemeng [20]. However, induction heating technology cannot prevent the ageing of asphalt pavement. And the pavement will be more and more prone to cracks, and the healing temperature will be higher than ever during the service process. The total mixing time should reach 5 min to get a homogeneous mix with minimum steel wool clusters. It is six times more than when normal asphalt pavement is applied [20]. And the heating efficiency is also limited; one hour can only heat 5 km since it takes 26.4 s for the temperature of the road surface to increase from 5 to 85 °C [31]. Large-scale induction equipment also requires further study in order to guarantee heating rates and maintenance times.

3.2. Microwave Heating

Microwave heating is also a good non-contact heating method used in road surface heating. The basic principle is that the direction of the electric polarity molecules in the object will vibrate with the oscillating electric field, and the inherent electromagnetic field of a molecule is changed and affects the adjacent molecules, so the vibration of the molecule is in the molecule passed between under the action of the electromagnetic field oscillated by microwave high frequency. Molecular vibration is internal energy, and increasing internal energy is like heating an object [32]. Microwaves cannot heat non-polar molecules. Bitumen contains a large number of polar molecules. And Lou et al. reported that microwave heating rarely aged asphalt, referring to the ageing index [33]. The mechanism of crack healing is the same as induction heating after the mixture is heated [34]. Researchers found that the incorporation of some additives can improve microwave heating effectiveness. Gallego et al. reported that 0.2% steel wool can significantly improve microwave heating potential, whereas only 1/10 dosage for induction heating can reach the same heat rate [35]. Li et al. found that nanometer microwave-absorber materials (like SiC, CNTs, and graphene) can also improve the microwave heating rate and healing properties of asphalt [36][37]. Sun et al. studied the heating and healing properties of a mixture incorporating steel slag and steel fibres using both induction and microwave technologies [38]. Lou et al. used three kinds of steel slag (hot braised, hot pour, and iron slag) to replace the coarse aggregates in the asphalt mixture and found that the microwave heating rate could improve. And 60% replacement is the most effective dosage [39]. Lou et al. also used ferrite fillers to replace limestone fillers in a mixture that incorporated steel slag, and the microwave heating rate was further improved [40]. Metallic powder and fly ash can also improve the microwave heating potential of asphalt [41][42]. In the Jahanbakhsh et al. study, carbon black increased the heating rate of asphalt pavement made of limestone and siliceous types of aggregate by 47% and 25%, respectively [43]. Wang et al. also found that pyrolysis carbon black (PCB) had good microwave absorbing performance for asphalt pavement. And the addition of 15% PCB increased the self-healing rate of bitumen by 3.59 times [44]. At present, the microwave heating cracking technology in the laboratory mainly relies on microwave ovens. The heating time and temperature are the biggest factors affecting the crack healing rate of asphalt concrete. Jose et al. comparatively studied the microwave and induction heating, the microwave healing rate of dense asphalt mixtures was superior to the induction healing rate through three-point bending test, the strength recover rate reached 93% for microwave healing, while 75% for induction heating. This is mainly because microwave heating is a holistic heating, while induction heating has a temperature gradient from top to bottom, and the bottom crack does not reach the optimal level of healing [45]. Zhu et al. investigated healing level of asphalt concrete with base bitumen and SBS modified bitumen in different temperature by semicircular bending test, it was found that the strength recover ratio could reach 85% in 80 °C [46]. The microwave heating healing ratios of asphalt mixtures with different structure (semi-dense, porous, and gap-graded) were investigated in Franesqui et al. study. It was found that top-down cracks (<4–5 mm)can be completely healed by microwave heating [41]. Crack healing level of asphalt concrete containing RAP was also investigated by microwave heating, the RAP content adversely affected the microwave healing [47]. Nevertheless, there are obvious disadvantages to microwave heating technology. It is challenging to control the microwave’s reflection from the flat surfaces. And the human body can also absorb microwave energy, which can heat exposed tissues and cause thermal damage [48]. Therefore, further extensive research needs to be conducted to enhance the efficiency of microwave healing on asphalt pavements while ensuring safety is not compromised.In heating technology, conductive materials (steel fibres and steel slag) or absorbing microwave materials (ferrite, SiC, CNTs, graphene, fly ash, and carbon black) that are added to asphalt concrete basically belong to the waste products of other industries. Specifically, steel fibres and ferrite come from waste from the steel cutting and forging industries. Steel slag is a waste product after steelmaking [49]. Reusing asphalt concrete can turn waste into treasure, make full use of resources, reduce the capture of new resources, and be more sustainable.

4. Agents Encapsulated Technology

The agent-encapsulated technology solves the shortcomings of the spraying rejuvenator, such as difficult penetration and uneven distribution. Rejuvenating aged asphalt pavement when the aging starts to result in cracking is the optimal solution. This will be the most effective way to prolong the life of the road. It is crucial to avoid prematurely releasing the rejuvenator before the bitumen has been aged, which will reduce the permanent deformation resistance of the road [50].

4.1. Saturated Porous Aggregates Encapsulate Rejuvenators

Garcia et al. first proposed the asphalt self-healing technology with capsules by applying self-healing capsules to cementitious materials [51]. The porous sand is used as the core material, and its internal porous structure can effectively store the rejuvenator. Then, the surface is coated with epoxy resin and cement as a shell. The capsules of various sizes (with diameters ranging from 1.6 to 7.1 mm and shell thicknesses ranging from 0.1 to 0.35 mm) were produced by the same procedure. It is found that larger capsule cores contain more oil, and their force resistance is over 10 N in capsule compression tests [52][53]. The saturated porous aggregate capsules were added to porous asphalt concrete and could resist high temperatures (up to 180 °C) and tension during the mixing and compaction of the asphalt mixture [53]. It was found that the capsules inside the porous concrete could break and the oil could flow out and diffuse into bitumen after the indirect tensile test, and the crack could be effectively healed, as shown in Figure 4 [54]. However, the capsules were unevenly distributed in the asphalt mixture. They tended to accumulate at a certain depth in the test sample. The capsules decrease the indirect tensile strength of asphalt concrete. This happened because its strength is lower than normal aggregates [54]. Oil in the capsule is also extremely limited owing to the fact that most holes in the porous aggregates are closed. This kind of capsule is not particularly suitable for asphalt concrete to improve its self-healing ability.
Figure 4. Characterization and healing process of saturated porous aggregates encapsulate rejuvenators [54].

4.2. Core-Shell Polymeric Microcapsules

Core-shell polymeric microcapsules involve two primary components: the core material (rejuvenators) and the shell materials [55]. These capsules are categorised based on their size as nano-capsules (1 m), micro-capsules (1 m < D < 1000 m), and macro-capsules (>1000 m) [56]. The section focuses mainly on the application of microcapsules in asphalt crack healing. The core material may be surrounded by one or two layers of shell materials. There are two types of core-shell capsules: (1) single-shell capsules [57] and (2) double-shell capsules [58]. Through in-situ polymerization and two-step coacervation processes, a type of core-shell microcapsule was created, which significantly reduced the size of encapsulated rejuvenators and improved their incorporation into bituminous materials [59]. These microcapsules consist of a rejuvenator core surrounded by a protective shell, which can be ruptured by propagating crack fronts, allowing for the release of the healing agent through capillary action. TGA tests have indicated that these microcapsules can withstand the storage and mixing temperatures of bitumen [60]. Sun et al. have demonstrated that they can resist mechanical agitation at high temperatures while still being able to release the rejuvenator during loading, thereby enhancing the healing capacity of aged bitumen [61]. Furthermore, fatigue-rest-fatigue tests have shown that the inclusion of microcapsules containing rejuvenator can enhance the fatigue resistance of aged asphalt binder, with a 1 wt% concentration resulting in a 45.68% increase in fatigue life compared to non-aged neat bitumen [57]. At the same time, a commercial prepolymer of melamine-formaldehyde modified by methanol (MMF) was also developed as the shell material of microcapsules [58][59][62][63]. Its SEM images are shown in Figure 5. Thermal tests showed that the microcapsules survived in 200 °C bitumen and could improve the self-healing ability of bitumen with the capsules [64]. Moreover, nano-CaCO3 powder was added to MMF as the shell to enhance adhesion with bitumen and thermal stability; these nano-CaCO3/polymer microcapsules survived in bitumen for a long service time under radical conditions without damage because of their good thermal stability [63].
Figure 5. SEM images of core–shell microcapsules: (a) external aspect, and (b,c) cross section of the microcapsules [58].
However, the capsule does have its limitations. Its preparation efficiency in the laboratory is relatively low, and the quantity of each preparation is limited, making it challenging to use on a large scale in road engineering. Additionally, there have been no experiments conducted on adding it to the asphalt mixtures; it is only added to binders. It is difficult to prove that it can also keep itself whole without breaking during mixing and compression. As the capsule has a single core, once it ruptures, all the rejuvenators inside are released completely, which could potentially reduce the asphalt concrete’s resistance to permanent deformation.

4.3. Ca-Alginate Capsule

Calcium alginate capsules are prepared by dripping the emulsion containing sodium alginate, surfactant, and regenerant into calcium chloride solution. The shell material of the capsule is to fix the chain alginate ions into a three-dimensional network of calcium alginate material by the method of ion replacement. Therefore, the rejuvenator can be stored in the gaps of the network structure [65]. Rao et al. also innovated the experimental apparatus and successfully fabricated the capsules with industrial raw materials on a large scale in the laboratory [66]. The size of capsules is typically 1.5–3 mm, and the capsule is incorporated into the asphalt concrete as an aggregate. Its internal structure is a multi-chamber structure [67], which enables multiple releases of the internal rejuvenator for long-term crack healing, as shown in Figure 6.
Figure 6. Morphological characterization of calcium alginate capsules.
This capsule healing technology uses an internal rejuvenator to soften the asphalt on the crack interface, reduce its surface energy, increase the flow activation energy of the asphalt, and promote crack healing. It is generally believed that there are two release mechanisms for the rejuvenator inside the calcium alginate capsule. The first one is the same as the core-shell capsule. The crack or loading induces the capsule to rupture and releases the rejuvenator inside, which can effectively heal the crack. Because the damaged capsules embedded in asphalt mixtures can be found by CT scan [68][69], as shown in Figure 7, The other is elastic contraction and expansion. Since the chambers inside the capsule are not all closed, under the action of the load, the capsules are deformed by pressure, the internal rejuvenator will flow out, and the capsule does not rupture. The release method could rejuvenate aged bitumen and improve its own self-healing capability [70]. The researchers studied the mechanical and thermal properties of the capsule itself. The uniaxial compression test to make capsules break is usually used to measure the mechanical strength of capsules. It was proved that the capsules could resist the pressure during mixing and compressive forces when the strength was higher than 10 N [51][71]. Zhang et al., Wan et al., Xu et al., Micaelo et al., Al-Mansoori et al., and Norambuena-Contreras et al. tested the strength of this capsule at different temperatures; the results ranged from 12–33 N [68][72][73][74][75]. By thermal gravimetric analysis (TGA), the capsules had a mass loss of 2.9–4% at 200 °C and 3.8–5.5% at 160 °C [68][72][73][74][75]. The rejuvenator content of the capsule weight could also be calculated by the thermogravimetric curve; it ranged from 52–80% [68][72][73][74][75]. It can be seen that the capsule can fully survive the mixing and compression of asphalt concrete.
Sustainability 15 09659 g007 550
Figure 7. CT-Scans reconstructions of the asphalt mixture with capsules, (a) sectional view, (b) broken capsules in mixtures, (c) 3D image [71].
More importantly, this capsule can effectively increase the crack healing ability of asphalt concrete in low temperature. Al-Mansoori et al. found that the capsules can effect the healing levels of samples when the healing temperature below 40 °C, asphalt samples with and without capsules owned same healing levels when temperature was over 40 °C by fracture- rest-healing-refracture test [73]. Zhang et al. found that the strength recovery ratio and fracture energy recovery ratio of asphalt with capsules could reach 92.7% and 180.2% respectively, while the reference samples are 61% and 31.5%, shown in Figure 8. The capsule also significantly improve the healing capability of porous asphalt concrete by semi-circular bending (SCB) test by Xu et al. [76]. The self-healing property of reflective crack of asphalt mixtures with capsules was investigated in Garcia-Hernández et al. study. It was found that the capsules had the best self-healing efficiency in porous asphalt concrete, then stone mastic asphalt mixture, the last one dense asphalt mixture [77]. Sustainability 15 09659 g008 550
/media/item_content/202306/6490ebcc0548asustainability-15-09659-g008.png
Figure 8. Recovery ratio of asphalt mixture with and without capsules: (a) strength, (b) fracture energy [65].

4.4. Hollow Fibers

Hollow fibres are used to provide a healing mechanism similar to that of encapsulated rejuvenators. Rejuvenators are encapsulated in the connected hollow pipe. And this method offers an advantage over capsule-based systems because the fibres increase the probability that rejuvenator will be released into cracks, which are more likely to pass through the fibre network [78]. Furthermore, the continuous pipe structure of the hollow system allows for the continuous supply of large volumes of rejuvenators, and the diameter of the fibres is usually 0.5–1.5 mm [79]. Zhang et al. prepared polyvinylidene fluoride resin (PVDF) hollow fibres by a one-step wet-spinning technology; the process is shown in Figure 9. They are distributed evenly in the bitumen base material and aim to reverse the ageing of bitumen and improve its crack repair capability [80]. The fibres were added to aged bitumen and still kept their integrality state by XCT test, proving they can resist the thermal actions of temperature changes in bitumen. Hollow fibres can survive in bitumen safely without debonding [79]. 
Sustainability 15 09659 g009 550
Figure 9. Schematic representation of the preparation of vascular hollow fibers and finished product: (a) fiber without rejuvenator, (b) fiber with rejuvenator, (c,d) cross-sectional of fiber with and without rejuvenator [79].

4.5. Compartment Fibers

Compartment fibres have their own advantages over hollow fibres. It does not allow the full release of the internal rejuvenator at one point of fracture, causing excessive local softening. Because the internal rejuvenator is separated into small droplets in the fibre. Its self-healing mechanism can be viewed as a merger of capsules and fibres.Tabakovi et al. used the physico-mechanical technique of wet-spinning to prepare the calcium alginate compartment fibres. The fibres have good thermal and mechanical properties because they still maintain their integrity after heating and mixing with bitumen [81]. These fibres present the rejuvenator distributed as individual droplets along their axis. The results demonstrated that the mechanical strength of mastic asphalt with fibres can increase by 36% compared to the reference, and the local micro-crack healing ability of samples with fibre also increases.After that, a microfluidic device was used to produce compartmented fibres with a commercial rejuvenator as a core and a sodium-alginate solution as a shell in Shu et al.’s study; the process is shown in Figure 10. The shell of fibres has excellent thermal stability and mechanical properties. The fibres were still intact after mixing and compacting with asphalt. The self-healing ratio of asphalt mix containing fibres increased by nearly 32% compared to asphalt mix without fibres. The system worked and enhanced the self-healing properties of the asphalt mixture [82][83]. In agent-encapsulated technologies, although the shell materials (epoxy resin, MF, MMF, Ca-alginate, and PVDF) used are all organic matter, they are basically non-toxic and will not flow into the environment and cause pollution when mixed into the asphalt. The core materials (commercial rejuvenator, sunflower oil, and waste oil) used are non-toxic and environment-friendly and will be part of bitumen, which can be recycled. This further advances the sustainability of asphalt pavement.
Sustainability 15 09659 g010 550
Figure 10. Microfluid synthetics compartment fibers and its morphology image, (a) optical microscope, (b) fluorescence microscope [82].

5. Other Technologies

There are also other technologies under study to help repair cracks in asphalt pavement. The comprehensive application of heating technology and rejuvenator supply technology is considered to overcome the shortcomings of their separate use. Xu et al. added both steel fibres and calcium alginate capsules to porous asphalt mixtures. The induction heating not only repairs cracks but also accelerates the outflow of the rejuvenators in the capsule and the diffusion in the bitumen [84]. Wan et al. design novel Ca-alginate capsules containing Fe3O4 powder, which can be induced to be heated to damage the shell of the capsules, leading to the rejuvenator’s release by the low-frequency (2.45 GHz) microwave. So the capsule can achieve an artificially controlled release time [75][85][86]. Electrically conductive asphalt pavements are also designed to heal cracks in asphalt pavements by adding nanostructured conductive polymers, although asphalt is not electrically conductive [87]. At the crack, the resistance of the conductive asphalt will increase, and the temperature will also increase to heal cracks, according to Joule’s law [88]. Three-dimensional printing technologies can also be applied for the maintenance of asphalt pavement cracks. Firstly, building 3D digital models of cracks by an advanced pavement distress detection system, then printing the crack directly in situ with prepared printing materials and equipment, and finally, checking printing quality by ultrasonic testing [89]. Jackson et al. realise bitumen can be directly used as a printing material to print into the cracks in the road surface to repair cracks at high temperatures to prolong the life of asphalt pavement [90]. Bitumen modified by polymer (SBS, Gilsonite, HDPE and crumb rubber in Lv et al. [91], SBS, HDPE and crumb rubber in Zhou et al. [92] crumb rubber, PPA, PE and gilsonite in Huang et al. [93]), nanomaterials (organoclay in Tabatabaee et al. [94], nano-silica in Ganjei et al. [95]), ionomers [96] and shape memory materials [97] to increasing the self-healing properties of bitumen itself can also improve the crack healing ability of the asphalt pavement.

References

  1. Chen, Y.P. Discussion on the Maintenance and Repair Technology of Asphalt Pavement Crack and Pit. J. Guangdong Commun. Polytech. 2016, 15–17.
  2. Tan, Y.; Liu, Y.; Zhou, M.; Wang, Z.; Ping, Y. Crack mechanism and prevention measures of concrete in the initial pouring based on field temperature gradient experiment. IOP Conf. Ser. Earth Environ. Sci. 2018, 153, 052021.
  3. Praticò, F.G.; Vaiana, R.; Iuele, T. Macrotexture modeling and experimental validation for pavement surface treatments. Constr. Build. Mater. 2015, 95, 658–666.
  4. Im, J.H.; Kim, Y.R. Methods for fog seal field test with polymer-modified emulsions: Development and performance evaluation. Transp. Res. Rec. 2013, 2361, 88–97.
  5. Xu, L.; Zhao, Z.; Li, X.; Yuan, J.; Zhou, Q.; Xiao, F. Cracking investigation on fog seal technology with waterborne acrylate and polyurethane as a clean modification approach. J. Clean. Prod. 2021, 329, 129751.
  6. Islam, R.M.; Arafat, S.; Wasiuddin, N.M. Quantification of reduction in hydraulic conductivity and skid resistance caused by fog seal in low-volume roads. Transp. Res. Rec. 2017, 2657, 99–108.
  7. Hou, X.; Xiao, F.; Guo, R.; Xiang, Q.; Wang, T.; Wang, J. Application of spectrophotometry on detecting asphalt content of emulsified asphalt. J. Clean. Prod. 2019, 215, 626–633.
  8. Liu, F.; Zheng, M.; Liu, X.; Ding, X.; Wang, F.; Wang, Q. Performance evaluation of waterborne epoxy resin-SBR composite modified emulsified asphalt fog seal. Constr. Build. Mater. 2021, 301, 124106.
  9. Ma, Z.; Wang, H.; Hui, B.; Jelagin, D.; You, Z.; Feng, P. Optimal design of fresh sand fog seal mortar using response surface methodology (RSM): Towards to its workability and rheological properties. Constr. Build. Mater. 2022, 340, 127638.
  10. Zhang, X.; Wang, H.; Hasan, M.R.M.; Gao, J.; Irfan, M. Traffic open time prediction of fog seal with sand using image processing technology. Constr. Build. Mater. 2019, 209, 9–19.
  11. Hager, M.D.; Greil, P.; Leyens, C.; van der Zwaag, S.; Schubert, U.S. Self-healing materials. Adv. Mater. 2010, 22, 5424–5430.
  12. Tang, J.; Liu, Q.; Wu, S.; Ye, Q.; Sun, Y.; Schlangen, E. Investigation of the optimal self-healing temperatures and healing time of asphalt binders. Constr. Build. Mater. 2016, 113, 1029–1033.
  13. Sun, Y.; Wu, S.; Liu, Q.; Hu, J.; Yuan, Y.; Ye, Q. Snow and ice melting properties of self-healing asphalt mixtures with induction heating and microwave heating. Appl. Therm. Eng. 2018, 129, 871–883.
  14. Yoo, D.-Y.; Kim, S.; Kim, M.-J.; Kim, D.; Shin, H.-O. Self-healing capability of asphalt concrete with carbon-based materials. J. Mater. Res. Technol. 2019, 8, 827–839.
  15. Vila-Cortavitarte, M.; Jato-Espino, D.; Castro-Fresno, D.; Calzada-Pérez, M.Á. Self-healing capacity of asphalt mixtures including by-products both as aggregates and heating inductors. Materials 2018, 11, 800.
  16. García, Á.; Schlangen, E.; van de Ven, M.; Liu, Q. Electrical conductivity of asphalt mortar containing conductive fibers and fillers. Constr. Build. Mater. 2009, 23, 3175–3181.
  17. García, A.; Norambuena-Contreras, J.; Partl, M.N. Experimental evaluation of dense asphalt concrete properties for induction heating purposes. Constr. Build. Mater. 2013, 46, 48–54.
  18. Liu, Q.; Schlangen, E.; van de Ven, M.; Poot, M. Optimization of Steel Fiber Used for Induction Heating in Porous Asphalt Concrete. Traffic Transp. Stud. 2010, 2010, 1320–1330.
  19. Liu, Q.; Wu, S.; Schlangen, E. Induction heating of asphalt mastic for crack control. Constr. Build. Mater. 2013, 41, 345–351.
  20. Liu, Q. Induction Healing of Porous Asphalt Concrete. Ph.D. Thesis, Delft University of Technology, Delft, The Netherlands, 2012.
  21. Garcia, A.; Schlangen, E.; Van de Ven, M. Key Engineering Materials; Trans Tech Publications: Stafa-Zurich, Switzerland, 2023; pp. 573–576.
  22. Liu, Q.; Schlangen, E.; van de Ven, M. Induction healing of porous asphalt concrete beams on an elastic foundation. J. Mater. Civ. Eng. 2013, 25, 880–885.
  23. Liu, Q.; Yu, W.; Wu, S.; Schlangen, E.; Pan, P. A comparative study of the induction healing behaviors of hot and warm mix asphalt. Constr. Build. Mater. 2017, 144, 663–670.
  24. Liu, Q.; Schlangen, E.; van de Ven, M.; van Bochove, G.; van Montfort, J. Evaluation of the induction healing effect of porous asphalt concrete through four point bending fatigue test. Constr. Build. Mater. 2012, 29, 403–409.
  25. Liu, Q.; García, Á.; Schlangen, E.; van de Ven, M. Induction healing of asphalt mastic and porous asphalt concrete. Constr. Build. Mater. 2011, 25, 3746–3752.
  26. Liu, Q.; Schlangen, E.; van de Ven, M. Induction Healing of Porous Asphalt. Transp. Res. Rec. J. Transp. Res. Board 2012, 2305, 95–101.
  27. Yang, C.; Wu, S.; Xie, J.; Amirkhanian, S.; Liu, Q.; Zhang, J.; Xiao, Y.; Zhao, Z.; Xu, H.; Li, N.; et al. Enhanced induction heating and self-healing performance of recycled asphalt mixtures by incorporating steel slag. J. Clean. Prod. 2022, 366, 132999.
  28. Yang, C.; Xie, J.; Wu, S.; Amirkhanian, S.; Wang, Z.; Song, J.; Zou, X.; Wang, F.; Zhang, L. Enhancement mechanism of induction heating on blending efficiency of RAP-virgin asphalt in steel slag recycled asphalt mixtures. Constr. Build. Mater. 2021, 269, 121318.
  29. Xu, S.; García, A.; Su, J.; Liu, Q.; Tabaković, A.; Schlangen, E. Self-Healing Asphalt Review: From Idea to Practice. Adv. Mater. Interfaces 2018, 5, 1800536.
  30. Jiang, Q.; Wang, F.; Liu, Q.; Xie, J.; Wu, S. Energy Consumption and Environment Performance Analysis of Induction-Healed Asphalt Pavement by Life Cycle Assessment (LCA). Materials 2021, 14, 1244.
  31. Van Bochove, G. Self Healing Asphalt-extending the service life by induction heating of asphalt. In Proceedings of the 6th Eurasphalt & Eurobitume Congress, Prague, Czech Republic, 1–3 June 2016.
  32. Wang, F.; Zhu, H.; Shu, B.; Li, Y.; Gu, D.; Gao, Y.; Li, C. Microwave heating mechanism and self-healing performance of asphalt mixture with basalt and limestone aggregates. Constr. Build. Mater. 2022, 342, 127973.
  33. Lou, B.; Sha, A.; Barbieri, D.M.; Zhang, X.; Chen, H.; Hoff, I. Evaluation of microwave aging impact on asphalt mixtures. Road Mater. Pavement Des. 2023, 24, 730–743.
  34. Norambuena-Contreras, J.; Gonzalez-Torre, I. Influence of the microwave heating time on the self-healing properties of asphalt mixtures. Appl. Sci. 2017, 7, 1076.
  35. Gallego, J.; del Val, M.A.; Contreras, V.; Páez, A. Heating asphalt mixtures with microwaves to promote self-healing. Constr. Build. Mater. 2013, 42, 1–4.
  36. Li, C.; Wu, S.; Chen, Z.; Tao, G.; Xiao, Y. Improved microwave heating and healing properties of bitumen by using nanometer microwave-absorbers. Constr. Build. Mater. 2018, 189, 757–767.
  37. Li, C.; Wu, S.; Shu, B.; Li, Y.; Chen, Z. Microwave absorption and anti-aging properties of modified bitumen contained SiC attached layered double hydroxides. Constr. Build. Mater. 2019, 227, 116714.
  38. Sun, Y.; Wu, S.; Liu, Q.; Zeng, W.; Chen, Z.; Ye, Q.; Pan, P. Self-healing performance of asphalt mixtures through heating fibers or aggregate. Constr. Build. Mater. 2017, 150, 673–680.
  39. Lou, B.; Sha, A.; Li, Y.; Wang, W.; Liu, Z.; Jiang, W.; Cui, X. Effect of metallic-waste aggregates on microwave self-healing performances of asphalt mixtures. Constr. Build. Mater. 2020, 246, 118510.
  40. Lou, B.; Sha, A.; Barbieri, D.M.; Liu, Z.; Zhang, F.; Jiang, W. Improved microwave heating uniformity and self-healing properties of steel slag asphalt containing ferrite filler. Mater. Struct. 2021, 54, 1–14.
  41. Franesqui, M.A.; Yepes, J.; García-González, C. Top-down cracking self-healing of asphalt pavements with steel filler from industrial waste applying microwaves. Constr. Build. Mater. 2017, 149, 612–620.
  42. Atakan, M.; Yıldız, K. Improving Microwave Heating Characteristic of Asphalt Binder by Using Fly Ash. In Proceedings of the ISBS 2019—4th International Sustainable Buildings Symposium, Dallas, TX, USA, 18–20 July 2019.
  43. Jahanbakhsh, H.; Karimi, M.M.; Jahangiri, B.; Nejad, F.M. Induction heating and healing of carbon black modified asphalt concrete under microwave radiation. Constr. Build. Mater. 2018, 174, 656–666.
  44. Wang, F.; Zhu, H.; Li, Y.; Gu, D.; Gao, Y.; Feng, J.; Xu, Z. Microwave heating mechanism and Self-healing performance of scrap tire pyrolysis carbon black modified bitumen. Constr. Build. Mater. 2022, 341, 127873.
  45. Norambuena-Contreras, J.; Garcia, A. Self-healing of asphalt mixture by microwave and induction heating. Mater. Des. 2016, 106, 404–414.
  46. Zhu, H.; Yuan, H.; Liu, Y.; Fan, S.; Ding, Y. Evaluation of self-healing performance of asphalt concrete for macrocracks via microwave heating. J. Mater. Civ. Eng. 2020, 32, 04020248.
  47. González, A.; Norambuena-Contreras, J.; Storey, L.; Schlangen, E. Effect of RAP and fibers addition on asphalt mixtures with self-healing properties gained by microwave radiation heating. Constr. Build. Mater. 2018, 159, 164–174.
  48. Gulisano, F.; Gallego, J. Microwave heating of asphalt paving materials: Principles, current status and next steps. Constr. Build. Mater. 2021, 278, 121993.
  49. Yi, H.; Xu, G.; Cheng, H.; Wang, J.; Wan, Y.; Chen, H. An overview of utilization of steel slag. Procedia Environ. Sci. 2012, 16, 791–801.
  50. Zhang, L.; Hoff, I.; Zhang, X.; Yang, C. Investigation of the self-healing and rejuvenating properties of aged asphalt mixture containing multi-cavity Ca-alginate capsules. Constr. Build. Mater. 2022, 361, 129685.
  51. García, Á.; Schlangen, E.; van de Ven, M.; Sierra-Beltrán, G. Preparation of capsules containing rejuvenators for their use in asphalt concrete. J. Hazard. Mater. 2010, 184, 603–611.
  52. García, Á.; Schlangen, E.; Van de Ven, M. Properties of capsules containing rejuvenators for their use in asphalt concrete. Fuel 2011, 90, 583–591.
  53. Garcia, A.; Austin, C.J.; Jelfs, J. Mechanical properties of asphalt mixture containing sunflower oil capsules. J. Clean. Prod. 2016, 118, 124–132.
  54. Garcia, A.; Jelfs, J.; Austin, C.J. Internal asphalt mixture rejuvenation using capsules. Constr. Build. Mater. 2015, 101, 309–316.
  55. Jyothi, N.V.N.; Prasanna, P.M.; Sakarkar, S.N.; Prabha, K.S.; Ramaiah, P.S.; Srawan, G.Y. Microencapsulation techniques, factors influencing encapsulation efficiency. J. Microencapsul. 2010, 27, 187–197.
  56. Whelehan, M.; Marison, I.W. Microencapsulation using vibrating technology. J. Microencapsul. 2011, 28, 669–688.
  57. Sun, D.; Li, B.; Tian, Y.; Lu, T.; Zhu, X.; Sun, G.; Gilabert, F. Aided regeneration system of aged asphalt binder based on microcapsule technology. Constr. Build. Mater. 2019, 201, 571–579.
  58. Su, J.-F.; Qiu, J.; Schlangen, E.; Wang, Y.-Y. Investigation the possibility of a new approach of using microcapsules containing waste cooking oil: In situ rejuvenation for aged bitumen. Constr. Build. Mater. 2015, 74, 83–92.
  59. Su, J.-F.; Schlangen, E. Synthesis and physicochemical properties of high compact microcapsules containing rejuvenator applied in asphalt. Chem. Eng. J. 2012, 198, 289–300.
  60. Sun, D.; Hu, J.; Zhu, X. Size optimization and self-healing evaluation of microcapsules in asphalt binder. Colloid Polym. Sci. 2015, 293, 3505–3516.
  61. Sun, D.; Li, B.; Ye, F.; Zhu, X.; Lu, T.; Tian, Y. Fatigue behavior of microcapsule-induced self-healing asphalt concrete. J. Clean. Prod. 2018, 188, 466–476.
  62. Su, J.; Wang, Y.; Yang, P.; Han, S.; Han, N.; Li, W. Evaluating and modeling the internal diffusion behaviors of microencapsulated rejuvenator in aged bitumen by FTIR-ATR tests. Materials 2016, 9, 932.
  63. Wang, Y.-Y.; Su, J.; Schlangen, E.; Han, N.; Han, S.; Li, W. Fabrication and characterization of self-healing microcapsules containing bituminous rejuvenator by a nano-inorganic/organic hybrid method. Constr. Build. Mater. 2016, 121, 471–482.
  64. Su, J.-F.; Schlangen, E.; Qiu, J. Design and construction of microcapsules containing rejuvenator for asphalt. Powder Technol. 2013, 235, 563–571.
  65. Zhang, L.; Liu, Q.; Li, H.; Norambuena-Contreras, J.; Wu, S.; Bao, S.; Shu, B. Synthesis and characterization of multi-cavity Ca-alginate capsules used for self-healing in asphalt mixtures. Constr. Build. Mater. 2019, 211, 298–307.
  66. Rao, W.; Liu, Q.; Yu, X.; Wan, P.; Wang, H.; Song, J.; Ye, Q. Efficient preparation and characterization of calcium alginate-attapulgite composite capsules for asphalt self-healing. Constr. Build. Mater. 2021, 299, 123931.
  67. Norambuena-Contreras, J.; Liu, Q.; Zhang, L.; Wu, S.; Yalcin, E.; Garcia, A. Influence of encapsulated sunflower oil on the mechanical and self-healing properties of dense-graded asphalt mixtures. Mater. Struct. 2019, 52, 1–13.
  68. Micaelo, R.; Al-Mansoori, T.; Garcia, A. Study of the mechanical properties and self-healing ability of asphalt mixture containing calcium-alginate capsules. Constr. Build. Mater. 2016, 123, 734–744.
  69. Xu, S.; Tabaković, A.; Liu, X.; Schlangen, E. Calcium alginate capsules encapsulating rejuvenator as healing system for asphalt mastic. Constr. Build. Mater. 2018, 169, 379–387.
  70. Wan, P.; Wu, S.; Liu, Q.; Zou, Y.; Zhao, Z.; Chen, S. Recent advances in calcium alginate hydrogels encapsulating rejuvenator for asphalt self-healing. J. Road Eng. 2022, 2, 181–220.
  71. Norambuena-Contreras, J.; Yalcin, E.; Garcia, A.; Al-Mansoori, T.; Yilmaz, M.; Hudson-Griffiths, R. Effect of mixing and ageing on the mechanical and self-healing properties of asphalt mixtures containing polymeric capsules. Constr. Build. Mater. 2018, 175, 254–266.
  72. Bao, S.; Liu, Q.; Rao, W.; Yu, X.; Zhang, L. Synthesis and characterization of calcium alginate-attapulgite composite capsules for long term asphalt self-healing. Constr. Build. Mater. 2020, 265, 120779.
  73. Al-Mansoori, T.; Norambuena-Contreras, J.; Garcia, A. Effect of capsule addition and healing temperature on the self-healing potential of asphalt mixtures. Mater. Struct. 2018, 51, 1–12.
  74. Norambuena-Contreras, J.; Yalcin, E.; Hudson-Griffiths, R.; García, A. Mechanical and self-healing properties of stone mastic asphalt containing encapsulated rejuvenators. J. Mater. Civ. Eng. 2019, 31, 04019052.
  75. Wan, P.; Liu, Q.; Wu, S.; Zhao, Z.; Chen, S.; Zou, Y.; Yu, X. A novel microwave induced oil release pattern of calcium alginate/nano-Fe3O4 composite capsules for asphalt self-healing. J. Clean. Prod. 2021, 297, 126721.
  76. Xu, S.; Liu, X.; Tabaković, A.; Schlangen, E. Investigation of the potential use of calcium alginate capsules for self-healing in porous asphalt concrete. Materials 2019, 12, 168.
  77. Garcia-Hernández, A.; Salih, S.; Ruiz-Riancho, I.; Norambuena-Contreras, J.; Hudson-Griffiths, R.; Gomez-Meijide, B. Self-healing of reflective cracks in asphalt mixtures by the action of encapsulated agents. Constr. Build. Mater. 2020, 252, 118929.
  78. Toohey, K.S.; Sottos, N.R.; Lewis, J.A.; Moore, J.S.; White, S.R. Self-healing materials with microvascular networks. Nat. Mater. 2007, 6, 581–585.
  79. Su, J.-F.; Zhang, X.; Guo, Y.; Wang, X.; Li, F.; Fang, Y.; Han, N. Experimental observation of the vascular self-healing hollow fibers containing rejuvenator states in bitumen. Constr. Build. Mater. 2019, 201, 715–727.
  80. Zhang, X.-L.; Su, J.; Guo, Y.; Wang, X.; Fang, Y.; Ding, Z.; Han, N. Novel vascular self-nourishing and self-healing hollow fibers containing oily rejuvenator for bitumen. Constr. Build. Mater. 2018, 183, 150–162.
  81. Tabaković, A.; Post, W.; Cantero, D.; Copuroglu, O.; Garcia, S.J.; Schlangen, E. The reinforcement and healing of asphalt mastic mixtures by rejuvenator encapsulation in alginate compartmented fibres. Smart Mater. Struct. 2016, 25, 084003.
  82. Shu, B.; Zhang, L.; Wu, S.; Dong, L.; Liu, Q.; Wang, Q. Synthesis and characterization of compartmented Ca-alginate/silica self-healing fibers containing bituminous rejuvenator. Constr. Build. Mater. 2018, 190, 623–631.
  83. Shu, B.; Bao, S.; Wu, S.; Dong, L.; Li, C.; Yang, X.; Norambuena-Contreras, J.; Liu, Q.; Wang, Q. Synthesis and effect of encapsulating rejuvenator fiber on the performance of asphalt mixture. Materials 2019, 12, 1266.
  84. Xu, S.; Liu, X.; Tabaković, A.; Schlangen, E. A novel self-healing system: Towards a sustainable porous asphalt. J. Clean. Prod. 2020, 259, 120815.
  85. Wan, P.; Liu, Q.; Wu, S.; Zou, Y.; Zhao, F.; Wang, H.; Niu, Y.; Ye, Q. Dual responsive self-healing system based on calcium alginate/Fe3O4 capsules for asphalt mixtures. Constr. Build. Mater. 2022, 360, 129585.
  86. Wan, P.; Wu, S.; Liu, Q.; Xu, H.; Wang, H.; Peng, Z.; Rao, W.; Zou, Y.; Zhao, Z.; Chen, S. Self-healing properties of asphalt concrete containing responsive calcium alginate/nano-Fe3O4 composite capsules via microwave irradiation. Constr. Build. Mater. 2021, 310, 125258.
  87. Shi, Y.; Wang, M.; Ma, C.; Wang, Y.; Li, X.; Yu, G. A conductive self-healing hybrid gel enabled by metal–ligand supramolecule and nanostructured conductive polymer. Nano Lett. 2015, 15, 6276–6281.
  88. Williams, K.A.; Boydston, A.J.; Bielawski, C.W. Towards electrically conductive, self-healing materials. J. R. Soc. Interface 2007, 4, 359–362.
  89. Gong, F.; Cheng, X.; Fang, B.; Cheng, C.; Liu, Y.; You, Z. Prospect of 3D printing technologies in maintenance of asphalt pavement cracks and potholes. J. Clean. Prod. 2023, 397, 136551.
  90. Jackson, R.J.; Wojcik, A.; Miodownik, M. 3D printing of asphalt and its effect on mechanical properties. Mater. Des. 2018, 160, 468–474.
  91. Lv, Q.; Huang, W.; Xiao, F. Laboratory evaluation of self-healing properties of various modified asphalt. Constr. Build. Mater. 2017, 136, 192–201.
  92. Zhou, L.; Huang, W.; Zhang, Y.; Lv, Q.; Yan, C.; Jiao, Y. Evaluation of the adhesion and healing properties of modified asphalt binders. Constr. Build. Mater. 2020, 251, 119026.
  93. Huang, W.; Lv, Q.; Xiao, F. Investigation of using binder bond strength test to evaluate adhesion and self-healing properties of modified asphalt binders. Constr. Build. Mater. 2016, 113, 49–56.
  94. Tabatabaee, N.; Shafiee, M.H. 7th RILEM International Conference on Cracking in Pavements: Mechanisms, Modeling, Testing, Detection and Prevention Case Histories; Springer: Berlin/Heidelberg, Germany, 2012; pp. 869–878.
  95. Ganjei, M.A.; Aflaki, E. Application of nano-silica and styrene-butadiene-styrene to improve asphalt mixture self healing. Int. J. Pavement Eng. 2019, 20, 89–99.
  96. Lee, Y.-J.; Seo, J.-Y.; Kim, S.-Y.; Lee, S.-H.; Hong, Y.-K. Self-Healing Asphalt Prepared by using Ionic Epoxy Resin. Elastomers Compos. 2015, 50, 167–174.
  97. Zhou, X.; Ma, B.; Wei, K.; Wang, X. Deformation recovery properties of asphalt mixtures with shape memory epoxy resin. Constr. Build. Mater. 2021, 268, 121193.
More
© Text is available under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/)
ScholarVision Creations
Feedback